High-strain-rate compression behavior and failure mechanism of 3D MWK carbon/epoxy composites

Abstract

The high-strain-rate compression experiments were performed on the three-dimensional multiaxial warp knitted (3D MWK) carbon/epoxy composites with different fiber architectures at room and elevated temperature using a split Hopkinson pressure bar apparatus. Macro-fracture and scanning electron microscope (SEM) micrographs were examined to understand the deformation and failure mechanism. The results show that 3D MWK carbon/epoxy composites have excellent high-strain-rate compression properties. The dynamic properties increase significantly with the strain rate and the composites show a high-strain-rate sensitivity. Meanwhile, composites with multidirectional symmetric fiber architecture have higher dynamic properties. Moreover, the composites show temperature sensitivity at high strain rates and the dynamic strength decreases significantly. The results also indicate the composites take on more serious damage and failure with the increase of strain rate. The failure of material with [0°/0°/0°/0°] behaves as binding fibers fracture in shear, 0° fibers tearing, overall expansion, and multiple 45° angle shear fracture, while the material with [0°/90°/+45°/−45°] is mainly interlaminar delaminating, and the local fibers tearing and shear on different fiber layers. In addition, with the increase of temperature, the composite shows less fracture and becomes more softened and plastic. The damages of matrix falling off, plasticity, and fiber/matrix interface debonding increase significantly.

Keywords

Textile composites braiding mechanical behavior failure mechanism

Get full access to this article

View all access options for this article.

References

Kamiya

Cheeseman

Popper

. Some recent advances in the fabrication and design of three-dimensional textile preforms: a review. Compos Sci Technol 2000; 60(1): 33–47.

Hufenbach

Böhm

Thieme

. Polypropylene/glass fibre 3D-textile reinforced composites for automotive applications. Mater Des 2011; 32(3): 1468–1476.

Jiang

. High strain rate behavior and failure mechanism of three-dimensional five-directional carbon/phenolic braided composites under transverse compression. Compos B 2011; 42(2): 309–317.

Bibo

Hogg

Kemp

. Mechanical characterisation of glass and carbon fibre reinforced composites made with non-crimp fabrics. Compos Sci Technol 1997; 57(9–10): 1221–1241.

Mattsson

Joffe

Varna

. Damage in NCF composites under tension: effect of layer stacking sequence. Eng Fract Mech 2008; 75(9): 2666–2682.

Zhao

Jiang

. A comparative study on the tensile properties and failure mechanism of 3D MWK composites at room and liquid nitrogen temperature. Polym Compos 2014; 35(7): 1294–1305.

Kong

Mouritz

Paton

. Tensile extension properties and deformation mechanisms of multiaxial non-crimp fabrics. Compos Struct 2004; 66(1–4): 249–259.

Edgren

Asp

. Approximate analytical constitutive model for non-crimp fabric composites. Compos A 2005; 36(2): 173–181.

Edgren

Mattsson

Asp

. Formation of damage and its effects on non-crimp fabric reinforced composites loaded in tension. Compos Sci Technol 2004; 64(5): 675–692.

10.

Jiang

. Characterizing and modeling bending properties of multiaxial warp knitted fabrics. Text Res J 1999; 69(9): 691–697.

11.

Lomov

Belov

Bischoff

. Carbon composites based on multiaxial multiply stitched preforms. Part 1: geometry of the preform. Compos A 2002; 33(9): 1171–1183.

12.

Lomov

Ivanov

Truong

. Experimental methodology of study of damage initiation and development in textile composites in uniaxial tensile test. Compos Sci Technol 2008; 68(12): 2340–2349.

13.

Sun

. Compressive behavior of multi-axial multi-layer warp knitted (MMWK) fabric composite at various strain rates. Compos Struct 2007; 78(1): 84–90.

14.

Zhou

Chen

. An experimental and numerical study on the impact energy absorption characteristics of the multiaxial warp knitted (MWK) reinforced composites. J Compos Mater 2005; 39(6): 525–542.

15.

Sugie

Nakai

Hamada

. Effect of CF/GF fibre hybrid on impact properties of multi-axial warp knitted fabric composite materials. Compos A 2009; 40(12): 1982–1990.

16.

Jiang

Zhao

. Charpy impact properties and failure mechanism of 3D MWK composites at room and cryogenic temperatures. Cryogenics 2014; 62: 37–47.

17.

Jiang

Zhao

. Experimental study on the tension fatigue behavior and failure mechanism of 3D multi-axial warp knitted composites. Compos B 2015; 68: 126–135.