Stresses and Deformations in Thick-Walled Cylinders Subjected to Combined Loading and a Temperature Gradient

Abstract

Stresses and deformations in composite cylindrical tubes as a result of combined loading (internal and external pressure, axial load, applied torque) and a tem perature gradient through the wall thickness are studied. The composite tubes studied are, in general, long thick-walled cylinders made of arbitrarily oriented—with respect to the tube axis—orthotropic plies. A displacement-based linear elasticity solution is used in the analysis. Classical Laminated Plate Theory (CLPT), which assumes the composite lami nate to be in a state of plane stress, does not predict any stresses in the thickness direction; however, in thick-walled tubes, through-the-thickness stresses may not always be negligi ble. The elasticity solution has shown that, under internal pressure only, in angle-ply and single-ply tubes, the resulting radial stress is virtually independent of the ply fiber orienta tion. In cross-ply tubes, these stresses show significant differences. In the case of a uni form temperature change only, the nonlinear distribution of the radial stress changes substantially depending on the ply fiber orientation. Another difference between the CLPT and Elasticity Theory for the analysis of cylindrical tubes is found in predicting the maxi mum twist rate of the cylinder with unbalanced wall laminate. Elasticity Theory has shown that for thick-walled, single-ply cylinders subjected to a uniform temperature change, the maximum twist rate occurs at the ply orientation angle greater than 45° , de pending on the wall thickness and the mean radius of the cylinder, as opposed to 45° as predicted by the CLPT. The twist rate in thin-walled tubes subjected to internal pressure only is found to be much greater than in thick-walled tubes, due to the presence of large radial and hoop stresses in thick walls. In multi-layer cylinders, jumps in hoop and axial stresses have been observed at ply interfaces. Their magnitudes are shown to depend upon the angles of fiber orientation.

Get full access to this article

View all access options for this article.

References

Hyer, M.W. , D.E. Cooper and D. Cohen 1986. "Stresses and Deformations in Cross-Ply Composite Tubes Subjected to a Uniform Temperature Change," J. Thermal Stresses , 9 97-117

Hyer, M.W. and D.E. Cooper 1986. "Stresses and Deformations in Composite Tubes due to a Circumferential Temperature Gradient," J. Applied Mechanics , 53 757-764

Whitney, J.M. 1971 "On the Use of Shell Theory for Determining Stresses in Composite Cylinders," J. Composite Materials, 5 340-353

Whitney, J.M. and J.C. Halpin 1968 "Analysis of Laminated Anisotropic Tubes under Combined Loading," J. Composite Materials , 2(3) 360-367

Pagano, N.J. , J.C. Halpin and J.M. Whitney. 1968 "Tension Buckling of Anisotropic Cylinders," J Composite Materials, 2(2) 154-167

Pagano, N.J. and J.M. Whitney 1970 "Geometric Design of Composite Cylindrical Characterization Specimens," J Composite Materials, 4.360-378

Timoshenko, S. and J.N. Goodier. 1969. Theory of Elasticity. New York McGraw-Hill.

Vinson, J.R. and R.L. Sierakowski 1986. The Behavior of Structures Composed of Composite Materials Boston

Martinus Nijhoff Publishers

Kreyszig, E. 1983 Advanced Engineering Mathematics. New York

John Wiley & Sons

10.

Chapra, S.C. and R.P. Canale 1985 Numerical Methods for Engineers New York: McGraw-Hill

11.

Tutuncu, N. 1991. "Thermal Stresses and Deformations in Composite Thick-Walled and Thin-Walled Tubes and Shells," Ph D. Thesis, Rensselaer Polytechnical Institute, New York.