Re-examination of the intumescence mechanism of ammonium polyphosphate/pentaerythritol/zeolite 4A fire-retarded formulation using advanced spectroscopic techniques
Restricted accessResearch articleFirst published online September, 2024
Re-examination of the intumescence mechanism of ammonium polyphosphate/pentaerythritol/zeolite 4A fire-retarded formulation using advanced spectroscopic techniques
The mixture of ammonium polyphosphate and pentaerythritol is a very efficient intumescent system suitable for polyolefins, especially polypropylene. In this article, the intumescence mechanism of this intumescent system with and without zeolite 4A used as a synergy agent is revisited. The intumescent system was investigated in depth using continuous-wave electron paramagnetic resonance spectroscopy, solid-state nuclear magnetic resonance, and the advanced technique, namely hyperfine sublevel correlation pulsed electron paramagnetic resonance. It was observed that the char generated between 250°C and 350°C is made of polycyclic heterocyclic radicals with nitrogen atoms and that free radicals are mainly generated at these temperatures with a spin concentration relatively stable at least up to 500°C. Moreover, the presence of hydrogen, carbon, nitrogen, and phosphorus was clearly evidenced in the chemical environment of free electrons at 350°C (hyperfine sublevel correlation pulsed electron paramagnetic resonance). Besides, it was also evidenced that 4A totally collapses below 250°C. Contrary to previous works suggesting the presence of aluminosilicophosphate complexes, this work demonstrated that distinct alumino- and silicophosphate complexes are generated and protected the residue at high temperatures.
CaminoGCostaLTrossarelliL.Study of the mechanism of intumescence in fire retardant polymers: part I-thermal degradation of ammonium polyphosphate-pentaerythritol mixtures. Polym Degrad Stab1984; 6(4): 243–252.
4.
CaminoGCostaLTrossarelliL.Study of the mechanism of intumescence in fire retardant polymers: part II-mechanism of action in polypropylene-ammonium polyphosphate-pentaerythritol mixtures. Polym Degrad Stab1984; 7(1): 25–31.
5.
CaminoGCostaLTrossarelliL, et al. Study of the mechanism of intumescence in fire retardant polymers: part IV-evidence of ester formation in ammonium polyphosphate-pentaerythritol mixtures. Polym Degrad Stab1984; 8(1): 13–22.
6.
CaminoGCostaLTrossarelliL, et al. Study of the mechanism of intumescence in fire retardant polymers: part VI-mechanism of ester formation in ammonium polyphosphate-pentaerythritol mixtures. Polym Degrad Stab1985; 12(3): 213–228.
7.
McKeeDWSpiroCLLambyEJ.Inhibition of graphite oxidation by phosphorus additives. Carbon1984; 22(3): 285–290.
8.
DelobelRLe BrasMOuassouN, et al. Thermal behaviours of ammonium polyphosphate-pentaerythritol and ammonium pyrophosphate-pentaerythritol intumescent additives in polypropylene formulations. J Fire Sci1990; 8(2): 85–108.
9.
CaminoGMartinassoGCostaL.Thermal degradation of pentaerythritol diphosphate, model compound for fire retardant intumescent systems: part I-overall thermal degradation. Polym Degrad Stab1990; 27(3): 285–296.
10.
CaminoGMartinassoGCostaL, et al. Thermal degradation of pentaerythritol diphosphate, model compound for fire retardant intumescent systems: part II-intumescence step. Polym Degrad Stab1990; 28: 17–38.
11.
BourbigotSLe BrasMDelobelR.Carbonization mechanisms resulting from intumescence association with the ammonium polyphosphate-pentaerythritol fire retardant system. Carbon1993; 31(8): 1219–1230.
12.
BourbigotSle BrasMDelobelR.Fire degradation of an intumescent flame retardant polypropylene using the cone calorimeter. J Fire Sci1995; 13(1): 3–22.
13.
BourbigotSDuquesneSLeroyJM.Modeling of heat transfer of a polypropylene-based intumescent system during combustion. J Fire Sci1999; 17(1): 42–56.
