Poly(e-caprolactone) (PCL)/poly(glycolic acid) (PGA) scaffolds were fabricated via solid-state cryomilling along with compression molding and porogen leaching techniques. Four types of scaffolds were produced using four distinct cryomilling times. These scaffolds were evaluated for their in-vitro degradation behavior hydrolytically in phosphate buffer saline (PBS). The degradation profiles were investigated over a period of 60 days. The percentage of weight loss, percentage of water absorption, morphology, compressive, thermal, and material properties were studied as a function of degradation time. Weight loss and water absorption demonstrated a high correlation, which showed an increasing behavior with increase in cryomilling time and degradation time. Morphology of the scaffolds analyzed through scanning electron microscopy (SEM) revealed micro-cracks on the surface of the cylindrical struts due to hydrolytic attack and dissolution of hydrophilic PGA. Changes in compressive modulus and crystallinity over the degradation period and material properties were analyzed using X-ray powder diffraction (XRD), differential scanning calorimetry (DSC), and Fourier transform infrared (FTIR) spectroscopy. DSC and XRD results indicated that hydrolytic attack had taken place during degradation, resulting in moments of increased and decreased percent crystallinity. This study successfully brought forth the differences in resultant properties of the PCL/PGA scaffolds as a function of degradation time.
SungHJMeredithCJohnsonC. The effect of scaffold degradation rate on three dimensional cell growth and angiogenesis. Biomaterials2004; 25: 5735–5742.
2.
ChungCBurdickJA. Engineering cartilage tissue. Adv Drug Deliv Rev2008; 60: 243–262.
3.
GaonaLAGómez RibellesJLPerillaJE. Hydrolytic degradation of PLLA/PCL microporous membranes prepared by freeze extraction. Polym Degrad Stab2012; 97: 1621–1635.
4.
YaskoKLuciDBMCláudiaG. Investigation of irradiated biodegradable blends by FTIR and wide-angle X-ray diffraction. NUKLEONIKA2009; 54: 107–113.
5.
KobayashiTMatsumuraS. Enzymatic synthesis and properties of novel biodegradable and biobased thermoplastic elastomers. Polym Degrad Stab2011; 96: 2071–2079.
6.
EglinDMortisenDAliniM. Degradation of synthetic polymeric scaffolds for bone and cartilage tissue repairs. Soft Matter2009; 5: 938–947.
7.
GopferichA. Mechanisms of polymer degradation and erosion. Biomaterials1996; 17: 104–114.
8.
PuppiDChielliniFPirasAM. Polymeric materials for bone and cartilage repair. Prog Polym Sci2010; 35: 403–440.
9.
AndradyALBiodegradability of polymers. In: MarkJE (ed). Physical properties of polymers handbook, New York, NY: Springer, 2007, pp. 951–964.
10.
EastmondGCPoly (ε-caprolactone) blends. In: EastmondGCHöckerHKleeD (eds). Advances in polymer science: biomedical applications polymer blends, New York, NY: Springer Berlin-Heidelberg, 2000, pp. 59–223. .
11.
WanYWuHCaoX. Compressive mechanical properties and biodegradability of porous poly(caprolactone)/chitosan scaffolds. Polym Degrad Stab2008; 93: 1736–1741.
12.
JonesDSDjokicJMcCoyCP. Poly(epsilon-caprolactone) and poly(epsilon-caprolactone)-polyvinylpyrrolidone-iodine blends as ureteral biomaterials: characterisation of mechanical and surface properties, degradation and resistance to encrustation in vitro. Biomaterials2002; 23: 4449–4458.
13.
CuiHSinkoPJ. The role of crystallinity on differential attachment/proliferation of osteoblasts and fibroblasts on poly (caprolactone-co-glycolide) polymeric surfaces. Front Mater Sci2012; 6: 47–59.
14.
BrownMFarrarD. Development of bioresorbable polymers in orthopaedics. Plast Rubber Compos2008; 37: 46–49.
15.
NairLSLaurencinCT. Biodegradable polymers as biomaterials. Prog Polym Sci2007; 32: 762–798.
16.
