Adhesion at the Interface in Cured Graphite Fiber Epoxy-Amine Resin Composites

Abstract

The effect of high temperature curing on the interface between unsized or epoxy-sized graphite fiber tow and epoxy-amine resin was examined by scanning electron microscopy of compression and freeze fractured specimens. Little or no adhesion was found between the unsized graphite fiber tows and the epoxy-amine resin on curing at 165°C for 17 hrs. Epoxy-sized graphite fibers showed a similar lack of adhesion between the fiber tows and the epoxy-amine resin at 3 and 17 hrs. cures, although good penetration of the resin into the sized fiber tows had occurred. Interfacial bond strengths for the composites could not be effectively measured by compression fracture of specimens.

Get full access to this article

View all access options for this article.

References

Scola, D.A. and C.S. Brooks. J. Adhesion, 2:213 (1970).

Goan, J.C. and S.P. Prosen. Interfaces in Composites, ASTM STP 452, p. 3 (1969 ).

Broutman, L.J. Interfaces in Composites, ASTM STP 452, p. 27 (1969).

Harris, B. , P.W.R. Beaumont and E.M. deFerran. J. Materials Sci., 6:238 (1971).

Lubin, G. , ed. Handbook of Composites. NY:Van Nostrand Reinhold Co. (1982 ).

Chiao, T.T. , E.S. Jessop and H.A. Newey. SAMPE Quart., 6(1):28 ( 1974).

Varma, D.S. , H.L. Needles , D.A. Kourtides and R.H. Fish. Org. Coatings and Appl. Polym. Sci. Proc. , 46:105 (1981).

Varma, D.S. , H.L. Needles , D.A. Kourtides and R.H. Fish. Polym. Composites, 4:98 (1983).

Broutman, L.J. and F.J. McGarry Modern Plastics, p. 161 (Sept. 1962).

10.

Hawthorne, H.M. and E. Teghtsoonian. J. Adhesion, 6:85 (1974).