Thermal and flame properties of calcium borate and intumescent ammonium polyphosphate in epoxy/glass fiber composites

Abstract

The thermal and flammability properties of halogen-free flame retardants, calcium borate and intumescent ammonium polyphosphate, were evaluated on epoxy/glass fiber composites. The evolved volatile products under thermal stresses were analyzed accordingly, and the thermal decomposition of the composites was studied. It was determined that ammonium polyphosphate and calcium borate releases water vapor and carbon dioxide during their thermal decomposition, as a method to overcome the fire. Ammonium polyphosphate that achieved the V-0 rating at 5 vol% loading had showed better fire resistance than calcium borate that failed to achieve any rating even at high loading of 20 vol%. However, the calcium borate had recorded higher residual content. The combination of 1 vol% calcium borate and 4 vol% ammonium polyphosphate exhibited a synergistic performance by mass producing more char as a protection for the composites. Nevertheless, this synergism was not observed with the other combination, which comprised a 50:50 ratio of ammonium polyphosphate–calcium borate.

Keywords

Thermal decomposition thermogravimetric analysis–mass spectrometer thermal stability flame retardants scanning electron microscope

Get full access to this article

View all access options for this article.

References

Toldy

Szabo

Novak

. Intrinsically flame retardant epoxy resin-fire performance and background-Part II. Polym Degrad Stabil 2008; 93(11): 2007–2013.

Wang

Liu

Zhao

. Metal compound-enhanced flame retardancy of intumescent epoxy resins containing ammonium polyphosphate. Polym Degrad Stabil 2009; 94(4): 625–631.

Gao

Yan

. Thermal degradation and flame retardancy of epoxy resins containing intumescent flame retardant. J Therm Anal Calorim 2009; 95(2): 605–608.

Zhang

Liu

Chen

. Novel flame retardant thermosets from nitrogen-containing and phosphorus containing epoxy resins cured with dicyandiamide. J Appl Polym Sci 2007; 106(4): 2391–2397.

Rakotomalala

Wagner

Doring

. Recent developments in halogen free flame retardants for epoxy resins for electrical and electronic applications. Materials 2010; 3(8): 4300–4327.

Samyn

Bourbigot

Duquesne

. Effect of zinc borate on the thermal degradation of ammonium polyphosphate. Thermochim Acta 2007; 456(2): 134–144.

Long

Wang

. Synthesis of hydrophobic zinc borate nanoflakes and its effect on flame retardant properties of polyethylene. J Solid State Chem 2010; 183(4): 957–962.

Ishii

Kokaku

Nagai

. Calcium borate flame retardation system for epoxy molding compounds. Polym Eng Sci 2006; 46(6): 799–806.

Jimenez

Duquesne

Bourbigot

. Intumescent fire protective coating: toward a better understanding of their mechanism of action. Thermochim Acta 2006; 449(1–2): 16–26.

10.

Laoutid

Alexandre

Lopez-Cuesta

. New prospects in flame retardant polymer materials: from fundamentals to nanocomposites. Mater Sci Eng R 2009; 63(3): 100–125.

11.

Wang

. Intumescent flame retardation of EVA using microencapsulated ammonium polyphosphate and pentaerythritols. Polym-Plast Technol 2008; 47(3): 247–254.

12.

Liu

Chiu

. Thermal stability of epoxy resins containing flame retardant components: an evaluation with thermogravimetric analysis. Polym Degrad Stabil 2002; 78(1): 41–48.

13.

Charuchinda

Srikulkit

Mowattana

. Coapplication of sodium polyphosphate and chitosan to improve flame retardancy of cotton fabric. J Sci Res 2005; 30(1): 97–107.

14.

Fukatsu

. Thermal degradation behaviour of aromatic polyamide fiber blended with cotton fiber. Polym Degrad Stabil 2002; 75(3): 479–484.

15.

Yang

Tai

. Fire and mechanical performance of nanoclay reinforced glass-fiber/PBT composites containing aluminium hypophosphite particles. Compos Part A-Appl S 2011; 42(7): 794–800.

16.

Zhao

Huang

Xiong

. A novel halogen-free flame retardant for glass-fiber-reinforced poly(ethylene terephthalate). Polym Degrad Stabil 2008; 93(6): 1188–1193.

17.

Lim

WKP

Mariatti

Chow

. Halogen free flame retardants for epoxy substrate in electronic applications. In: Electronic manufacturing technology symposium (IEMT), 34th IEEE/CPMT International, Melaka, 2010, pp.1–4.

18.

Weil

. Synergists, adjuvants and antagonists in flame retardant systems. In: Grand

Wilkie

(eds) Fire retardancy of polymeric materials. New York: Marcel Dekker, 2000, ch. 4, pp.129–130.

19.

Shen

Kochefahani

Jouffret

. Boron-based flame retardants and flame retardancy. In: Wilkie

Morgan

(eds) Fire retardancy of polymeric materials. 2nd ed.. Boca Raton, FL: Taylor and Francis, 2010, ch. 10, p.207.

20.

Genovese

Shanks

. Structural and thermal interpretation of the synergy and interactions between the fire retardants magnesium hydroxide and zinc borate. Polym Degrad Stabil 2007; 92(1): 2–13.