AghdamRMNajarianSShakhesi. Investigating the effect of PGA on physical and mechanical properties of electrospun PCL/PGA blend nanofibers. J Appl Polym Sci2012; 124: 123–131.
17.
OttenJEWiedmann-Al-AhmadMJahnkeH. Bacterial colonization on different suture materials–a potential risk for intraoral dentoalveolar surgery. J Biomed Mater Res B Appl Biomater2005; 74: 627–635.
18.
BramfeldtHVermetteP. Enhanced smooth muscle cell adhesion and proliferation on protein modified polycaprolactone-based copolymers. J Biomed Mater Res A2009; 88: 520–530.
19.
MehdinavazRNajarianSEmamiHS. In vitro evaluation of biodegradable poly (e-caprolactone)-based blended nanofibrous scaffold for soft tissue engineering. Int J Acad Res2011; 3: 477–483.
20.
JonnalagaddaJBRiveroIV. Effect of cryomilling times on the resultant properties of porous biodegradable poly(e-caprolactone)/poly(glycolic acid) scaffolds for articular cartilage tissue engineering. J Mech Behav Biomed Mater2014; 40: 33–41.
StranzMKosterUKatzenbergF. Formation of polymer blends and nano-composites by cryogenic mechanical milling. J Metastable Nanocryst Mater2005; 24-25: 609–614.
23.
Terife G and Narh KA. Creating polymer-carbon nanotubes nanocomposites by cryomilling. In: ANTEC 2009 plastics: annual technical conference proc. Chicago, IL, 22--24 June 2009, pp.349--353.
24.
SmithAPAdeHBalikCM. Cryogenic mechanical alloying of poly (methyl methacrylate) with polyisoprene and poly (ethylene-alt-propylene). Macromolecules2000; 33: 2595–2604.
25.
GhoshSVianaJCReisRL. The double porogen approach as a new technique for the fabrication of interconnected poly(L-lactic acid) and starch based biodegradable scaffolds. J Mater Sci Mater Med2007; 18: 185–193.
26.
ReignierJHuneaultMA. Preparation of interconnected poly (ε-caprolactone) porous scaffolds by a combination of polymer and salt particulate leaching. Polymer2006; 47: 4703–4717.
27.
LebourgMAntonJSGomez RibellesJL. Porous membranes of PLLA– PCL blend for tissue engineering applications. Eur Polym J2008; 44: 2207–2218.
28.
Standard specification for poly(glycolide) and poly(glycolide-co-lactide) resins for surgical implants with mole fractions greater than or equal to 70% Glycolide. ASTM Standard F 2313-08, 2008.
29.
LamCXSavalaniMMTeohSH. Dynamics of in vitro polymer degradation of polycaprolactone-based scaffolds: accelerated versus simulated physiological conditions. Biomed Mater2008; 3: 1–15.
30.
DıazESandonisIPuertoI. In vitro degradation of PLLA/nHA composite scaffolds. Polym Eng Sci2014; 54: 2571–2578.
31.
CorreloVMBoeselLFPinhoE. Melt-based compression-molded scaffolds from chitosan polyester blends and composites – morphology and mechanical properties. J Biomed Mater Res A2009; 91: 489–504.
32.
PengHHanYLiuT. Morphology and thermal degradation behaviour of highly exfoliated CoAl-layered double hydroxide/polycaprolactone nanocomposites prepared by simple solution intercalation. Thermochim Acta2010; 502: 1–7.
33.
ZongXHWangZGHsiaoBS. Structure and morphology changes in absorbable poly(glycolide) and poly(glycolide-co-lactide) during in vitro degradation. Macromolecules1999; 32: 8107–8114.
34.
Castilla-CortázarIMás-EstellésJMeseguer-Dueñas. Hydrolytic and enzymatic degradation of a poly(ε-caprolactone) network. Polym Degrad Stab2012; 97: 1241–1248.
35.
PanZDingJ. Poly(lactide-co-glycolide) porous scaffolds for tissue engineering and regenerative medicine. Interface Focus2012; 2: 366–377.
36.
SabirMIXuXLiL. A review on biodegradable polymeric materials for bone tissue engineering applications. J Mater Sci2009; 44: 5713–5724.