The main objective of this study was to investigate the effect of waste glass addition on the properties of fired clay brick. Milled waste glass was added into brick clay at a ratio of 0% (control sample), 2.5, 5 and 10%. Four different series of test samples were produced by extrusion pressing. Samples were fired at 850, 950 and 1050 °C. The microstructures of the fired samples were investigated by scanning electron microscopy. The compressive strength of the fired samples was significantly improved by the addition of waste glass. It was concluded that the amorphous nature of waste glass particles enhanced the sintering action and this led to better strength behaviour.
Alvarez-Mendez, A., Torres-Gonzalez, LC, Alvarez, N., & Torres-Martinez, LM (2003) Kinetic thermal analysis of glass ceramics from industrial wastes. Journal of Non-Crystalline Solids, 329, 73-76.
2.
Astm. (ed.) (1986) ASTM, C 67. Standard Methods of Sampling and Testing Brick and Structural Clay Tile. Brick Manufacturing, Part I. American Society for Testing and Measurement, West Conshohoken, PA, USA.
3.
Bernardo, E., Castellan, R., Hreglich, S., & Lancellotti, I. (2006) Sintered sanidine glass-ceramics from industrial wastes. Journal of the European Ceramic Society , 26, 3335-3341.
4.
Bernardo, E., Castellan, R., & Hreglich, S. ( 2007) Sintered glass-ceramics from mixtures of wastes. Ceramics International, 33, 27-33.
5.
Bragança, S.R., Vicenzi, J., Guerino, K., & Bergmann, C.P. (2006) Recycling of iron foundry sand and glass waste as raw material for production of whiteware. Waste Management & Research, 24, 60-66.
6.
CWC Report (ed.) (2000) Densification, Crystallization, and Sticking Behaviour of Crushed Waste Glass Sintered in Refractory Molds With Release Agents. Report no. GL-00-2, Prepared by: Haun Labs., http://www.cwc.org/glass/gl002rpt.pdf , 2008.
7.
Colombo, P., Brusatin, G., Bernardo, E., & Scarinci, G. ( 2003) Inertization and reuse of waste materials by vitrification and fabrication of glass-based products. Current Opinion in Solid State and Materials Science, 7, 225-239.
8.
Erol, M., Kucukbayrak, S., Ersoy-Mericboyu A., & Ovecoglu, M.L. (2001) Crystallization behaviour of glasses produced from fly ash. Journal of the European Ceramic Society, 21, 2835-2841.
9.
Karamberi, A., Orkopoulos, K., & Moutsatsou, A. (2007) Synthesis of glass-ceramics using glass cullet and vitrified industrial by-products. Journal of the European Ceramic Society, 27, 629-636.
10.
Kısacık, I.E. ( 2002) Using Glass in Concrete. BS Thesis. Department of Civil Engineering, Faculty of Engineering and Architecture, Osmangazi University, Turkey, p. 52.
11.
Leshina, V.A. & Pivnev, A.L. ( 2002) Ceramic wall materials using glass waste. Glass and Ceramics, 59, 9-10.
12.
Lingart, Y. ( 1998) Imitation of natural material tiling using waste glass . Glass Technology, 39, 42-43.
13.
Manukyan, R.V. & Davydova, N.S. ( 1996) Use of waste in the ceramic industry. Glass and Ceramics, 53, 247-248.
14.
Matteucci, F., Dondi, M., & Guarini, G. ( 2002) Effect of soda-lime glass on sintering and technological properties of porcelain stoneware tiles. Ceramics International , 28, 873-880.
15.
Mear, F., Yot, P., Cambon, M., & Ribes, M. ( 2006) The characterization of waste cathode-ray tube glass. Waste Management, 26, 1468-1476.
16.
Pelino, M. ( 2000) Recycling of zinc-hydrometallurgy wastes in glass and glass ceramic materials. Waste Management, 20, 561-568.
17.
Pontikes, Y., Esposito, L., Tucci, A., & Angelopoulos, G.N. (2007) Thermal behaviour of clays for traditional ceramics with soda-lime-silica waste glass admixture . Journal of the European Ceramic Society, 27, 1657-1663.
18.
Raimondo, M., Zanelli, C., Matteucci, F., Guarini, G., Dondi, M., & Labrincha, J.A. (2007) Effect of waste glass (TV/PC cathodic tube and screen) on technological properties and sintering behaviour of porcelain stoneware tiles. Ceramics International, 33, 615-623.
19.
Rambaldi, E., Tucci, A., & Esposito, L. ( 2004) Use of recycled materials in the traditional ceramic industry . Ceramics International, 1-2, 13-23.
20.
Seung B.P., Lee B.C., & Kim J.H. ( 2004) Studies on mechanical properties of concrete containing waste glass aggregate. Cement and Concrete Research, 34, 2181-2189.
21.
Shil’tsina, A.D. & Selivanov, V.M. ( 2000) Ceramic tiles made of granular technogenic raw materials . Glass and Ceramics, 57, 7-8.
22.
Topcu, I.B. & Canbaz, M. ( 2004) Properties of concrete containing waste glass. Cement and Concrete Research, 34, 267-274.
23.
TS EN 771-1 (Turkish Standard Institution) (ed.) (2005) Specification for Masonry Units, Part 1: Clay Masonry Units. Turkish Standard Institution, Ankara, Turkey.
24.
TS EN 772-1 (Turkish Standard Institution) (ed.) (2005) Methods of Test for Mortar for Masonry Units; Part 1: Determination of Compressive Strength. Turkish Standard Institution, Ankara, Turkey.
25.
Tucci, A., Esposito, L., Rastelli, E., Palmonari, C., & Rambaldi, E. ( 2004) Use of soda-lime scrap-glass as a fluxing agent in a porcelain stoneware mix. Journal of the European Ceramic Society, 24, 83-92.
26.
Turgut, P. ( 2008) Properties of masonry blocks produced with waste limestone . Construction and Building Materials, 22, 1422-1427.