14.
BourbigotSLe BrasMDelobelR, et al. 4A zeolite synergistic agent in new flame retardant intumescent formulations of polyethylenic polymers—study of the effect of the constituent monomers. Polym Degrad Stab1996; 54: 275–287.
15.
BourbigotSLe BrasMDelobelR, et al. Synergistic effect of zeolite in an intumescence process: study of the interactions between the polymer and the additives. J Chem Soc Faraday Trans1996; 92(1): 149–158.
16.
WeiPJiangPHanZ, et al. An investigation of the effects of zeolites on the thermal degradation and charring of APP-PER by TGA-XPS. J Fire Sci2005; 23(2): 173–184.
17.
TsvetkovIDMolinINVoyevodskiiVV.Investigation of electron paramagnetic resonance spectra of some irradiated polymers. Polym Sci USSR1961; 2(1–2): 165–174.
18.
ChiangTCSibiliaJP.Electron paramagnetic resonance study of thermal-oxidative degradation of nylon 6. J Polym Sci Part A-1 Polym Chem1972; 10: 605–612.
19.
TkáčA.The relation between thermal decomposition of polymers and free radical formation under high vacuum pyrolysis. J Polym Sci1976; 57: 109–120.
20.
TkáčA.Radical processes in polymer burning and its retardation—I. ESR methods for studying the thermal decomposition of polymers in the preflame and flame zones. J Polym Sci1981; 19(6): 1475–1493.
21.
TkáčAŠpildaI.Radical processes in polymer burning and its retardation. II. An ESR study of flame retardation of polypropylene. J Polym Sci1981; 19(6): 1495–1508.
22.
NguyenTAIchiseSKinashiK, et al. Spin trapping analysis of the thermal degradation of polypropylene. Polym Degrad Stab2022; 197: 109871.
23.
KaurBGurISBhatnagarHL.Studies on the chars of flame-retardant phosphorylated cotton fibres containing transition metal ions. Fire Saf J1989; 14(3): 151–165.
24.
BaggaSLJainRKGurIS, et al. Thermal and spectroscopic studies on flame-retardant cotton cellulose modified with THPC-urea-ADP and its transition metal complexes. Br Polym J1990; 22(2): 107–120.
25.
BhagwanJLalKHorrocksAR, et al. Thermal, spectral and morphological studies on cellulose, cellulose ethylthiophosphate and its metal complexes in air. Polym Int1993; 30(1): 33–45.
26.
TrehanRKadGLLalK.Thermal and spectroscopic studies on cellulose and its organophosphorus derivatives. J Indian Inst Sci1995; 75(6): 683–692.
27.
SinghRAroraSLalK.Thermal and spectral studies on cellulose modified with various cresyldichlorothiophosphates. Thermochim Acta1996; 289(1): 9–21.
28.
SinghRAroraSLalK.Thermal and spectral studies on cellulose arylthiophosphate in air. Indian J Chem1996; 35: 18–24.
29.
LevchikSVCaminoGCostaL, et al. Mechanistic study of thermal behaviour and combustion performance of carbon fibre-epoxy resin composites fire retarded with a phosphorus-based curing system. Polym Degrad Stab1996; 54(2–3): 317–322.
30.
LevchikSVLevchikGFCaminoG, et al. Fire-retardant action of potassium nitrate in polyamide 6. Angew Makromol Chemie1997; 245: 23–35.
31.
DuquesneSLe BrasMBourbigotS, et al. Mechanism of fire retardancy of polyurethanes using ammonium polyphosphate. J Appl Polym Sci2001; 82(13): 3262–3274.
32.
NaikADBourbigotSBellayerS, et al. Salen complexes as fire protective agents for thermoplastic polyurethane: deep electron paramagnetic resonance spectroscopy investigation. ACS Appl Mater Interfaces2018; 10(29): 24860–24875.
33.
HuYFanWCWangQA, et al. Study on gas phase long-lived radicals in combustion of polyurethane modified by phosphazene. Prog Nat Sci1999; 9(2): 103–108.
