Effects of Cooling Rate on the Crystallinity and Mechanical Properties of Thermoplastic Composites

Abstract

Tests were performed to evaluate the effects of crystallinity on the mechanical properties of PEEK 150P polymer and APC-2 graphite/PEEK composite. The tensile strengths, ten sile moduli and fracture toughnesses of the polymer, and the mixed mode I and mode II fracture toughnesses of the composite were measured at crystallinities ranging from 27 to 43 percent by weight. The results show that, in the crystallinity range studied, the tensile properties are not affected significantly by changes in crystallinity, while the fracture toughness depends strongly on the crystallinity. A model is also described which can be used to calculate the crystallinity from the known applied cooling rate. The validity of the model was verified by tests performed with PEEK 150P polymer.

Get full access to this article

View all access options for this article.

References

Ecker, E.R.G. and R.M. Drake. Heat and Mass Transfer. New York: McGraw-Hill (1975).

Ozawa, T. "Kinetics of Non-Isothermal Crystallization," Polymer , 12:150-158 (1971).

Gray, A.P. Thermochimica Acta, 1:563-579 (1970).

Broek, D. Elementary Engineering Fracture Mechanics Amsterdam : Martinus Nijhoff (1984).

Tirosh, J. "The Mixed Mode Fracture of Unidirectional Composites," Engineering Fracture Mechanics, 13.119-127 (1980).

Lakshminarayana, H.V. "A Symmetric Rail Shear Test for Mode II Fracture Toughness of Composite Materials—Finite Element Analysis," J. Composite Materials, 18:227-238 (1984).

Wu, E.M. and R.C. Reuter , Jr. "Crack Extension in Fiberglass Reinforced Plastics," T&AM Report, No. 275, University of Illinois (1965 ).

Seferis, J.C. and C.N. Velisaris. "Modeling-Processing-Structure Relationships of Polyetheretherketone (PEEK) Based Composites," in Materials Sciences for the Future. J. L. Bauer and R. Dunaetz , eds. Society for the Advancement of Material and Process Engineering, pp. 1236-1252 (1986).

Cebe, P. and S. Hong. "Crystallization Behavior of Poly(etheretherketone," Polymer, 27:1183-1192 (1986 ).

10.

Blundell, D.J. and B.N. Osborn. "The Morphology of Poly(aryl-ether-ether-ketone ," Polymer, 24:953-958 (1983)