Aluminum hypophosphite combined with melamine cyanurate and poly(phenylene oxide) was applied to flame retard TPE-S system (blends of SEBS and polyolefin). TPE-S containing 16 wt% aluminum hypophosphite, 20 wt% melamine cyanurate, and 10 wt% poly(phenylene oxide) pass a V-0 rating in the UL-94 test and its limiting oxygen index value is 28.2%. Zinc borate and magnesium hydroxide were added to modify the AHP/MCA/PPO formulation. Thermogravimetric–Fourier transform infrared analysis tests showed that aluminum hypophosphite and melaminecyanurate acted in gaseous phase while aluminum hypophosphite and poly(phenylene oxide) helped to form char residue. TPE-S/AHP/MCA/PPO significantly decreased the heat release rate (reduction in peak heat release rate from 2001 to 494 kW m−2). Scanning electron microscopy/energy dispersive spectrometry results demonstrated that zinc borate and magnesium hydroxide promoted to retain more P and O elements in residue. Zinc borate and magnesium hydroxide in AHP/MCA/PPO formulation enhanced the char formation and reduced gas evolution of TPE-S, thus deteriorating the combination between gaseous phase and condensed phase.
TiggemannHMRibeiroVFCelsoFet al. Effect of commercial clays on the properties of SEBS/PP/oil thermoplastic elastomers. Part 1. Physical, mechanical and thermal properties. Appl Surf Sci2015; 109–110: 151–156.
2.
SutAGreiserSJägerCet al. Aluminium diethylphosphinate versus ammonium polyphosphate: a comprehensive comparison of the chemical interactions during pyrolysis in flame-retarded polyolefine/poly(phenylene oxide). Thermochim Acta2016; 640: 74–84.
3.
TiggemannHMTomacheskiDCelsoFet al. Use of wollastonite in a thermoplastic elastomer composition. Polym Test2013; 32(8): 1373–1378.
4.
ZangYLiBXuM.Flame retardancy and water resistance of novel intumescent flame-retardant oil-filled styrene-ethylene-butadiene-styrene block copolymer polypropylene composites. J Appl Polym Sci2014; 131: 1–9.
5.
JazaniOMArefazarASaebMRet al. Evaluation of mechanical properties of polypropylene/polycarbonate/SEBS ternary polymer blends using Taguchi experimental analysis. J Appl Polym Sci2010; 116: 2312–2319.
6.
GreinCGahleitnerMBernreitnerK.Mechanical and optical effects of elastomer interaction in polypropylene modification: ethylene-propylene rubber, poly-(ethylene-co-octene) and styrene-butadiene elastomers. Express Polym Lett2012; 6(9): 688–696.
7.
MaZJiangPWangLet al. Effect of styrene-ethylene-butadiene-styrene and its synergetic effect with ethylene vinyl acetate on the mechanical, thermal, dielectric, and water-treeing behaviors of crosslinked polyethylene. J Appl Polym Sci2010; 118: 2350–2357.
8.
WuZWangHTianXet al. Mechanical and flame-retardant properties of styrene–ethylene–butylene–styrene/carbon nanotube composites containing bisphenol A bis(diphenyl phosphate). Compos Sci Technol2013; 82: 8–14.
9.
JiangZLiuSZhaoJet al. Flame-retarded mechanism of SEBS/PPO composites modified with mica and resorcinol bis(diphenyl phosphate). Polym Degrad Stabil2013; 98(12): 2765–2773.
10.
XiaoWDKibbleKA.Comparison of aluminium hydroxide and magnesium hydroxide as flame retardants in SEBS-based composites. Polym Polym Composite2008; 16(7): 415–422.
11.
XiaoWDKevinAKLinF.Mechanical properties and flame retardancy of SEBS-based composite with MDH. Polymer2009; 17(2): 117–125.
12.
OyamaHTSekikawaMShidaS.Effect of the interface structure on the morphology and the mechanical, thermal, and flammability properties of polypropylene/poly(phenylene ether)/magnesium hydroxide composites. Polym Degrad Stabil2012; 97(5): 755–765.
13.
LangfeldKWilkeASutAet al. Halogen-free fire retardant styrene–ethylene–butylene–styrene-based thermoplastic elastomers using synergistic aluminum diethylphosphinate–based combinations. J Fire Sci2015; 33(2): 157–177.
14.
WilkeALangfeldKUlmerBet al. Halogen-free multicomponent flame retardant thermoplastic styrene–ethylene–butylene–styrene elastomers based on ammonium polyphosphate–expandable graphite synergy. Ind Eng Chem Res2017; 56(29): 8251–8263.
15.
ZhuZ-MRaoW-HKangA-Het al. Highly effective flame retarded polystyrene by synergistic effects between expandable graphite and aluminum hypophosphite. Polym Degrad Stabil2018; 154: 1–9.
16.
WuNLiX.Flame retardancy and synergistic flame retardant mechanisms of acrylonitrile-butadiene-styrene composites based on aluminum hypophosphite. Polym Degrad Stabil2014; 105: 265–274.
17.
WuNLangS.Flame retardancy and toughness modification of flame retardant. Polym Degrad Stabil2016; 123: 26–35.
18.
ZhaoPGuoCLiL.Exploring the effect of melamine pyrophosphate and aluminum hypophosphite on flame retardant wood flour/polypropylene composites. Constr Build Mater2018; 170: 193–199.
19.
XuWZWangPCWangSQet al. Synthesis of microsphere aluminum hypophosphite and its application in polyurethane elastomer. J Appl Polym Sci2015; 132: 1–7.
