Parametric Damage Modelling of Composites Due to Moisture Absorption

Abstract

This article presents a theoretical parametric model for the assessment of strength degradation of composite laminates subjected to different degrees of moisture concentration. The model is based on the real observation that the failure mechanism of composites after moisture absorption always initiates as debonding at the interface be tween the reinforcement and the matrix. In the development of the model, the composite is treated as a three-phase material: (1) the reinforcing fibers, (2) a thin bonding layer be tween matrix and fibers, and (3) the matrix. The material properties are assumed to be af fected by the moisture content according to a linear empirical relation. Finally, the overall performance of the composite is determined by the combined effect of all the empirical pa rameters related to the three phases.

Get full access to this article

View all access options for this article.

References

Weitsman, Y. 1986. "Moisture in Composites: Sorption and Damage," Mechanics and Materials Center, Texas A&M University, Report No. MM5022-86-11.

Adams, D.F. 1987. "A Micromechanics Analysis of the Influence on the Interface on the Performance of Polymer-Matrix Composites," Journal of Reinforced Plastics and Composites, 6:66-88.

Bascom, W.D. 1974. "Surface Chemistry of Moisture Induced Composite Failures," Composite Materials, Vol. 6, L. J. Broutman and R. H. Krock, eds.

Palley, I. 1990. "A Fracture Mechanics Approach to Interlammar Failure of Unidirectionally Reinforced Composites," Journal of Reinforced Plastics and Composites, 9:174-181.

Tsotsis, T.K. and Y. Weitsman. 1990. "Energy Release Rates for Cracks Caused by Moisture Absorption in Graphite/Epoxy Composites," Journal of Composite Materials, 24:483-496.

Ashbee, K.H.G. and R.C. Wyatt. 1969. "Water Damage in Glass Fiber/Resin Composites," Proc. Roy. Soc. London, Series A, Vol. 312, p. 553.

Kaelble, D.H. et al. 1975. "Interface Mechamsms of Moisture Degradation in Graphite/Epoxy Composites," Adhesion , 7:25.

Scola, D.A. 1974. "Fiber and Fiber-Resin Interface in Resin Composites," Composite Materials, Vol. 6, L. J. Broutman and R. H. Krock , eds.

Shih, G.C. and L.J. Ebert. 1987. "Theoretical Modelling of the Effect of the Interfacial Shear Strength on the Longitudinal Tensile Strength of Unidirectional Composites," Journal of Composite Materials , 21:207-224.