Isolation of hydrodynamic parameters for the fibre length attrition in injection-moulded short-fibre polymer composites

Abstract

A comprehensive study of the fibre breakage mechanisms during mould filling in injection moulding of short-fibre polymer composites requires the isolation of the main parameters promoting fibre length attrition. In this work, hydrodynamic parameters such as injection flow rate and residence time in the range of injection moulding were isolated, and their effect on fibre length attrition was studied. Fibre breakage was quantified by means of a capillary rheometer attached to an injection moulding machine minimising fibre-equipment interactions. Fibre breakage increased linearly as a function of injection flow rate in the range of 30–120 cm³.s⁻¹. It was also found that residence time in the order of milliseconds had a significant effect on fibre breakage. The results shown that longer fibres had less breakage probability, which contradicts the buckling failure theory for brittle fibres in a simple shear flow. This result was attributed to the similar rotation period of the fibres in comparison with the test residence times.

Keywords

Glass fibres polymer-matrix composites optical microscopy injection moulding fibre breakage

Get full access to this article

View all access options for this article.

References

Chen

Cieslinski

Baird

. Progress in modeling long glass and carbon fiber breakage during injection molding. AIP Conf Proc 2015; 1664: 60004.

Inoue

Morita

Tanaka

, et al. Effect of screw design on fiber breakage and dispersion in injection-molded long glass-fiber-reinforced polypropylene. J Compos Mater 2013; 49: 75–84.

Durin

De Micheli

Ville

, et al. A matricial approach of fibre breakage in twin-screw extrusion of glass fibres reinforced thermoplastics. Compos Part A Appl Sci Manuf 2013; 48: 47–56.

Wolf

Holin

White

. Residence time distribution in a commercial twin-screw extruder. Polym Eng Sci 1986; 26: 640–646.

Hopmann

Weber

van Haag

, et al. A validation of the fibre orientation and fibre length attrition prediction for long fibre-reinforced thermoplastics. AIP Conf Proc 2015; 1664: 50008.

Phelps

Abd El-Rahman

Kunc

, et al. A model for fiber length attrition in injection-molded long-fiber composites. Compos Part A Appl Sci Manuf 2013; 51: 11–21.

Goris

Back

Yanev

, et al. A novel fiber length measurement technique for discontinuous fiber-reinforced composites: a comparative study with existing methods. Polym Compos 2018; 39: 4058–4070.

Goris

Simon

Montoya

, et al. Experimental study on fiber attrition of long glass fiber-reinforced thermoplastics under controlled conditions in a couette flow. Conference proceedings of society of plastics engineers (SPE) annual technical conference (ANTEC), Anaheim, CA, 8–10 may, 2017, Vol. 2017, pp. 600–606.

Moritzer

Heiderich

. Fiber length reduction during shearing in polymer processing. AIP Conf Proc 2017; 1914: 30002.

10.

Quijano-Solis

Yan

. Characterization of biofiber breakage in composite processing using a capillary rheometer. J Reinf Plast Compos 2014; 33: 1463–1473.

11.

Tian

Liang

Wang

, et al. Fiber breakage behavior of long glass fiber-reinforced polypropylene through the convergent channel. J Reinf Plast Compos 2017; 36: 1629–1638.

12.

Thomasset

Carreau

Sanschagrin

, et al. Rheological properties of long glass fiber filled polypropylene. J Nonnewton Fluid Mech 2005; 125: 25–34.

13.

Lakkanna

Mohan Kumar

Kadoli

. Computational design of mould sprue for injection moulding thermoplastics. J Comput Des Eng 2016; 3: 37–52.

14.

ASTM D3835-16 . Standard Test Method for Determination of Properties of Polymeric Materials by Means of a Capillary Rheometer. West Conshohocken, PA. Epub ahead of print 2016. DOI: 10.1520/D3835-16.

15.

Middleman

. Fundamentals of Polymer Processing. New York: McGray-Hill, Inc., 1977.

16.

Giusti

Zanini

Lucchetta

. Automatic glass fiber length measurement for discontinuous fiber-reinforced composites. Compos Part A Appl Sci Manuf 2018; 112: 263–270.

17.

ISO 22314 . Plastics – Glass-Fibre-Reinforced Products – Determination of Fibre Length, 2006.

18.

Sturges

. The choice of a class interval. J Am Stat Assoc 1926; 21: 65–66.

19.

Wang

Geng

Luo

, et al. Shear induced fiber orientation, fiber breakage and matrix molecular orientation in long glass fiber reinforced polypropylene composites. Mater Sci Eng A 2011; 528: 3169–3176.

20.

Lafranche

Krawczak

Ciolczyk

J-P

, et al. Injection moulding of long glass fiber reinforced polyamide 66: processing conditions/microstructure/flexural properties relationship. Adv Polym Technol 2005; 24: 114–131.

21.

Hine

Parveen

Brands

, et al. Validation of the modified rule of mixtures using a combination of fibre orientation and fibre length measurements. Compos Part A Appl Sci Manuf 2014; 64: 70–78.

22.

Ville

Inceoglu

Ghamri

, et al. A study of fiber breakage during compounding in a Buss Kneader. Int Polym Process 2012; 27: 245–251.

23.

Zhuang

Zong

, et al. Relationship between fiber degradation and residence time distribution in the processing of long fiber reinforced thermoplastics. Express Polym Lett 2008; 2: 560–568.

24.

Yang

Nian

Sun

. Flow visualization of filling process during micro-injection molding. Int Polym Process 2002; 17: 354–360.

25.

Forgacs

Mason

Particle motions in sheared suspensions: IX. Spin and deformation of threadlike particles. J Colloid Sci 1959; 14: 457–472.

26.

Salinas

Pittman

JFT

. Bending and breaking fibers in sheared suspensions. Polym Eng Sci 1981; 21: 23–31.

27.

Jeffery

Filon

LNG

. The motion of ellipsoidal particles immersed in a viscous fluid. Proc R Soc London Ser A, Contain Pap a Math Phys Character 1922; 102: 161–179.

Supplementary Material

Please find the following supplemental material available below.

For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.

For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.

0.00 MB

6.21 MB

1.88 MB