Low Velocity Transverse Impact Behavior of 8-ply,Graphite-Epoxy Laminates

Abstract

This work discusses the behavior of 8-ply, quasi-isotropic, graphite epoxy laminates subjected to low velocity transverse impact loading. Large deflection theory of plates was used to predict the load-deflection characteristics during the impact event. The im pact model considered that the indentation, flexural and shear stiffnesses could be represented by 3-equivalent springs in series.

The analysis of static and dynamic impact loading test-data concluded that the mem brane parameter, β, used in flexural stiffness relation was proportional to the square of the coefficient of restitution, e, of the impactor. Use of β = 0.443 e² was made in load- deflection relations to consider the drop in plate stiffness due to delamination.

The results of impact tests up to impact velocity 5.3 m/sec. were found in close agreement of the predictions.

Get full access to this article

View all access options for this article.

References

"Foreign Objects Damage to Composites,"

ASTM STP 586, 1976.

Elber, W. , "Deformation and Failure Mechanics in Low Velocity Impacts on Thin Composite Plates," Proc. of the Army Symposium on Solid Mechanics, 1982, pp. 288-317.

Timoshenko, S. and Woinowsky-Krieger, S. , "Theory of Plates and Shells," McGraw-Hill Book Co., N.Y., 1959 .

Lal, K.M.

"Prediction of Residual Tensile Strength of Transversely Impacted Composite Laminates,"

NASA CP 2245, 1982, pp. 97-112.

Spencer, A.J.M. , "Deformations of Fibre-Reinforced Materials," Clarendon Press, Oxford, 1972, pp. 10-12.

Lal, K.M. , "Coefficient of Restitution for Low Velocity Transverse Impact of Thin GraphiteEpoxy Laminates," NASA Grant No. NAG-1-196, Progress Report April, 1983.