34.
PanYHanLGuoZ, et al. Improving the flame-retardant efficiency of aluminum hydroxide with fullerene for high-density polyethylene. J Appl Polym Sci2017; 134(9): 1–9.
35.
RakhimkulovADLomakinSMDubnikovaIL, et al. The effect of multi-walled carbon nanotubes addition on the thermo-oxidative decomposition and flammability of PP/MWCNT nanocomposites. J Mater Sci2010; 45(3): 633–640.
36.
ZaikovGERakhimkulovADLomakinSM, et al. Thermal degradation and combustion behavior of polypropylene/MWCNT composites. In: CP1255, Vth international conference on times of polymers (TOP) and composites, 20–23 June 2010, Ischia (Italy), 2010, pp. 1–4.
37.
Le BrasMBourbigotSDelporteC, et al. New intumescent formulations of fire—retardant polypropylene—discussion of the free radical mechanism of the formation of carbonaceous protective material during the thermo-oxidative treatment of the additives. Fire Mater1996; 20(4): 191–203.
38.
MüllerDHoebbellDGessnerW.27Al NMR studies of aluminosilicate solutions. Influences of the second coordination sphere on the shielding of aluminium. Chem Phys Lett 1981; 84(1): 25.
39.
MüllerDGessnerWBehrensHJ, et al. Determination of the aluminium coordination in aluminium-oxygen compounds by solid-state high-resolution 27AI NMR. Chem Phys Lett1981; 79(1): 59–62.
40.
BourbigotSLe BrasMDelobelR, et al. Synergistic effect of zeolite in an intumescence process study of the interactions between the polymer and the additives. J Chem Soc Faraday Trans1996; 92(18): 3435–3444.
41.
OestrikeRYangWHKirkpatrickRJ, et al. High-resolution 23Na, 27Al and 29Si NMR spectroscopy of framework Aluminosilicate glasses. Geochim Cosmochim Acta1987; 51(8): 2199–2209.
42.
WawrzynESchartelBSeefeldtH, et al. What reacts with what in bisphenol a polycarbonate/silicon rubber/bisphenol a bis(diphenyl phosphate) during pyrolysis and fire behavior. Ind Eng Chem Res2012; 51(3): 1244–1255.
43.
WawrzynESchartelBKarraschA, et al. Flame-retarded bisphenol A polycarbonate/silicon rubber/bisphenol A bis(diphenyl phosphate): adding inorganic additives. Polym Degrad Stab2014; 106: 74–87.
44.
WeedingTLDe JongBHWSVeemanWS, et al. Silicon coordination changes from 4-fold to 6-fold on devitrification of silicon phosphate glass. Nature1985; 318(6044): 352–353.
45.
LiangTLinXHZouYR, et al. Elucidating the chemical structures of petroleum resin using solid-state 13C NMR. Chem Geol2023; 630: 121492.
46.
BassoMCPizziADelmotteL, et al. Analysis of the cross-linking reaction of lignin with triethyl phosphate by MALDI-TOF and 13C NMR. Polymers (Basel)2017; 9(6): 206.
47.
VanderHartDLSimmonsSGilmanJW.Solid-state 13C nuclear magnetic resonance spectroscopy of ethylene/vinyl alcohol copolymers: morphological partitioning of hydroxyls. Polymer (Guildf)1995; 36(22): 4223–4232.
48.
EarlWLVanderhartDL.Measurement of 13C Chemical Shifts in Solids. J Magn Reson1982; 48(1): 35–54.
49.
ZabińskiJMaciejewskaDWolskaI.Solid state structural analysis of new pentamidine analogs designed as chemotherapeutics that target DNA by X-ray diffraction and 13C, 15N CP/MAS NMR methods. J Mol Struct2010; 984(1–3): 68–74.
50.
GilmanJWAwadWHDavisRD, et al. Polymer/layered silicate nanocomposites from thermally stable trialkylimidazolium-treated montmorillonite. Chem Mater2002; 14(9): 3776–3785.
51.
