New routes to flame retard polyamide 6,6 for electrical applications

Abstract

Polyamide 6,6 is used in many industrial fields such as housing materials, transport or electrical engineering applications. Due to its chemical composition, this polymer is easily flammable. As far as the main applications concern electrical and electronic equipments, its flame-retardant properties become an important requirement. The most discriminating tests are the limiting oxygen index, UL94 and glow wire flammability index. The aim is to obtain high limiting oxygen index values, V0 rating at UL94 test for 1.6- or 0.8-mm-thick samples and a validation at 960°C of the glow wire flammability index. The usual way to fire retard polyamide 6,6 consists of incorporating an important loading of fire-retardant additives, which often reduce the intrinsic properties of the polymer. It is also difficult to combine a thin polymer thickness (e.g. 0.8 mm) and a high amount of additives because of processing issues. In this article, we first carried out a rapid screening to determine the best fire retardant for polyamide 6,6 and its optimized amount to achieve the previously defined fire retardant properties. It was shown that an amount of 23% of aluminium diethylphosphinate Exolit OP1230 allows reaching the requirements. Then, carrying out two different surface treatments (coating of polysiloxanes by plasma-enhanced chemical vapour deposition and use of an intumescent waterborne varnish), we have tried to reach the same results. It was shown that the use of surface treatment alone does not allow reaching the objectives. As a consequence, the combination of the bulk approach at low loadings with the surface treatment was investigated. This new route allows the combination of the condensed phase mechanism of the intumescent barrier with the gas phase mechanism of the OP1230 and leads to very good results: the use of 5% of the flame-retardant additives combined with a 100-µm-thick waterborne intumescent varnish leads to better results than a 23% of additive loading.

Keywords

Polyamide 6 6 fire retardancy electrical and electronic equipments aluminium diethylphosphinate plasma-enhanced chemical vapour deposition intumescent coating glow wire flammability index UL94 limiting oxygen index

Get full access to this article

View all access options for this article.

References

Lewin

. In: Le Bras

Camino

Bourbigot

. (eds) Fire retardancy of polymers – the use of intumescence. Cambridge, UK: The Royal Society of Chemistry, 1998,p. 3. Physical and Chemical Mechanisms of Flame Retarding of Polymers

Nelson

. In: Nelson

(ed.) Proceedings of the American chemical society symposium, fire and polymers II. Washington, DC: American Chemical Society, 1995, p. 1. Fire and Polymers: An Overview.

Weber

Greim

. The toxicity of brominated and mixed-halogenated dibenzo-p-dioxins and dibenzofurans: an overview. J Toxicol Env Health 1997; 50(3): 195.

Camino

Luda

Costa

. In: Casal

(ed.) Chemical industry and environment, general aspects – risk analysis, Proceedings of Chemical industry and environment vol. I. 1993, p.221. Girona. Universitat Politecnica de Catalunja

Hamerton

. Recent developments in the chemistry of halogen-free flame-retardant polymers. Prog Polym Sci 2002; 27(8): 1661.

Balabanovich

Levchik

. Fire retardance in polyamide-6: the effects of red phosphorus and radiation-induced cross-links. Fire Mater 2001; 25(5): 179.

Jana

Roy

Maiti

. Biodegradable film: 7. Modification of the biodegradable film for fire retardancy. Polym Degrad Stabil 2000; 69(1): 79.

Bourbigot

Jama

Le Bras

. New approach to flame retardancy using plasma assisted surface polymerisation techniques. Polym Degrad Stabil 1999; 66(1): 153.

Jama

Quedé

Goudmand

. In: Nelson

Wilkie

(eds) Fire and polymers, materials and solutions for hazard prevention. ACS Symposium Series 797. Fire Retardancy and Thermal Stability of Materials Coated by Organosilicon Thin Films Using a Cold Remote Plasma Process. Washington, DC: American Chemical Society Publication, 2001, Ch. 16, p. 200.

10.

Jama

Quédé

Sadiki

. In: Lewin

(ed.) Recent advances in flame retardancy of polymeric materials, vol. 12. Norwalk, CT: Business Communications Co., Inc., 2001, p. 127. Studies of plasma applied polymer fire retardant coatings

11.

Quédé

Jama

Supiot

. Elaboration of fire retardant coatings on polyamide-6 using a cold plasma polymerization process. Surf Coat Tech 2002; 151–152: 424.

12.

Quédé

Mutel

Supiot

. Characterization of organosilicon films synthesized by N2-PACVD. Application to fire retardant properties of coated polymers. Surf Coat Tech 2004; 180–181: 265.

13.

Camino

Lomakin

Lazzari

. Polydimethylsiloxane thermal degradation part 1. Kinetic aspects. Polymer 2001; 42(6): 2395.

14.

Duquesne

Renaut

Bardollet

. In: Wilkie

Morgan

Nelson

(eds) Fire retardancy of polypropylene composites using intumescent coatings, fire and polymers V. ACS symposium series 1013. ACS, 2009, Ch. 12, pp. 200–212. Fire Retardancy of Polypropylene Composites Using Intumescent Coatings p. 192–204. (mistake in page number) Washington DC: American Chemical Society Publication.

15.

Jimenez

Duquesne

Bourbigot

. Fire protection of polypropylene and polycarbonate by intumescent coatings. Polym Advan Technol 2011; 22: 130.

16.

Supiot

Callebert

Dessaux

. Spectroscopic study of the reaction of tetramethyldisiloxane with a cold remote nitrogen plasma. Effect of dioxygen addition in the reactive mixture. Plasma Chem Plasma P 1993; 13(3): 539.

17.

Callebert

Supiot

Goudmand

. In: 11th International symposium on plasma chemistry, Loughborough, 1993, p. 1493. J. Hary editor, Spectroscopic study of the reaction of tetramethyldisiloxane with a cold remote nitrogen plasma.

18.

ASTM 3359-B:1987. Standard test method for measuring by tape test.

19.

ASTM D 2863/77:1977. Standard test method for measuring the minimum oxygen concentration to support candle-like combustion of plastics (oxygen index).

20.

ASTM E 1354-90a:1990. Standard test method for heat and visible smoke release for materials and products using an oxygen depletion calorimeter.

21.

International Standard IEC 60695-2-12. Fire hazard testing – Part 2-12: Glowing/hot-wire based test methods – glow wire flammability test method for materials. 2010.

22.

ASTM D3801:1996. Standard test method for measuring the comparative burning characteristics of solid plastics in a vertical position.

23.

Mouhmid

Imad

Benseddiq

. A study of the mechanical behaviour of a glass fibre reinforced polyamide 6,6: experimental investigation. Polym Test 2006; 25(4): 544.

24.

Braun

Schartel

Fichera

. Flame retardancy mechanisms of aluminium phosphinate in combination with melamine polyphosphate and zinc borate in glass-fibre reinforced polyamide 6,6. Polym Degrad Stabil 2007; 92: 1528.

25.

Costa

Camino

Luda Di Cortemiglia

. In: Nelson

(ed.) Fire and polymers. ACS symposium series 425. Washington DC, 1990, Mechanism of Thermal Degradation of Fire-Retardant Melamine Salts p. 211. American Chemical Society Publication.

26.

Weil

Levchik

. Current practice and recent commercial developments in flame retardancy of polyamides. J Fire Sci 2004; 22: 251.

27.

Jimenez

Bellayer

Duquesne

. Improvement of heat resistance of high performance fibers using a cold plasma polymerization process. Surf Coat Tech 2010; 205: 745.