As part of a NASA program on high performance polymers for space applications, polymers containing silicon and phosphorus were prepared, characterized and exposed to an oxygen plasma under vacuum. Thin films of polyimides containing pendent siloxane groups, thermosetting resins contain ing silicon and poly(arylene ether)s containing phenylphosphine oxide were ex posed to a radio frequency generated oxygen plasma to assess their stability. The weight loss of the films was monitored as a function of exposure time and compared with that of Ultem® and Kapton® polyimide films of the same thick ness exposed under identical conditions. All of the experimental materials ex hibited better weight retention than either of the commercial polyimides. The thermosetting resins containing silicon and poly(arylene ether)s containing phosphine oxide exhibited only minor weight loss (0-5%) compared to that ex hibited by Ultem® (75-100%) and Kapton® (35-82%). Organic polymers con taining silicon are known to form silicates and silicon dioxide when exposed to atomic oxygen providing an in situ protective coating. Likewise, polymers con taining phosphorus have been shown to form an inorganic phosphate surface layer which subsequently provides protection from further oxidation. The same inherent characteristics that provide the polymers with atomic oxygen resis tance (i.e., high oxidation state or inorganic oxide formation) may also impart fire resistance. Materials containing phosphorus are known to exhibit good flame resistance. The chemistry, properties, limiting oxygen index and oxygen plasma resistance of these materials will be discussed.
Get full access to this article
View all access options for this article.