KarraschAJägerCKarakawaM, et al. Solid-state NMR studies of methyl celluloses. Part 1: regioselectively substituted celluloses as standards for establishing an NMR data basis. Cellulose2009; 16(1): 129–137.
52.
KarraschAJägerCSaakeB, et al. Solid-state NMR studies of methyl celluloses. Part 2: determination of degree of substitution and O-6 vs. O-2/O-3 substituent distribution in commercial methyl cellulose samples. Cellulose2009; 16(6): 1159–1166.
53.
GilmanJWRitchieSJKashiwagiT, et al. Fire—retardant additives for polymeric materials—I. Char formation from silica gel-potassium carbonate. Fire Mater1997; 21(1): 23–32.
54.
GilmanJWLomakinSKashiwagiT, et al. Characterization of flame-retarded polymer combustion chars by solid-state 13C and 29Si NMR and EPR. Fire Mater1998; 22(2): 61–67.
55.
MandalaVSLohDMShepardSM, et al. Bacterial phosphate granules contain cyclic polyphosphates: evidence from 31P solid-state NMR. J Am Chem Soc2020; 142(43): 18407–18421.
56.
JessenHJDürr-MayerTHaasTM, et al. Lost in condensation: poly-, cyclo-, and ultraphosphates. Acc Chem Res2021; 54(21): 4036–4050.
57.
SannigrahiPIngallE.Polyphosphates as a source of enhanced P fluxes in marine sediments overlain by anoxic waters: evidence from 31P NMR. Geochem Trans2005; 6(3): 52–59.
58.
KirkpatrickRJBrowRK.Nuclear magnetic resonance investigation of the structures of phosphate and phosphate-containing glasses: a review. Solid State Nucl Magn Reson1995; 5(1): 9–21.
59.
YuYGuoHPujari-PalmerM, et al. Advanced solid-state 1H/31P NMR characterization of pyrophosphate-doped calcium phosphate cements for biomedical applications: the structural role of pyrophosphate. Ceram Int2019; 45(16): 20642–20655.
60.
BerezickaASzumeraMSułowskaJ, et al. Unraveling the nature of sulfur-bearing silicate-phosphate glasses: insights from multi-spectroscopic (Raman, MIR, 29Si, 31P MAS-NMR, XAS, XANES) investigation. Ceram Int2022; 48(3): 4238–4254.
61.
HahnDMasoudi AlaviAQuirmbachP.Powder XRD and 31P and 27Al solid state MAS NMR investigations of phase transformations in aluminium phosphate bonded Al2O3–MgAl2O4 refractories. Mater Chem Phys2021; 267: 124663.
62.
CoelhoCAzaïsTLaurentG, et al. Efficiency of the refocused 31P−29Si MAS-J-INEPT NMR experiment for the characterization of silicophosphate crystalline phases and amorphous gels. Inorg Chem2007; 46(4): 1379–1387.
63.
HartmannPJanaCVogelJ, et al. 31P MAS and 2D exchange NMR of crystalline silicon phosphates. Chem Phys Lett1996; 258: 107–112.
64.
Skrzypczak-BonduelleABinetLDelpouxO, et al. EPR of radicals in primitive organic matter: a tool for the search of biosignatures of the most ancient traces of life. Appl Magn Reson2008; 33(4): 371–397.
65.
BourbinMGourierDDerenneS, et al. Dating carbonaceous matter in Archean cherts by electron paramagnetic resonance. Astrobiology2013; 13(2): 151–162.
66.
Fel’dmanEBLacelleS.Configurational averaging of dipolar interactions in magnetically diluted spin networks. J Chem Phys1996; 104(5): 2000–2009.
67.
BourbinMLe DuYBinetL, et al. Implementing a new EPR lineshape parameter for organic radicals in carbonaceous matter. Source Code Biol Med2013; 8(15): 1–11.
68.
RichardsEMurphyDMCheM.An EPR characterisation of stable and transient reactive oxygen species formed under radiative and non-radiative conditions. Res Chem Intermed2019; 45: 5763–5779.
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.