To improve the radical oxidative stability, a series of covalently cross-linked blend membranes have been prepared from a sulfonated poly(sulfide sulfone) with 80% degree of sulfonation (SPSSF80) and a polybenzimidazole with pendant amino groups (H2N-PBI) using glycidyloxypropyltrimethoxysilane (KH-560) and bisphenol A diglycidyl ether (BADGE) as cross-linkers. The resulting cross-linked membranes show increased tensile strength but slightly decreased elongation at break compared with the plain SPSSF80. The radical oxidative stability of the blend membranes is significantly improved due to the synergic action of the covalent cross-linking and the presence of the PBI component. For example, the cross-linked membrane with the composition of SPSSF80/H2N-PBI/KH-560 = 7/1/3 started to break into pieces after being soaked in Fenton’s reagent for 98 min, which is about 4 times longer than that (20 min) of the plain SPSSF50 (degree of sulfonation = 50%). The covalent cross-linking is also essential to suppress membrane swelling and to enhance membrane water stability. The KH-560-cross-linked blend membranes tend to show higher proton conductivities at low relative humidities than the BADGE-cross-linked one due to the hydrophilic silica network in the former. At fully hydrated state, the cross-linked membranes generally show high proton conductivities comparable with that of Nafion112®.
AsanoNAokiMSuzukiSMiyatakeKUchidaHWatanabeM. Aliphatic/aromatic polyimide ionomers as a proton conductive membrane for fuel cell applications. J Am Chem Soc2006; 128: 1762–1769.
3.
GotoKRozhanskiiIYamakawaY. Development of aromatic polymer electrolyte membrane with high conductivity and durability for fuel cell. Polym J2009; 41: 95–104.
4.
ZhuXZhangHLiangYZhangYLuoQBiC. Challenging reinforced composite polymer electrolyte membranes based on disulfonated poly(arylene ether sulfone)-impregnated expanded PTFE for fuel cell applications. J Mater Chem2007; 17: 386–397.
5.
XuNGuoXFangJYinJYuanMChenB. Preparation and properties of crosslinked sulphonated poly(sulphide sulphone) membranes for fuel cell applications. Fuel Cells2009; 9: 363–371.
6.
LuJTangHLuSWuHJiangSP. A novel inorganic proton exchange membrane based on self-assembled HPW-meso-silica for direct methanol fuel cells. J Mater Chem2011; 21: 6668–6676.
7.
OkamotoK-IYinYYamadaOIslamMDNHondaTMishimaT. Methanol permeability and proton conductivity of sulfonated co-polyimide membranes. J Membr Sci2005; 258: 115–122.
8.
LinC-CChangC-BWangY-Z. Preparation and properties of cross-linked sulfonated poly(imide-siloxane) for polymer electrolyte fuel cell application. J Power Sources2013; 223: 277–283.
9.
ZhouSHaiSDKimD. Cross-linked poly(arylene ether ketone) proton exchange membranes with high ion exchange capacity for fuel cells. Fuel Cells2012; 12: 589–598.
10.
MiyaharaTHayanoTMatsunoSWatanabeMMiyatakeK. Sulfonated polybenzophenone/poly(arylene ether) block copolymer membranes for fuel cell applications. ACS Appl Mater Interfac2012; 4: 2881–2884.
11.
BorupRMeyersJPivovarBKimYSMukundanRGarlandN. Scientific aspects of polymer electrolyte fuel cell durability and degradation. Chem Rev2007; 107: 3904–3951.
12.
HubnerGRodunerE. EPR investigation of HO· radical initiated degradation reactions of sulfonated aromatics as model compounds for fuel cell proton conducting membranes. J Mater Chem1999; 9: 409–418.
13.
LawrenceJYamaguchiT. The degradation mechanism of sulfonated poly(arylene ether sulfone)s in an oxidative environment. J Membr Sci2008; 325: 633–640.
SchusterMKreuerK-DAndersenHTMaierJ. Sulfonated poly(phenylene sulfone) polymers as hydrolytically and thermooxidatively stable proton conducting ionomers. Macromolecules2007; 40: 598–607.
16.
WuSQiuZZhangSYangXYangFLiZ. The direct synthesis of wholly aromatic poly(p-phenylene)s bearing sulfobenzoyl side groups as proton exchange membranes. Polymer2006; 47: 6993–7000.
17.
ZhangGGuoXFangJChenKOkamotoK-I. Preparation and properties of covalently cross-linked sulfonated copolyimide membranes containing benzimidazole groups. J Membr Sci2009; 326: 708–713.
18.
ZhaoDLiJSongM-KYiBZhangHLiuM. A durable alternative for proton-exchange membranes: sulfonated poly(benzoxazole thioether sulfone)s. Adv Energy Mater2011; 1: 203–211.
19.
XingDKerresJ. Improved performance of sulfonated polyarylene ethers for proton exchange membrane fuel cells. Polym Adv Technol2006; 17: 591–597.
20.
DanilczukMSchlickSComsFD. Cerium(III) as a stabilizer of perfluorinated membranes used in fuel cells: in situ detection of early events in the ESR resonator. Macromolecules2009; 42: 8943–8949.
21.
ZhaoDYiBLZhangHMYuHMWangLMaYW. Cesium substituted 12-tungstophosphoric (CsxH3−xPW12O40) loaded on ceria-degradation mitigation in polymer electrolyte membranes. J Power Sources2009; 190: 301-–306.
HanMZhangGLiMWangSLiuZLiH. Sulfonated poly(ether ether ketone)/polybenzimidazole oligomer/epoxy resin composite membranes in situ polymerization for direct methanol fuel cell usages. J Power Sources2011; 196: 9916–9923.
