Impact of Nd-YAG Laser Drilling on the Fatigue Characteristics of APC-2A/AS4 Thermoplastic Composite Material

Abstract

Both carbon fiber thermoset and thermoplastic materials can be drilled using a laser. This, however, results in significant damage to the material, but the extent to which this would reduce the fatigue life was not known. Studies have been conducted to evaluate this for an aerospace application, which required a light-weight, but perforated, skin panel through which air could be sucked. The objective has been to determine the impact on the fatigue life of quasi-isotropic APC-2A/AS4 due to Nd-YAG laser-drilled holes (~120 μm diameter, spaced ~500 μm apart). Static tensile tests indicate a 29% reduction in strength. The maximum stress versus cycles to failure (S—N) relationship is represented by a power law function: S=KN^m. The laser drilling has been seen to reduce the value of K (coefficient of fatigue strength), but the value of m (fatigue strength degradation exponent), which was determined from nonperforated specimens, was unchanged.

Keywords

Nd-YAG laser drilling APC-2A/AS4 thermoplastic laminates fatigue damage fatigue life.

References

Joslin, R.D. (1998). Overview of Laminar Flow Control, NASA TP-1998-208705 , Langley Research Centre, USA.

Boeing (1999). High Reynolds Number Hybrid Laminar Flow Control (HLFC) Flight Experiment, NASA CR-1999-209325/CR-1999-209326 , Boeing Commercial Airplane Group, Seattle, USA.

Young, T.M. (2004). Fuel Sensitivity Analyses for Active Drag Reduction Systems, Aeronautical Journal of the Royal Aeronautical Society , 108: 215-221.

Young, T. , Mahony, B. , McClafferty, A. , Corish, J. , Humphreys, B. and Totland, E. (2003). Durability of Hybrid Laminar Flow Control (HLFC) Surfaces, Journal of Aerospace and Technology, 7: 181-190.

Matthams, T.J. and Clyne, T.W. (1999). Mechanical Properties of Long-Fibre Thermoplastic Composites with Laser Drilled Microperforations: 1. Effect of Perforations in Consolidated Material, Composites Science and Technology, 59: 1169-1180.

Rodden, W.S.O. , Kudesia, S.S. , Hand , D.P. and Jones, J.D.C. (2002). A Comprehensive Study of the Long Pulse Nd:YAG Laser Drilling of Multi-Layer Carbon Fibre Composites , Optic Communications, 210: 319-328.

Young, T. and O'Driscoll, D. (2002). Impact of Nd-YAG Laser Drilled Holes on the Strength and Stiffness of Laminar Flow Carbon Fibre Reinforced Composite Panels, J. Composites Part A 33: 1-9.

Young, T.M. , Humphreys, B. and Fielding, J.P. (2001). Investigation of Hybrid Laminar Flow Control (HLFC) Surfaces, J. Aircraft Design, 4: 127-146.

Astm D 3039/D 3039M-95a. (1999). Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials, Vol. 15.03, pp. 99-109.

10.

Astm D 5766/D 5766M-02. Test Method for Open Hole Tensile Strength of Polymer Matrix Composite Laminates, Vol. 15.03.

11.

Astm D 3479/D 3479M-96. Standard Test Method for Tension-Tension Fatigue of Polymer Matrix Composite Materials, Vol. 15.03 .

12.

Jen M.-H.R. and Lee C.-H. (1998). Strength and Life in Thermoplastic Composite Laminates Under Static and Fatigue Loads, Part 1: Experimental, Int. J. Fatigue, 20: 605-615.

13.

Curtis, D.C. , Moore, D.R. , Slater, B. and Zahlan, N. (1988). Fatigue Testing of Multi-Angle Laminates of CF/PEEK , J. Composites, 19: 446-452.