Polymeric biomaterial was synthesized by copolymerizing 50:50 mol% of monomers, glycidyl methacrylate and methyl methacrylate. Iodine atoms were then grafted to the epoxide groups of glycidyl methacrylate units, rendering the copolymer radiopaque. The percentage weight of iodine in the present copolymer was found to be as high as 23%. The iodinated copolymer showed higher glass transition temperature and thermal stability in comparison with unmodified polymer. Radiographic analysis showed that the copolymer possessed excellent radiopacity. The iodinated copolymer was cytocompatible to L929 mouse fibroblast cells. The in vivo toxicological evaluation by intracutaneous reactivity test of the copolymer extracts has revealed that the material was nontoxic. Subcutaneous implantation of iodinated copolymer in rats has shown that the material was well tolerated. Upon explantation and histological examination, no hemorrhage, infection or necrosis was observed. The samples were found to be surrounded by a vascularized capsule consisting of connective tissue cells. The results indicate that the iodinated copolymer is biocompatible and may have suitable applications as implantable materials.
MichelV. Polymeric biomaterials: strategies of the past vs. strategies of the future. Progr Polym Sci2007; 32: 755–761.
2.
YangJM. Polymerization of acrylic bone cement using differential scanning calorimetry. Biomaterials1997; 18: 1293–1298.
3.
HorakDMetalovaMRypacekFJ. New radiopaque poly HEMA-based hydrogel particles. J Biomed Mater Res1997; 34: 183–188.
4.
SaralidzeKAldenhoffYBKnetschMLKooleLH. Injectable polymeric microspheres with X-ray visibility. Preparation, properties, and potential utility as new traceable bulking agents. Biomacromolecules2003; 4(3): 793–798.
5.
MolinoLNTopoleskiLD. Effect of BaSO4 on the fatigue crack propagation rate of PMMA bone cement. J Biomed Mater Res1996; 31(1): 131–137.
6.
LewisGVan Hooy-CorstjensCSJBhattaramAKooleLH. Influence of the radiopacifier in an acrylic bone cement on its mechanical, thermal, and physical properties: barium sulfate-containing cement versus iodine-containing cement. J Biomed Mater Res B Appl Biomater2005; 73(1): 7787.
7.
JensenMEEvansAJMathisJMKallmesDFCloftHJDionJE. Percutaneous polymethylmethacrylate vertebroplasty in the treatment of osteoporotic vertebral body compression fractures: technical aspects. Am J Neuroradiol1997; 18: 1897– 1904.
8.
CottenABoutryNCortetBAssakerRDemondionXLeblondD. Percutaneous vertebroplasty: state of the art. Radiographics1998; 18: 311–320.
9.
RawlsHRGranierRJSmidJCabassoI. Thermomechanical investigation of poly(methylmethacrylate) containing an organobismuth radiopacifying additive. J Biomed Mater Res1996; 31: 339–343.
10.
Smid J, Delaviz Y and Cobasso, I. Homogeneous radiopaque polymer-organobismuth composites. US Patent 5256334.
11.
CabassoISmidJSureshS. Radiopaque miscible systems composed of poly(methyl methacrylate) and transition and nontransition metal salts: Spectroscopic, thermal, and radiographic characterization. J Appl Polym Sci1989; 38(9): 1653–1666.
12.
ZahariaCZecheruTMarculescuBFilmonRMabilleauGCincuC. Chemical structure of methylmethacrylate-2-[2',3',5'-triiodobenzoyl]oxoethyl methacrylate copolymer, radio-opacity, in vitro and in vivo biocompatibility. Acta Biomat2008; 4: 1762–1769.
13.
Van Hooy-CorstjensCSJSaralidzeKKnetschMLWEmansPJde HaanMWMagusinPCMM. New intrinsically radiopaque hydrophilic microspheres for embolization: synthesis and characterization. Biomacromolecules2008; 9(1): 84–90.
14.
LakshmiSJamesNRJayakrishnanA. Synthesis and polymerization of a new iodine-containing monomer. J Appl Polym Sci2003; 88: 2580–2584.
15.
Van Hooy-CorstjensCSJGovaertLESpoelstraABBulstraSKWetzelsGMKooleLH. Mechanical behaviour of a new acrylic radiopaque iodine-containing bone cement. Biomaterials2004; 25(13): 2657–2667.
DawleeSJayakrishnanAJayabalanM. Studies on novel radiopaque methyl methacrylate: glycidyl methacrylate based polymer for biomedical applications. J Mater Sci Mater Med2009; 20: 243–250.
19.
MottuFRufenachtDADoelkarE. Radiopaque polymeric materials for medical applications. Current aspects of biomaterial research. Invest Radiol1999; 34: 323–335.
20.
BoelenEJLewisGXuJSlotsTKooleLHVan Hooy-CorstjensCSJ. Evaluation of a highly-radiopaque iodine-containing acrylic bone cement for use in augmentation of vertebral compression fractures. J Biomed Mater Res2008; 86A(1): 76–88.
21.
ISO. Biological evaluation of medical devices. Part 5. Tests for cytotoxicity: In vitro methods. ISO-10993-5. Geneva: ISO, 2009.
22.
ISO. Biological evaluation of medical devices. Part 10. Test for irritation and delayed type hypersensitivity. Intracutaneous Reactivity Test. ISO-10993-10, Geneva: ISO, 2002.
23.
ISO. Biological evaluation of medical devices. Part 6. Tests for local effects after implantation, ISO-10993-6. Geneva: ISO, 2007.
24.
SafaKDNasirtabriziMH. Ring opening reactions of glycidyl methacrylate copolymers to introduce bulky organosilicon side chain substituents. Polym Bull2006; 57: 293–304.
25.
VasquezBGinebraMPGilFGPlanellJALópez BravoASan RománJ. Radiopaque acrylic cements prepared with a new acrylic derivative of iodo-quinoline. Biomaterials. 201999, pp. 2047–2053.
26.
Navarro-RodriguezDRodriguez-GonzalezFJRomero-GarciaJJimenez-RegaladoEJGuillonD. Chemical modification of glycidyl methacrylate polymers with 4-hydroxy-4′-methoxybiphenyl groups. Eur Polym J1998; 34: 1039–1045.
27.
PereiraIHAyresEPatrícioPSGóesAMGomideVSJuniorEP. Photopolymerizable and injectable polyurethanes for biomedical applications: synthesis and biocompatibility. Acta Biomater2010; 6(8): 3056–3066.
28.
VelayudhanSAnilkumarTVKumaryTVMohananPVFernandezACVarmaHK. Biological evaluation of pliable hydroxyapatite-ethylene vinyl acetate co-polymer composites intended for cranioplasty. Acta Biomater2005; 1(2): 201–209.
29.
KaoWJHiltnerAAndersonJLodoenGA. Theoretical analysis of in vivo macrophage adhesion and foreign body giant cell formation on strained poly(etherurethane urea) elastomers. J Biomed Mater Res1994; 28(7): 819–829.
30.
ZhaoOHAndersonJMHiltnerALodoenGAPayetCR. Theoretical analysis on cell size distribution and kinetics of foreign-body giant cell formation in vivo on polyurethane elastomers. J Biomed Mater Res1992; 26(8): 1019–1038.
31.
IhovaB. Biocompatibility of biomaterials: hemocompatibility, immunocompatiblity and biocompatibility of solid polymeric materials and soluble targetable polymeric carriers. Adv Drug Deliv Rev1996; 21(2): 157–176.