Catalyst-Transfer Condensation Polymerization for the Synthesis of Well-Defined Polythiophene with Hydrophilic Side Chain and of Diblock Copolythiophene with Hydrophilic and Hydrophobic Side Chains

Abstract

Chain-growth condensation polymerization of 2-bromo-5-chloromagnesio-3-[2-(2-metho-xyethoxy)ethoxy]methylthiophene (2) with Ni catalysts was studied, and the block copolymer of poly2 and poly(3-hexylthiophene) was synthesized by this polymerization method. The polymerization of 2 depended on the ligands of the Ni catalyst, and poly2 with the lowest polydispersity was obtained when 1,2-bis(diphenylphosphino)ethane (dppe) was used as the ligand. The linear relationships between the conversion of 2 and Mn of the polymer and between the feed ratio of 2 to the Ni catalyst and Mn of the polymer indicate that this polymerization proceeds in a chain-growth polymerization manner via a catalyst-transfer condensation polymerization mechanism. The block copolymerization of 2 and 2-bromo-5-chloromagnesio-3-hexylthiophene (1) was then carried out in four ways by changing the order of polymerization of the two monomers and the catalysts. It turned out that the block copolymer was obtained without the formation of the homopolymers by the polymerization of 1 with Ni(dppe)Cl2 or Ni(dppp)Cl2 (dppp = 1,2-bis(diphenylphosphino)propane), followed by the postpolymerization of 2. Of the two catalysts, Ni(dppe)Cl2 resulted in narrower polydispersity of the block copolymer.

Keywords

Chain-growth polymerization condensation polymerization polycondensation polythiophene block copolymers Ni-catalysts

Get full access to this article

View all access options for this article.

References

Weissbach

, and Pestka

(1977). Molecular Mechanism of Protein Biosynthesis, Academic Press, New York.

Bermek

(1985). Mechanism of Protein Synthesis. Structure-function Relations, Control Mechanisms, and Evolutionary Aspects, Springer-Verlag, New York.

Kornberg

(1960). Biologic synthesis of deoxyribonucleic acid, Science, 131: 1503–1508.

Yokozawa

, Asai

, Sugi

, Ishigooka

, and Hiraoka

(2000). Chain-Growth Polycondensation for Nonbiological Polyamides of Defined Architecture, J. Am. Chem. Soc., 122: 8313–8314.

Shibasaki

, Araki

, Okazaki

, and Ueda

(2002). Control of molecular weight distribution in polycondensation polymers. Polyamide synthesis, Polym. J., 34: 261–266.

Yokozawa

, Muroya

, Sugi

, and Yokoyama

(2005) Convenient method of chain-growth poly-condensation for well-defined aromatic polyamides, Macromol. Rapid Commun., 26: 979–981.

Sugi

, Yokoyama

, Furuyama

, Uchiyama

, and Yokozawa

(2005). Inductive Effect-Assisted Chain-Growth Polycondensation. Synthetic Development from para- to meta-Substituted Aromatic Polyamides with Low Polydispersities, J. Am. Chem. Soc., 127: 10172–10173.

Washita

, Yokoyama

, and Yokozawa

(2005). Synthesis of well-defined aromatic polyesters by chain-growth polycondensation under suppression of transesterification, J. Polym. Sci., Part A: Polym. Chem., 43: 4109–4117.

Yokozawa

, Suzuki

, and Hiraoka

(2001). Aromatic Polyethers with Low Polydispersities from Chain-Growth Polycondensation, J. Am. Chem. Soc., 123: 9902–9903.

10.

Suzuki

, Hiraoka

, Yokoyama

, and Yokozawa

(2003). Chain-Growth Polycondensation for Aromatic Polyethers with Low Polydispersities: Living Polymerization Nature in Polycondensation, Macro-molecules, 36: 4756–4765.

11.

Yokozawa

, Taniguchi

, Suzuki

, and Yokoyama

(2002). Chain-growth polycondensation of monomer consisting of two aromatic rings: synthesis of well-defined poly(ether sulfone) from 4-fluoro-4'-hydroxydiphenyl sulfone, J. Polym. Sci., Part A: Polym. Chem., 40: 3460–3464.

