In vivo Testing of a Biostable Polyurethane

Abstract

At present all the commercially available "medical grade" urethane elastomers exhibit a phenomenon known as environmental stress cracking (ESC). This phenomenon is characterized by surface microcracking when the elastomer is elongated while in vivo. The degree of strain that is required to initiate microcracking varies from composition to composition. It has been found that harder compounds generally tend to have a higher strain threshold than corresponding softer ones.

We theorized that this degradation occurs when certain enzymes (present only in vivo) attack and break down the ether linkages that link the polymer molecules together. Those elastomers that contain more ether linkages (such as the softer compositions) appear to microcrack more easily than elastomers with fewer ether linkages (such as the harder ones).

The molecular composition of ChronoFlex™ urethane has been chosen so that the finished elastomer will be free of ether linkages; thus, it is expected to be immune from environmental stress cracking.

Keywords

biostable polyurethanes environmental stress cracking surface fissuring microcracking ether-free polyurethanes medical grade polyurethanes.

Get full access to this article

View all access options for this article.

References

Szycher, M. and W.A. McArthur. 1985. "Surface Fissuring of Polyurethanes following in vivo Exposure," Corrosion and Degradation of Implant Materials, ASTM STP 859, Fraker and Griffin , eds., Philadelphia, PA, pp. 308-321.

Szycher, M. , D. Dempsey and V.L. Poirier. 1984. "Surface Fissuring of Polyurethane-Based Pacemaker Leads," Second World Congress on Biomaterials , 1984, Society for Biomaterials, p. 24.

Williams, D.F. 1977. J. Bioeng., 1:279-294.

Phua, S.K. , E. Castillo , J.M. Anderson and A. Hiltner. 1987. "Biodegradation of a Polyurethane in vitro," J. Biomed. Mat. Res., 21:231-246.

Szycher, M. 1988. "Biostability of Polyurethane Elastomers: A Critical Revieiw ", J. Biomat. Appl., 3(2):297-402.

Stokes, K.B. 1988. "Polyether Polyurethanes: Biostable or Not?" J. Biomat. Appl., 3(2):228-259.

Stokes, K.B. and P. Urbanski. 1989. "The Biostability of Polyether Polyurethanes: In vivo Degradation Mechanisms and Test Methods," Proceedings, Third Annual Seminar on Biodegradation of Polyurethanes, Coral Gables, Florida, 1989, Lancaster, PA: Technomic Publishing Co., Inc.

Stokes, U.P. and K. Cobian. 1987. "New Test Methods for the Evaluation of Stress Cracking and Metal-Catalyzed Oxidation in Implanted Polymers," Polyurethanes in Biomed. Eng. II, H. Planck et al., eds., Amsterdam: Elsevier , pp. 109-128.

Coury, A.J. , C.M. Hobot , et al. 1990. "A New Family of Implantable Biostable Polyurethanes ," Transactions, Soc. for Biomaterials, 16th Annual Meeting, 1990, p. 158.