Effect of Non-halogen Flame Retardant Additives on the Properties of Vinyl Ester Resins and their Composites

Abstract

The paper describes the effect of combination of char forming additives and char forming catalysts on limiting oxygen index (LOI), smoke density and mechanical properties of neat as well as glass fibre reinforced vinyl ester (VE) resins. Three different samples of VE resins were prepared by reacting diglycidyl ether of bisphenol-A and methacrylic acid in stoichiometric (1: 2, sample A) and non-stoichiometric (1: 1.7, sample B and 1: 1, sample C) amounts. These resins were diluted with reactive diluents (50% w/w) styrene (S)/glycidyl methacrylate (GMA) or a combination of GMA with S for fabrication of neat sheets as well as composites. Incorporation of flame retardant additives (combination of ammonium polyphosphate, azobiscarbonamide, tris (2-hydroxyethyl) isocyanurate and hydrated alumina) in the laminates increased the LOI and decreased the smoke density values. The highest LOI was observed in laminates based on resin C containing flame retardant additives and a phosphorus containing amine as a hardener.

Keywords

vinyl ester resins epoxy resins thermosetting flame resistance flame retardant additives phosphine oxide azobiscarbonamide alumina trihydrate

Get full access to this article

View all access options for this article.

References

Le Lay, F and Gutierrez, J. (1999). Polymer Degradation and Stability, 64: 397-401.

La Rosa, A , Recca, A. , Carter, J.T. and McGrail, P.T. (1999). Polymer, 40: 4093-4098.

Weil, E.D. , Zhu, W. , Patel, N. and Mukhopadhyay, S.M. (1996). Polymer Degradation and Stability, 54: 125-136.

Knox, C.L. and Damle, S.B. (1993). U.S. Pat. 5,227,416.

Weil, E.D. and Choudhary, V. (1995). J. Fire. Sciences, 13: 104.

Crews, G.M. (Sept/Oct 1992). Plastics Compounding, Melamine Chemicals Inc., Donaldsonville, La.

Vandersall, H.L. (1971). J. Fire Flammability, 2: 97.

Camino, G.G. and Costa, L. (1986). Reviews in Inorganic Chemistry, 8(1-2): 69-100.

Braumann, S. (1977). J. Fire. Ret. Chem., 4: 18-37.

10.

Braumann, S. (1977). J. Fire. Ret. Chem., 4: 38-58.

11.

Nalepa, R.W. and Scharf, D.J. (1993). U.S. Pat. 5204392.

12.

Bockmann, G. (to Dr. Beck and Co. A.G. ) 1973 Ger. appl. 2,159,757. Chem. Abstr., 79(12): 67518z.

13.

Weil, E.D. (1997). PCT Patent Application WO97/31056.

14.

Gachter, R. and Muller, H. (1987). In: Plastics Additives Handbook, 2nd Edn. pp. 622, Hanser Publishers, Munich, Vienna, New York.

15.

Varma, I.K. , Fohlen, G.M. and Parker, J.A. (1983). J. Macromol. Sci. Chem. Ed., A-19: 209-224.