20.
ZhanJMaLLiuXet al. Mechanical, thermal, and flame-retardant behaviors of thermoplastic polyether–ester elastomer composites with polyphenylene oxide and aluminum hypophosphite. Polym-Plast Technol2016; 56(10): 1096–1107.
21.
LiuGGaoS.Synergistic effect between aluminum hypophosphite and a new intumescent flame retardant system in poly(lactic acid). J Appl Polym Sci2018; 135: 1–9.
PawlowskiKHSchartelBFicheraMAet al. Flame retardancy mechanisms of bisphenol A bis(diphenyl phosphate) in combination with zinc borate in bisphenol A polycarbonate/acrylonitrile-butadiene-styrene blends. Thermochim Acta2010; 498: 92–99.
28.
HeMCaoWCWangLJet al. Synergistic effects of organo-sepiolite and zinc borate on the fire retardancy of polypropylene. Polym Advan Technol2013; 24: 1081–1088.
29.
OualhaMAAmdouniNLaoutidF.Synergistic flame-retardant effect between calcium hydroxide and zinc borate in ethylene-vinyl acetate copolymer (EVA). Polym Degrad Stabil2017; 144: 315–324.
30.
NaikADFontaineGSamynFet al. Melamine integrated metal phosphates as non-halogenated flame retardants: synergism with aluminium phosphinate for flame retardancy in glass fiber reinforced polyamide 66. Polym Degrad Stab2013; 98(12): 2653–2662.
31.
SutAGreiserSJägerCet al. Interactions in multicomponent flame-retardant polymers: solid-state NMR identifying the chemistry behind it. Polym Degrad Stabil2015; 121: 116–125.
32.
FengCMZhangYLiangDet al. Influence of zinc borate on the flame retardancy and thermal stability of intumescent flame retardant polypropylene composites. J Anal Appl Pyrolysis2015; 115: 224–232.
33.
ZhangFChenPWangYet al. Smoke suppression and synergistic flame retardancy properties of zinc borate and diantimony trioxide in epoxy-based intumescent fire-retardant coating. J Therm Anal Calorim2016; 123: 1319–1327.
34.
MakhloufGHassanMNourMet al. Evaluation of fire performance of linear low-density polyethylene containing novel intumescent flame retardant. J Therm Anal Calorim2017; 130: 1031–1041.
35.
ZhangZWuWZhangMQet al. Hydrothermal synthesis of 4ZnO·B2O3·H2O_RGO hybrid material and its flame retardant behavior in flexible PVC and magnesium hydroxide composites. Appl Surf Sci2017; 425: 896–904.
36.
SchartelBWilkieCACaminoG.Recommendations on the scientific approach to polymer flame retardancy: part 2—concepts. J Fire Sci2016; 35(1): 3–20.
37.
SchartelBWilkieCACaminoG.Recommendations on the scientific approach to polymer flame retardancy: part 1—scientific terms and methods. J Fire Sci2016; 34(6): 447–467.
WuQQuBJ.Synergistic effects of silicotungistic acid on intumescent flame-retardant polypropylene. Polym Degrad Stabil2001; 74(2): 255–261.
40.
YiJSYinHQCaiXF.Effects of common synergistic agents on intumescent flame retardant polypropylene with a novel charring agent. J Therm Anal Calorim2013; 111(1): 725–734.
41.
MircescuNEOlteanMChişVet al. FTIR, FT-Raman, SERS and DFT study on melamine. Vib Spectrosc2012; 62: 165–171.
42.
LaiXTangSLiHet al. Flame-retardant mechanism of a novel polymeric intumescent flame retardant containing caged bicyclic phosphate for polypropylene. Polym Degrad Stabil2015; 113: 22–31.
43.
AlongiJHanZBourbigotS.Intumescence: tradition versus novelty. A comprehensive review. Prog Polym Sci2015; 51: 28–73.
44.
WangD-YCaiX-XQuM-Het al. Preparation and flammability of a novel intumescent flame-retardant poly(ethylene-co-vinyl acetate) system. Polym Degrad Stabil2008; 93(12): 2186–2192.
45.
JachowiczJKowalskM. Thermal degradation of poly(2,6-dimethyl-1,4-phenylene oxide). I. The mechanism of degradation. J Appl Polym Sci1978; 22: 2891–2899.
46.
JachowiczJKryszewskiM.Thermal degradation of poly(2,6-dimethyl-1,4-phenylene oxide): 2. Mass spectroscopic analysis of dimeric products from degradation of poly(2,6-dimethyl-1,4-phenylene oxide). Polymer1978; 19(1): 93–98.
47.
MurashkoEALevchikGFLevchikSVet al. Fire retardant action of resorcinol bis(diphenyl phosphate) in a PPO/HIPS blend. J Fire Sci1998; 16(4): 233–249.
48.
CarpentierFBourbigotSBrasMLet al. Charring of fire retarded ethylene vinyl acetate copolymer-magnesium hydroxide/zinc borate formulations. Polym Degrad Stabil2000; 69: 83–92.
49.
LiangJZhangY.A study of the flame-retardant properties of polypropylene/Al(OH)3/Mg(OH)2 composites. Polym Int2010; 59(4): 539–542.
50.
BraunUSchartelBFicheraMAet al. Flame retardancy mechanisms of aluminium phosphinate in combination with melamine polyphosphate and zinc borate in glass-fibre reinforced polyamide6,6. Polym Degrad Stabil2007; 92(8): 1528–1545.