Compressive Failure Due to Shear Instability: Experimental Investigation of Waviness and Correlation with Analysis

Abstract

Tv1 panels of unidirectional T800/924 carbon fibre-epoxy were fabricated with a kink running across the width to produce fibre waviness. One panel had maximum fibre misalignment varying through the thickness from about 1.70 to 3.9° with a wavelength of about 6.0 mm, and the other varied from 2.20 to 5.60 with a wavelength of about 6.6 mm. Specimens loaded in compression showed increasing bending followed by catastrophic failure at average stresses of 1085 and 840 MPa. This is well below the compressive strength of 1816 MPa reported elsewhere for nominally straight specimens, confirming the critical effect of fibre waviness. The stress-strain response of the specimens was predicted well from finite element analysis accounting for large fibre rotations and non-linear shear properties. Failure was predicted at stresses 5.6% and 8.0% below the measured values. The model showed that the failure was precipitated by shear instability rather than classical compressive instability. The good correlation obtained validates the modelling approach and shows that it can be applied to predicting the effects of fibre waviness in composite components.

Get full access to this article

View all access options for this article.

References

1. Argon, A. 1972. Treatise on Materials Science and Technology, Vol. 1, New York: Academic Press, p. 79-79.

2. Davis, J. G., Jr. 1975. "Compressive Strength of Fibre-Reinforced Composite Materials," in Composite Reliability, AS7M STP S80, pp. 364-377.

3. Wang, A. S. D. 1978. "A Non-Linear Microbuckling Model Predicting the Compressive Strength of Unidirectional Composites,"ASME paper 78-WA/Aero-4.

4. Budiansky, B. 1983. "Micromechanics," Computers and Structures, 16:3-12.

5. Shuart, M. J. 1985. "Short-Wavelength Buckling and Shear Failures for Compression Loaded Composite Laminates," NASA TM-87640.

6. Hahn, H. T. and J. G. Wiliams . 1986. "Compression Failure Mechanisms in Unidirectional Composites," in Composite Materials: Testing and Design (Seventh Conf.), AS7'M STP 893, pp. 115-139.

7. Wisnom, M. R. 1990. "The Effect of Fibre Misalignment on the Compressive Strength of Carbon Fibre-Epoxy," Composites, 21(5):403-407.

8. Wisnom, M. R. 1993. "Analysis of Shear Instability under Compression due to Fibre Waviness," Journal of Reinforced Plastics and Composites, 12(11):1171-1189.

9. Fleck, N. A. and B. Budiansky . 1990. "Compressive Failure of Fibre Composite due to Microbuckling," in Inelastic Deformation of Composite Materials, G. J. Dvorak , ed., Springer-Verlag, pp. 235-274.

10.

10. Zhang, G. and R. A. Latour, Jr. 1993. "FRP Composite Compressive Strength and Its Dependence upon Interfacial Bond Strength, Fiber Misalignment and Matrix Non-Linearity," American Society for Composites Technical Conf, Cleveland, pp. 519-528.

11.

11. Williams, T. O. and D. S. Cairns . 1994. "A Model for the Compressive Failure of Composite Materials," Journal of Composite Materials, 28:92-111.

12.

12. Highsmith, A. L. , J. J. Davis and K. L. E. Helms . 1992. "The Influence of Fiber Waviness on the Compressive Behavior of Unidirectional Continuous Fiber Composites," Composite Materials: Testing and Design (Tenth Volume), AS7M STP 1120, pp. 20-36

13.

13. Camponeschi, E. T. 1993. "Kink-Band Failure Analysis of Thick Composites in Compression," Journal of Composite Materials, 27:471-490.

14.

14. Adams, D. O. and M. W. Hyer . 1993. "Effects of Layer Waviness on the Compression Strength of Thermoplastic Composite Laminates," Journal of Reinforced Plastics and Composites, 12:414-429.

15.

15. Mrse, A. M. and M. R. Piggott . 1993. "Compressive Properties of Unidirectional Carbon Fibre Laminates: II. The Effects of Unintentional and Intentional Fibre Misalignments," Composites Science and Technology, 46:219-227.

16.

16. Haeberle, J. G. and F. L. Matthews . 1990. "Studies on Compressive Failure in Unidirectional CFRP Using an Improved Test Method," Proc. ECCM4, Stuttgart, pp. 517-523.

17.

17. Curtis, P. T. 1988. "CRAG Test Methods for the Measurement of the Engineering Properties of Fibre Reinforced Plastics," RAE Technical Report 88012.

18.

18. Curtis, P. T. , J. Gates and C. G. Molyneux . 1991. 'An Improved Engineering Test Method for Measurement of the Compressive Strength of Unidirectional Carbon Fibre Composites," Composites, 22:363-368.

19.

19. ABAQUS, Hibbitt, Karlsson and Sorensen, Inc., 1080 Main St., Pawtucket, RI.