Degradation Property of Commercially Available Si-containing Polyimide in Simulated Atomic Oxygen Environments for Low Earth Orbit

Abstract

Real-time measurement of the erosion rate of a commercially available Si-containing polyimide (BSF30) under hyperthermal atomic oxygen (AO) beam exposure condition, which simulates the AO environment in low Earth orbit (LEO), was performed. It was found that the erosion rate of BSF30 decreased with increasing AO fluence and it reached as low as 4% of the standard PMDA-ODA polyimide. X-ray photoelectron spectroscopy confirmed that the surface of AO-exposed BSF30 was covered by a SiO₂ layer which functioned as a protective coating. In contrast, an SiO₂ surface layer thick enough to protect bulk BSF30 was not formed by thermal AO, which was generated by vacuum ultraviolet exposure in an O₂ atmosphere. Exposure to hyperthermal AO collision in LEO can also form an SiO₂ layer which enables the surface to be self-healing and is desirable for a polyimide that would be used in LEO.

Keywords

Atomic oxygen polyimide protective coating silicon low Earth orbit

Get full access to this article

View all access options for this article.

References

Gilmore G.D. ( 1994). In: Satellite Thermal Control Handbook, Chapter IV, The Aerospace Corporation Press, El Segundo, CA. 4-73-4-84.

Banks, B.A. , Mirtich, M.J. , Rutledge, S.K. and Swec, D.M. (1985). Sputtered Coating for Protection of Spacecraft Polymers, Thin Solid Films, 127(1-2): 107-114.

Sanders, J.H. and Tatarchuk, B.J. (1990). Pinhole Plugging Characteristics of Silica/iron/silver Protective Coating in Atomic Oxygen Environments, Thin Solid Films, 192(1): 79-95.

Tagawa, M. and Minton, T.K. ( 1996). Effect of Ion-implantation on Atomic Oxygen Reactivity with Polyimide Films in Low Earth Orbit, Proceedings of the 20th International Conference on Space Technology and Science, Morioka, Japan, 96-b-07.

Rutledge, S.K. and Mihelcic, J.A. (1989). Undercutting of Defects in Thin Film Protective Coating on Polymer Surfaces Exposed to Atomic Oxygen, Surf. Coating Technol, 39/40(2): 607-615.

Banks, B.A. , Snyder, A. , Miller, S.K. and Demko, R. ( 2002). Issues and Consequences of Atomic Oxygen Undercutting of Protected Polymers in Low Earth Orbit, NASA/TM- 2002-211577.

Gonzalez R.I. , Tomczak, S.J. , Minton, T.K. , Brunsvold, A.L. and Hoflund, G.B. ( 2003). Synthesis and Atomic Oxygen Erosion Testing of Space-survivable POSS (polyhedral oligomeric silsesquioxane) Polyimides, In: Proc. 9th International Symposium on Materials in a Space Environment, ESA Publications Division, Noordwijk, The Netherlands, ESA-540, pp. 113-120.

Tagawa, M. , Yokota, K. , Ohnae , N. and Kenoshita, H. (2000). Volume Diffusion of Atomic Oxygen in a-SiO2 Protective Coating, High Perform. Polym. , 12: 53-63.

Matijasevic, V. , Garwin, E.L. and Hammond, R.H. (1990). Atomic Oxygen Detection by a Silver-coated Quartz Deposition Monitor, Rev. Sci. Instr. , 61(6): 1747-1749.

10.

Silverman, B.D. , Bartha, J.W. , Clabes, J.G. , Ho , P.S. and Rossi, A.R. (1986). Molecular Orbital Analysis of the XPS Spectra of PMDA-ODA Polyimide and its Polyamic Acid Precursor, J. Polym. Sci., A: Polym. Chem. , 24: 3325-3333.

11.

Moulder, J.F. , Stickle, W.F. , Sobol, P.E. and Bomben, K.D. (1992). Handbook of X-ray Photoelectron Spectroscopy, Perkin-Elmer Corporation, Eden Prairie, MN.

12.

Beamson, G. and Briggs, D. ( 1992). High Resolution XPS of Organic Polymers: Scienta 3000 database, John Wiley and Sons, Chichester.

13.

Minton, T.K. , Garton, D.J. , Zhang, J. and Seale, J. ( 1999). Materials Degradation in Low Earth Orbit: an Oxygen Atom’s Accomplice, In: Proc. 6th Japan International SAMPE Symposium, Japan Chapter of SAMPE, Tokyo, pp. 1159-1162.

14.

Tagawa, M. , Yokota, K. , Ohnae, N. , Kenoshita, H. and Umeno, M. , (2001). Oxidation Properties of Hydrogen-terminated Si (001) Surfaces Following Use of a Hyperthermal Broad Atomic Oxygen Beam at Low Temperatures, Jpn J. Appl. Phys., 40: 6152-6156.