12.

Shibasaki

, Araki

, Nagahata

, and Ueda

(2005). Control of molecular weight distribution in polycondensation polymers 2. Poly(ether ketone) synthesis, Eur. Polym. J., 41: 2428–2433.

13.

Yokozawa

, Ogawa

, Sekino

, Sugi

, and Yokoyama

(2002). Chain-Growth Polyconden-sation for Well-Defined Aramid. Synthesis of Unprecedented Block Copolymer Containing Aramid with Low Polydispersity, J. Am. Chem. Soc., 124: 15158–15159.

14.

Chavan

N.N.

, Ciferri

, Dell'Erba

, Novi

, and Renamayor

C.S.

(1996). Tailored rigid-flexible block copolymers. Part 1. Synthesis of diblocks of poly(p-benzamide) and poly(m-phenyleneisophthala-mide), Macromol. Chem. Phys., 197: 2415–2428.

15.

Yokoyama

, Miyakoshi

, and Yokozawa

(2004). Chain-growth polymerization for poly(3-hexyl-thiophene) with a defined molecular weight and a low polydispersity, Macromolecules, 37: 1169–1171.

16.

Miyakoshi

, Yokoyama

, and Yokozawa

(2004). Synthesis of poly(3-hexylthiophene) with a narrower polydispersity, Macromol. Rapid Commun., 25: 1663–1666.

17.

Iovu

M.C.

, Sheina

E.E.

, Gil

R.R.

, and McCullough

R.D.

(2005). Experimental Evidence for the Quasi-“Living” Nature of the Grignard Metathesis Method for the Synthesis of Regioregular Poly(3-alkylthiophenes), Macromolecules, 38: 8649–8656.

18.

Miyakoshi

, Yokoyama

, and Yokozawa

(2005). Catalyst-Transfer Polycondensation. Mechanism of Ni-Catalyzed Chain-Growth Polymerization Leading to Well-Defined Poly(3-hexylthiophene), J. Am. Chem. Soc., 127: 17542–17547.

19.

Adachi

, Miyakoshi

, Yokoyama

, and Yokozawa

(2006). Synthesis of Well-Defined Polythio-phene with Oxyethylene Side Chain: Effect of Phosphine Ligands on Catalyst-Transfer Polycondensation, Macromolecules, 39: 7793–7795.

20.

McCullough

R.D.

, and Williams

S.P.

(1993). Toward tuning electrical and optical properties in conjugated polymers using side-chains: highly conductive head-to-tail, heteroatom functionalized polythiophenes, J. Am. Chem. Soc., 115: 11608–11609.

21.

Sheina

E.E.

, Khersonsky

S.M.

, Jones

E.G.

, and McCullough

R.D.

(2005). Highly Conductive, Re-gioregular Alkoxy-Functionalized Polythiophenes: A New Class of Stable, Low Band Gap Materials, Chem. Mater., 17: 3317–3319.

22.

van Beek

, Jenneskens

L.W.

, Zdravkova

A.N.

, Van der Eerden

J.P.J.M.

, and van Walree

C.A.

(2005). Polythiophenes containing oligo(oxyethylene) side chains as a thin film on a ZnSe single crystal surface, Macromol. Chem. Phys., 206: 1006–1014.

23.

Langeveld-Voss

B.M.W.

, Waterval

R.J.M.

, Janssen

R.A.J.

, and Meijer

E.W.

(1999). Principles of “Majority Rules” and “Sergeants and Soldiers” Applied to the Aggregation of Optically Active Polythiophenes: Evidence for a Multichain Phenomenon, Macromolecules, 32: 227–230.

24.

Loewe

R.S.

, Ewbank

P.C.

, Liu

, Zhai

, and McCullough

R.D.

(2001). Regioregular, Head-to-Tail Coupled Poly(3-alkylthiophenes) Made Easy by the GRIM Method: Investigation of the Reaction and the Origin of Regioselectivity, Macromolecules, 34: 4324–4333.