A linear oligobenzoxazine precursor with cyclotriphosphazene ring was prepared through the Schiff base route. The resulting polymers showed higher molecular weight and better thermal stability than those from the traditional Mannich polycondensation method. The oligomeric benzoxazine precursor can form a high-quality transparent yellow film; however, it was fragile after being cured. In order to identify the effect of end groups on the cured polymer, an aniline-capped polymer was prepared by the same Schiff base method and then was changed into a benzoxazine end group. The results indicated that the uncapped polymer exhibited higher stability than the capped polymer. This can be ascribed to different chemical structures resulting from different end groups.
LiuJ. Synthesis, characterization, reaction mechanism and kinetics of 3,4-dihydro-2H- 1,3-benzoxazine and its polymers. PhD Thesis, Case Western University, USA, 1995.
6.
TakeichiTKanoTAgagT. Synthesis and thermal cure of high molecular weight polybenzoxazine precursors and the properties of the thermosets. Polymer2005; 46: 12172–12180.
7.
ChernykhALiuJPIshidaH. Synthesis and properties of a new crosslinkable polymer containing benzoxazine moiety in the main chain. Polymer2006; 47: 7664–7669.
8.
LiuJAgagTIshidaH. Main-chain benzoxazine oligomers: A new approach for resin transfer moldable neat benzoxazines for high performance applications. Polymer2010; 51: 5688–5694.
9.
SawarynCLandfesterKTadenA. Advanced chemically induced phase separation in thermosets: Polybenzoxazines toughened with multifunctional thermoplastic main-chain benzoxazine prepolymers. Polymer2011; 52: 3277–3287.
10.
ChutayothinPIshidaH. Polymerization of p-cresol, formaldehyde, and piperazine and structure of monofunctional benzoxazine-derived oligomers. Polymer2011; 52: 3897–3904.
11.
LinCHChangSLShenTY. Flexible polybenzoxazine thermosets with high glass transition temperatures and low surface free energies. Polym Chem2012; 3: 935–945.
12.
DemirKDKiskanBLattheSS. Thermally curable fluorinated main chain benzoxazine polyethers via Ullmann coupling. Polym Chem2013; 4: 2106–2114.
13.
OieHMoriASudoA. Polyaddition of bifunctional 1,3-benzoxazine and 2-methylresorcinol. J Polym Sci Pol Chem2013; 51: 3867–3872.
14.
Velez-HerreraPDoyamaKAbeH. Synthesis and characterization of highly fluorinated polymer with the benzoxazine moiety in the main chain. Macromolecules2008; 41: 9704–9714.
15.
KiskanBAydoganBYagciY. Synthesis, characterization, and thermally activated curing of containing benzoxazine moieties in the main chain. J Polym Sci Pol Chem2009; 47: 804–811.
16.
WangLZhengSX. Morphology and thermomechanical properties of main-chain polybenzoxazine-block-polydimethylsiloxane multiblock copolymers. Polymer2010; 51: 1124–1132.
17.
TakeichiTKanoTAgagT. Preparation of high molecular weight polybenzoxazine prepolymers containing siloxane unites and properties of their thermosets. J Polym Sci Pol Chem2010; 48: 5945–5952.
18.
BagherifamSKiskanBAydoganB. Thermal degradation of polysiloxane and polyetherester containing benzoxazine moieties in the main chain. J Anal Appl Pyrol2011; 90: 155–163.
19.
LiYZhengSX. Nanostructured polybenzoxazine thermosets via reaction-induced microphase separation. J Polym Sci Pol Phys2010; 48: 1148–1159.
20.
BaqarMAgagTIshidaH. Poly(benzoxazine-co-urethane)s: a new concept for phenolic/urethane copolymers via one-pot method. Polymer2011; 52: 307–317.
21.
AgagTArzaCRMaurerFHJ. Crosslinked polyamide based on main-chain type polybenzoxazines derived from a primary amine-functionalized benzoxazine monomer. J Polym Sci Pol Chem2011; 49: 4335–4342.
22.
ChernykhAAgagTIshidaH. Effect of polymerizing diacetylene groups on the lowering of polymerization temperature of benzoxazine groups in the highly thermally stable, main-chain-type polybenzoxazines. Macromolecules2009; 42: 5121–5127.
AltinkokCKiskanBYagciY. Synthesis and characterization of sulfone containing main chain oligobenzoxazine precursors. J Polym Sci Pol Chem2011; 49: 2445–2450.
25.
BaiJShiZXYinJ. A novel main chain benzoxazine polymer with the ability of UV-induced self-surface modification. Polymer2013; 54: 2498–2505.
26.
HanbeyogluBKiskanBYagciY. Hydroxyl functional polybenzoxazine precursor as a versatile platform for post-polymer modifications. Macromolecules2013; 46: 8434–8440.
27.
JinLIshidaH. New thermo-oxidative protective coating for carbon/carbon composites in mid-temperature range using a combination of nano-filler and macro-filler with polybenzoxazine as a carbon-forming matrix. Polym Compos2011; 32: 1164–1173.
28.
AlhassanSMQutubuddinSSchiraldiDA. Preparation and thermal properties of graphene oxide/main chain benzoxazine polymer. Eur Polym J2013; 49: 3825–3833.
29.
WuXZhouYLiuSZ. Highly branched benzoxazine monomer based on cyclotriphosphazene: synthesis and properties of the monomer and polybenzoxazines. Polymer2011; 52: 1004–1012.
30.
WuXZhouYLiuSZ. Well-defined organiceinorganic hybrid benzoxazine monomers based on cyclotriphosphazene: synthesis, properties of the monomers and polybenzoxazines. Polymer2011; 52: 4235–4245.
31.
Wisian-NeilsonP.A worldwide insight. In: GleriàMJaegerRD (eds) Phosphazenes. New York, NY: Nova Science, 2004, pp. 109–125.
32.
StraussSHPawlikMJSkowyraJ. Comparison of the molecular and electronic structures of (μ-oxo)bis[(5,10,15,20-tetraphenylporphyrinato) iron(III)] and (μ-oxo)bis [(7,8-dihydro-5,10,15,20-tetraphenyl-porphyrinato) iron(III)]. Inorg Chem1987, 26: 724–730.
33.
AndreuRReinaJARondaJC. Studies on the thermal polymerization of substituted benzoxazine monomers: electronic effects. J Polym Sci Pol Chem2008; 46: 3353–3366.
34.
LowHIshidaH. Structural effects of phenols on the thermal and thermo-oxidative degradation of polybenzoxazines. Polymer1999; 40: 4365–4376.
35.
LowHIshidaH. An investigation of the thermal and thermo-oxidative degradation of polybenzoxazines with a reactive functional group. J Polym Sci Pol Phys1999; 37: 647–659.