24.
XuNGuoXFangJXuHYinJ. Synthesis of novel polybenzimidazoles with pendant amino groups and the formation of their crosslinked membranes for medium temperature fuel cell applications. J Polym Sci A: Polym Chem2009; 47: 6992–7002.
25.
XuHChenKGuoXFangJYinJ. Synthesis of novel sulfonated polybenzimidazole and preparation of cross-linked membranes for fuel cell application. Polymer2007; 48: 5556–5564.
26.
HouHWangSJiangQJinWJiangLSunG. Durability study of KOH doped polybenzimidazole membrane for air-breathing alkaline direct ethanol fuel cell. J Power Sources2011; 196: 3244–3248.
27.
XiaZYuanSJiangGGuoXFangJLiuL. Polybenzimidazoles with pendant quaternary ammonium groups as potential anion exchange membranes for fuel cells. J Membr Sci2012; 390–391: 152–159.
28.
WainrightJSWangJ-TWengDSavinellRFLittM. Acid-doped polybenzimidazoles: a new polymer electrolyte. J Electrochem Soc1995; 142: L121–L123.
29.
LiQHeRJensenJOBjerrumNJ. PBI-based polymer membranes for high temperature fuel cells-preparation, characterization and fuel cell demonstration. Fuel Cells2004; 4: 147–159.
30.
YuSXiaoLBenicewiczBC. Durability studies of PBI-based high temperature PEMFCs. Fuel Cells2008; 8: 165–174.
31.
XiaoLZhangHScanlonERamananthanLSChoeE-WRogersD. High-temperature polybenzimidazole fuel cell membranes via a sol-gel process. Chem Mater2005; 17: 5238–5333.
32.
LinHLHsiehYSChiuCWYuTLChenLC. Durability and stability test of proton exchange membrane fuel cells prepared from polybenzimidazole/poly(tetrafluoro ethylene) composite membrane. J Power Sources2009; 193: 170–174.
33.
XiaoLZhangHJanaTScanlonEChenRChoeE-W. Synthesis and characterization of pyridine-based polybenzimidazoles for high temperature polymer electrolyte membrane fuel cell applications. Fuel Cells2005; 5: 287–295.
34.
LiuZTsouY-MCalundannGCastroED. New process for high temperature polybenzimidazole membrane production and its impact on the membrane and the membrane electrode assembly. J Power Sources2011; 196: 1055–1060.
35.
ShengLXuHGuoXFangJFangLYinJ. Synthesis and properties of novel sulfonated polybenzimidazoles from disodium 4,6-bis(4-carboxyphenoxy)benzene-1,3-disulfonate. J Power Sources2011; 196: 3039–3047.
36.
PeronJRuizEJonesDJRoziereJ. Solution sulfonation of a novel polybenzimidazole A proton electrolyte for fuel cell application. J Membr Sci2008; 314: 247–256.
37.
QingSHuangWYanD, Synthesis and characterization of thermally stable sulfonated polybenzimidazoles. Eur Polym J2005; 41: 1589–1595.
38.
QingSHuangWYanD. Synthesis and characterization of thermally stable sulfonated polybenzimidazoles obtained from 3,30-disulfonyl-4,4′-dicarboxyldiphenylsulfone. J Polym Sci A: Polym Chem2005; 43: 4363–4372.
39.
NgFPeronJJonesDJRoziereJ. Synthesis of novel proton-conducting highly sulfonated polybenzimidazoles for PEMFC and the effect of the type of bisphenyl bridge on polymer and membrane properties. J Polym Sci A: Polym Chem2011; 49: 2107–2117.
40.
ZhengHLuoHMatheM. Proton exchange membranes based on poly(2,5-benzimidazole) and sulfonated poly(ether ether ketone) for fuel cells. J Power Sources2012; 208: 176–179.
41.
SenUAcarOBozkurtAAtaA. Proton conducting polymer blends from poly(2,5-benzimidazole) and poly(2-acrylamido-2-methyl-1- propanesulfonic acid). J Appl Polym Sci2011; 120: 1193–1198.
42.
AcarOSenUBozkurtAAtaA. Blend membranes from poly(2,5-benzimidazole) and poly(styrene sulfonic acid) as proton-conducting polymer electrolytes for fuel cells. J Mater Sci2010; 45: 993–998.
43.
AcarOSenUBozkurtAAtaA. Proton conducting membranes based on Poly(2,5-benzimidazole) (ABPBI)–poly(vinylphosphonic acid) blends for fuel cells. Inter J Hydrogen Energy2009; 34: 2724–2730.
ThomasODPeckhamTJThanganathanUYangYHoldcroftS. Sulfonated polybenzimidazoles: proton conduction and acid–base crosslinking. J Polym Sci A Polym Chem2010; 48: 3640–3650.
46.
YinYFangJWatariTTanakaKKitaHOkamotoK. Synthesis and properties of highly sulfonated proton conducting polyimides from bis(3-sulfopropoxy)benzidine diamines. J Mater Chem2004; 14: 1062–1070.
47.
ZhaiFGuoXFangJXuH. Synthesis and properties of novel sulfonated polyimide membranes for direct methanol fuel cell application. J Membr Sci2007; 296: 102–109.
48.
SaitoJMiyatakeKWatanabeM. Synthesis and properties of polyimide ionomers containing 1H-1,2,4-triazole groups. Macromolecules2008; 41: 2415–2420.
49.
KobayashiTRikukawaMSanuiKOgataN. Proton-conducting polymers derived from poly(ether-etherketone) and poly(4-phenoxybenzoyl-1,4-phenylene). Solid State Ionics1998; 106: 219–225.