The Atomic Oxygen Erosion Depth and Cone Height of Various Materials at Hyperthermal Energy

Abstract

Atomic oxygen readily reacts with most spacecraft polymer materials exposed to the low Earth orbital (LEO) environment. If the atomic oxygen arrival comes from a fixed angle of impact, the resulting erosion will foster the development of a change in surface morphology as material thickness decreases. Hydrocarbon and halopolymer materials, as well as graphite, are easily oxidized and textured by directed atomic oxygen in LEO at energies of ∼4.5 eV. What has been curious is that the ratio of cone height to erosion depth is quite different for different materials. The formation of cones under fixed direction atomic oxygen attack may contribute to a reduction in material tensile strength in excess of that which would occur if the cone height to erosion depth ratio was very low because of greater opportunities for crack initiation. In an effort to understand how material composition affects the ratio of cone height to erosion depth, an experimental investigation was conducted on 18 different materials exposed to a hyperthermal energy directed atomic oxygen source (∼70 eV). The materials were first salt-sprayed to provide microscopic local areas that would be protected from atomic oxygen. This allowed erosion depth measurements to be made by scanning microscopy inspection. The polymers were then exposed to atomic oxygen produced by an end Hall ion source that was operated on pure oxygen. Samples were exposed to an atomic oxygen effective fluence of 1.0 1 10²⁰ atoms cm^-2 based on Kapton H polyimide erosion. The average erosion depth and average cone height were determined using field emission scanning electron microscopy (FESEM). The experimental ratio of average cone height to erosion depth is compared to polymer composition and other properties.

Keywords

Atomic Oxygen Polymers Space Environment Erosion Depth Cone Height

Get full access to this article

View all access options for this article.

References

Banks, B.A. , de Groh, K.K. and Miller, S.K. (2004). Low Earth Orbital Atomic Oxygen Interactions With Spacecraft Materials. NASA TM-2004-213400 and paper presented at the Fall 2004 Meeting of the Materials Research Society, Boston, Massachusetts, November 29-December 3.

Banks, B.A. , Waters, D.L. , Thorson, S.D. , de Groh, K.K. , Snyder, A. , Miller, S. (2006). Comparison of Atomic Oxygen Erosion Yields of Materials at Various Energies and Impact Angles. In Proceedings of ISMSE-ICPMSE 2006, Collioure, France.

Banks, B.A. (1997). The Use of Fluoropolymers in Space Applications . In Modern Fluoropolymers: High Performance Polymers for Diverse Applications, J. Scheirs (ed.), John Wiley & Sons, Ltd.

de Groh, K. Banks, B. , McCarthy, C. , Rucker, R. , Berger, L. , and Roberts, L. (2006). Analysis of the MISSE PEACE Polymers International Space Station Environmental Exposure Experiment. In Proceedings of 10th International Symposium on Materials in a Space Environment , Collioure, France, June 19-23.

Astm E 2089-00 (2000). Standard Practices for Ground Laboratory Atomic Oxygen. Interaction Evaluation of Materials for Space Applications.

Kahn, J.R. and Robinson, R.S. (1989). NASA contract report, Front Range Research, Fort Collins, CO, Sept. 28, 1989.

Banks, B.A. , Rutledge, S.K. , Chan, A. and Sahota, M. (2001). The Development of Surface Roughness and Implications for Cellular Attachment in Biomedical Applications. NASA TM 2001-211288, presented at the 2001 Fall Meeting of the Materials, Research Society, Boston, MA, November 26-30.