Sublaminate Buckling and Compression Strength of Stitched Uniweave Graphite/Epoxy Laminates

Abstract

Effects of through-the-thickness stitching on the sublaminate buckling and residual compression strength (often referred as compression-after-impact or CAI strength) of graphite/epoxy uniweave laminates are experimentally investigated. Primarily, three stitching variables: type of stitch yarn, linear density of stitch yarn and stitch density were studied. Delaminations were created by implanting teflon inserts during processing. The improvement in the CAI strength of the stitched laminates was up to 400% compared to the unstitched laminates. Stitching was observed to effectively restrict sublaminate buckling failure of the laminates. The CAI strength increases rapidly with increase in stitch density. It reaches a peak CAI strength that is very close to the compression strength of the undamaged material. All the stitch yarns in this study demonstrated very close performance in improving the CAI strength. It appears that any stitch yarn with adequate breaking strength and stiffness successfully restricts the sublaminate buckling.

Get full access to this article

View all access options for this article.

References

1. Suemasu, H. 1993. "Effects of Multiple Delaminations on Compressive Buckling Behaviors of Composite Panels," Journal of Composite Materials, 27(12):1172-1192.

2. Davidson, B. D. 'An Experimental Investigation of Delamination Buckling and Growth," AIAA-90-1023-CP, pp. 1218-1226.

3. Cox, B. N. 1994. "Delamination and Buckling in 3 D Composites," Journal of Composite Materials, 28(12):1114-1126.

4. Dow, M. B. and D. L. Smith . "Damage Tolerant Composite Materials Produced by Stitching Carbon Fabrics," Int. SAMPE Technical Conf. Series, 21:595-605.

5. Sharma, S. K. and B. V. Sankar . Sept. 1994. "Effect of Stitching on Impact and Interlaminar Properties of Graphite/EPoxy Laminates," Proceeding of the Tenth Annual Technical Meeting of the American Society of Composites, Technomic Publications, Lancaster, PA, pp. 700-708.

6. Sharma, S. K. and B. V. Sankar . Feb. 1995. "Effects of Through-the-Thickness Stitching on Impact and Interlaminar Fracture Properties of Textile Graphite/Epoxy Laminates," NASA-CR 195042, NASA Langley Research Center, Hampton, VA, pp. 1-127.