Recycling carbon fiber-reinforced polymers by pyrolysis and reused to prepare short-cut fiber C/C composite

Abstract

A new idea of reusing carbon fiber recycled from carbon fiber-reinforced epoxy resin (CF/EP) composite to fabricate short-cut fiber C/C composite by moulding was proposed. The recycled carbon fiber (rCF) maintains comparable properties to virgin carbon fiber (vCF) except for a small amount of pyrolytic carbon attached to it. The wettability of rCF-furfural acetone resin (FA), vCF-FA and pyrolytic carbon-FA is nearly the same by sessile drop method. The obtained rCF was subsequently fabricated into C/C composite by moulding. The density of the prepared rCF C/C composite is 1.51 g·cm⁻³ which is slightly higher than that of vCF C/C composite of 1.48 g·cm⁻³. The flexural strength of rCF C/C composite is 34.2 MPa, which is slightly lower than that the vCF C/C composite of 38.8 MPa. However, the vCF C/C composite exhibits pseudo-ductile fracture behavior, while the rCF C/C composite presents a brittle fracture behavior after reaching the maximum value. The reason can be attributed to the cluster structure of rCF resulting in its dispersion lower than that of vCF. Destruction of cluster structure and dispersion of rCF are vital for improving the mechanical properties of short-cut rCF C/C composite.

Keywords

CFRPs recycling carbon fiber reuse C/C composite

Get full access to this article

View all access options for this article.

References

Lester

Kingman

Wong

et al . Microwave heating as a means for carbon fibre recovery from polymer composites: a technical feasibility study. Mater Res Bull 2004; 39: 1549–1556.

Zheng

Shen

et al . A novel approach to recycling of glass fibers from non-metal materials of waste printed circuit boards. J Hazard Mater 2009; 170: 978–982.

Pimenta

Pinho

ST.

Recycling carbon fibre reinforced polymers for structural applications: technology review and market outlook. Waste Manage 2011; 31: 378–392.

Palmer

Ghita

Savage

et al . Successful closed-loop recycling of thermoset composites. Compos Part A 2009; 40: 490–498.

Palmer

Savage

Ghita

et al . Sheet moulding compound (SMC) from carbon fibre recyclate. Compos Part A 2010; 41: 1232–1237.

Steenkamer

Sullivan

JL.

On the recyclability of a cyclic thermoplastic composite material. Compos Part B 1998; 29: 745–752.

Fromonteil

Bardelle

Cansell

Hydrolysis and oxidation of an epoxy resin in sub- and supercritical water. Ind Eng Chem Res 2000; 39: 922–925.

Dang

Kubouchi

Sembokuya

et al . Chemical recycling of glass fiber reinforced epoxy resin cured with amine using nitric acid. Polymer 2005; 46: 1905–1912.

Suyama

Kubota

Shirai

et al . Effects of alcohols on the degradation of crosslinked unsaturated polyester in sub-critical water. Polym Degrad Stab 2006; 91: 983–986.

10.

Pickering

SJ.

Recycling technologies for thermoset composite materials – current status. Compos Part A 2006; 37: 1206–1215.

11.

Meyer

Schulte

CFRP-recycling following a pyrolysis route: process optimization and potentials. J Compos Mater 2009; 43: 1121–1132.

12.

Oliveux

Dandy

Leeke

GA.

Current status of recycling of fibre reinforced polymers: review of technologies, reuse and resulting properties. Prog Mater Sci 2015; 72: 61–99.

13.

Oliveux

Bailleul

Gillet

et al . Recovery and reuse of discontinuous carbon fibres by solvolysis: realignment and properties of remanufactured materials. Compos Sci Technol 2017; 139: 99–108.

14.

Wong

Mohammed

Pickering

et al . Effect of coupling agents on reinforcing potential of recycled carbon fibre for polypropylene composite. Compos Sci Technol 2012; 72: 835–844.

15.

Stoeffler

Andjelic

Legros

et al . Polyethylene sulphide (PPS) composites reinforced with recycled carbon fiber. Compos Sci Technol 2013; 84: 65–71.

16.

Harper

Turner

Martin

JRB

et al . Fiber alignment in directed carbon fiber preforms – a feasibility study. J Compos Mater 2009; 43: 57–74.

17.

Connor

ML.

Characterization of recycled carbon fibers and their formation of composites using injection molding. Master thesis, North Carolina State University, USA, 2008.

18.

Feraboli

Kawakami

Wade

et al . Recyclability and reutilization of carbon fiber fabric/epoxy composites. J Compos Mater 2012; 46: 1459–1473.

19.

Yang

Wang

Huo

et al . Synthesis of a phosphorus/nitrogen-containing compound based on maleimide and cyclotriphosphazene and its flame-retardant mechanism on epoxy resin. Polym Degrad Stabil 2016; 126: 9–16.

20.

Liang

Zhao

Zhang

et al . Enhanced flame retardancy of DGEBA epoxy resin with a novel bisphenol-A bridged cyclotriphosphazene. Polym Degrad Stabil 2017; 144: 292–303.

21.

Michael

Derek

Determination of band shifts as a function of strain in carbon fibers using Raman microline focus spectrometry (MIFS). Carbon 1993; 31: 1057–1064.

22.

Obraztsova

Fujii

Hayashi

et al . Raman identification of onion-like carbon. Carbon 1998; 36: 821–826.

23.

Naito

Yang

Inoue

et al . The effect of surface modification with carbon nanotubes upon the tensile strength and Weibull modulus of carbon fibers. J Mater Sci 2012; 47: 8044–8051.

24.

Watanabe

Tanaka

Okuda

et al . Tensile strength distribution of carbon fibers at short gauge lengths. Adv Compos Mater 2014; 23: 535–550.