The Interlaminar Fracture Properties of Carbon Fiber Reinforced PEEK Laminates with Offset Centre Plies

Abstract

A series of mode I and mode II fracture tests have been undertaken on carbon fiber reinforced poly ether ether ketone (PEEK) in order to investigate the effect of fiber bridging on the interlaminar fracture resistance of high performance composite materials. Fiber bridging was reduced by offsetting the two centre plies by several degrees relative to each other. It has been shown that the fracture response of these slightly modified laminates is very different to that of conventional unidirectional composites. Offsetting the centre plies in double cantilever beam specimens resulted in a change in the mode of crack propagation from stable to unstable. The effects of varying processing parameters and loading rate were more pronounced in the offset specimens than in the standard unidirectional samples. It is concluded that even limited amounts of fiber bridging conceals the true interlaminar fracture response of many composite materials.

Get full access to this article

View all access options for this article.

References

1. Chen, V. L. , H.-Y. T. Wu and H.-Y. Yeh . 1993. "A Parametric Study of Residual Strength and Stiffness for Impact Damaged Composites," Composite Structures, 25:267-275

2. Baker, A. A. , R. Jones and R. J. Callinan . 1985. "Damage Tolerance of Graphite/Epoxy Composites," Composite Structures, 4:15-44

3. Abrate, S. 1991. "Impact on Laminated Composite Materials," Applied Mechanical Reviev, 44:155-190.

4. Morton, J. and E. W. Godwin . 1989. "Impact Response of Tough Carbon Fibre Composites," Composite Structures, 13:1-19.

5. Davies, P. , W. J. Cantwell , P. Y. Jar , H. Richard , D. J. Neville and H. H. Kausch . 1991. "Cooling Rate Effects in Carbon Fiber/PEEK Composites," ASTMSTP 1110, T. K. O'Brien , ed., pp. 70-88.

6. Sue, H. J. , R. E. Jones and E. I. Garcia-Meitin . 1993. "Fracture Behaviour of Model Toughened Composites under Mode I and Mode II Delamination," J. Materials Science, 28:6381-6391.

7. Glessner, A. L. , M. T. Takemori , M. A. Vallance and S. K. Gillford . 1989. "Mode I Interlaminar Fracture Toughness of Unidirectional Carbon Fiber Composites Using a Novel Wedge-Driven Delamination Design," ASTMSTP 1012, P. Lagace , ed., pp. 181-200.

8. Masters, J. E. 1987."Correlation oflmpact and Delamination Resistance in Interleafed Laminates," Proc. ICCM6/ECCM2, F. L. Matthews , N. C. R. Buskell , J. M. Hodgkinson and J. Morton , eds., Elsevier App. Sci., pp. 3-3.96-103.107-107.

9. Hine, P. J. , B. Brew , R. A. Duckett and I. M. Ward . 1989. "Failure Mechanisms in Continuous Carbon Fibre Reinforced PEEK Composites," Comp. Sci. and Tech., 35:31-51.

10.

10. Russell, A. J. and K. N. Street . 1985. "Moisture and Temperature Effects on the Mixed-Mode Delamination Fracture Toughness of Unidirectional Graphite/Epoxy," in Delamination and Debonding of Materials, ASTMSTP 876, W. S. Johnson , ed., pp. 349-370.

11.

11. Cantwell, W. J. and M. Blyton . "The Influence of Loading Rate on the Interlaminar Fracture Properties of Composite Materials," to be published in Key Engineering Materials.

12.

12. Beguelin, P. , M. Barbezat and H. H. Kausch . 1991. "Mechanical Characterisation of Polymers and Composites with a Servohydraulic High-Speed Tensile Tester," J. Phys. III, pp. 1867-1880.

13.

13. Mall, S. , G. E. Law and M. Katouzian . 1987. "Loading Rate Effect on the Interlaminar Fracture Toughness of a Thermoplastic Composite," J Composite Materials, 21:569-579.

14.

14. Curtis, P. T. , P. Davies , I. K. Partridge and J. P. Sainty . 1987. Proc. ICCM6-ECCM2, F. L. Matthews, N. C. R. Buskell and J. M. Hodgkinson, eds., London, Elsevier Applied Science, 4:401-412.

15.

15. Huang, X. H. and D. Hull . 1989. "Effects of Fibre Bridging on Gic of a Unidirectional Glass/Epoxy Composite," Comp. Sci. and Tech., 35:283-300.

16.

16. Davies, P. , W. Cantwell , C. Moulin and H. H. Kausch . 1989. "A Study of the Delamination Resistance of IM6/PEEK Composites," Composites Science and Technology, 36:153-166.

17.

17. Marais, C. , M. C. Merieene and P. Sigety . 1986. "Mesure de L'Energie de Rupture en Mode I des Resines et des Materiaux Composites Unidirectionnelles," Proc. 5th National Conference on Composites JNC5, Paris, September.

18.

18. Johnson, W. S. and P. D. Mangalgiri . 1986. "Investigation of Fiber Bridging in Double Cantilever Beam Specimens," NASA TM87716

19.

19. Blackman, B. R. K. , J. P. Dear , A. J. Kinloch , H. MacGillivray , Y. Wang and J. G. Williams . 1995. "The Failure of Fibre Composites and Adhesively Bonded Fibre Composites under High Rates of Test," J Materials Science, 30:5885-5900.

20.

20. Cantwell, W. J. and R. Zulfkifli . J. Materials Science Letters, 16(7):509-511.