Effect of cure pressure on microstructure and interlaminar shear strength properties of carbon fiber–reinforced plastics with microwave curing

Abstract

Under a given microwave curing process, different curing pressures were applied to the carbon fiber–reinforced epoxy resin pre-impregnated laminates. Nondestructive testing and microscopic analysis were used to assess the effect of curing pressure on the interlaminar shear strength (ILSS) of the carbon fiber–reinforced plastic (CFRP) laminates. Results showed that in the low curing pressure stage (below 0.4 MPa), the porosity and ILSS of the components were reduced substantially as the curing pressure increased. In the high curing pressure stage (above 0.4 MPa), the ILSS only increased by 2.2% or so and the porosity and ILSS were no longer sensitive to the pressure, which indicated there was a threshold value (0.4 MPa) of mechanical property for forming the CFRP by the microwave curing. Above the threshold value, the curing pressure should be sufficient to allow the volatile gases to dissolve in the resin, thereby eliminating the generation of voids fundamentally, and the effect of curing pressure on the quality of composites was becoming small. These results could give process engineers some basic references for eliminating the voids in the CFRP component, so that they could reach a balance between preserving the mechanical properties and reducing the curing pressure in a cost-effective way.

Keywords

Microwave carbon fiber–reinforced plastic curing pressure microstructure interlaminar shear strength

Get full access to this article

View all access options for this article.

References

Gao

. Tooling design and microwave curing technologies for the manufacturing of fiber-reinforced polymer composites in aerospace applications. Int J Adv Manuf Technol 2014; 70: 591–606.

Tan

Falzon

. Modelling the nonlinear behaviour and fracture process of AS4/PEKK thermoplastic composite under shear loading. Compos Sci Technol 2016; 126: 60–77. DOI: 10.1016/j.compscitech.2016.02.008.

Sorrentino

Esposito

Bellini

. A new methodology to evaluate the influence of curing overheating on the mechanical properties of thick FRP laminates. Compos B Eng 2017; 109: 187–196. DOI: 10.1016/j.compositesb.2016.10.064.

Tominaga

Shimamoto

Hotta

. Quantitative evaluation of interfacial adhesion between fiber and resin in carbon fiber/epoxy composite cured by semiconductor microwave device. Compos Interface 2016; 23: 395–404. DOI: 10.1080/09276440.2016.1143273.

Sato

Hotta

. Carbon fiber/epoxy composite materials cured thermally and with microwave irradiation. Compos Interface 2015; 22: 67–74. DOI: 10.1080/15685543.2015.988581.

Zhou

. Drilling delamination and thermal damage of carbon nanotube/carbon fiber reinforced epoxy composites processed by microwave curing. Int J Mach Tool Manu 2015; 97: 11–17. DOI: 10.1016/j.ijmachtools.2015.06.005.

Kardos

Duduković

Dave

. Void growth and resin transport during processing of thermosetting — Matrix composites. In: Dušek

(ed) Epoxy resins and composites IV. Berlin, Heidelberg: Springer Berlin Heidelberg, 1986, pp. 101–123.

Zhan

Chen

. The influence of cure pressure on microstructure, temperature field and mechanical properties of advanced polymer-matrix composite laminates. Fiber Polym 2014; 15: 2404–2409. DOI: 10.1007/s12221-014-2404-0.

Naganuma

Naito

Kyono

. Influence of prepreg conditions on the void occurrence and tensile properties of woven glass fiber-reinforced polyimide composites. Compos Sci Technol 2009; 69: 2428–2433. DOI: 10.1016/j.compscitech.2009.06.012.

10.

Hosoi

Yamaguchi

. Detection of delamination in GFRP and CFRP by microwaves with focusing mirror sensor. Mater Sci Forum 2013; 750: 142–146. DOI: 10.4028/ www.scientific.net/MSF.750.142.

11.

Aman

Morgner

. Monitoring of carbon fibre breakage in composites based on microwave emission. Compos Sci Technol 2013; 84: 58–64. DOI: 10.1016/j.compscitech.2013.05.010.

12.

Sorrentino

Polini

Bellini

. To design the cure process of thick composite parts: experimental and numerical results. Adv Compos Mater 2014; 23: 225–238. DOI: 10.1080/09243046.2013.847780.

13.

Guo

Zhang

. Temperature field of thick thermoset composite laminates during cure process. Compos Sci Technol 2005; 65: 517–523. DOI: 10.1016/j.compscitech.2004.07.015.

14.

Olivier

Cavarero

. Comparison between longitudinal tensile characteristics of thin and thick thermoset composite laminates: influence of curing conditions. Comput Struct 2000; 76: 125–137. DOI: 10.1016/S0045-7949(99)00161-3.

15.

Hang

. A temperature distribution prediction model of carbon fiber reinforced composites during microwave cure. J Mater Proc Technol 2016; 230: 280–287. DOI: 10.1016/j.jmatprotec.2015.12.001.

16.

Kwak

Robinson

Bismarck

. Microwave curing of carbon–epoxy composites: penetration depth and material characterisation. Compos A Appl Sci Manuf 2015; 75: 18–27. DOI: 10.1016/j.compositesa.2015.04.007.

17.

Chen

Zhan

Huang

. A novel method for curing carbon fiber reinforced plastics by high-pressure microwave. Fibers and Polymers 2017; 17: 2143–2152. DOI: 10.1007/s12221-016-6784 -1.

18.

Hao

. A comparative experiment for the analysis of microwave and thermal process induced strains of carbon fiber/bismaleimide composite materials. Compos Sci Technol 2015; 106: 15–19. DOI: 10.1016/j.compscitech.2014.10.008.

19.

Thostenson

Chou

. Microwave and conventional curing of thick-section thermoset composite laminates: experiment and simulation. Polym Compos 2001; 22: 197–212.

20.

Zhou

Wang

Yuan

. Comparison of the E44 epoxy resins in different contents of curing agent by microwave and thermal curing methods. J Wuhan Univ Technol 2000; 15: 35–39.

21.

Papargyris

Day

Nesbitt

. Comparison of the mechanical and physical properties of a carbon fibre epoxy composite manufactured by resin transfer moulding using conventional and microwave heating. Compos Sci Technol 2008; 68: 1854–1861. DOI: 10.1016/j.compscitech.2008.01.010.

22.

Feher

Drechsler

Filsinger

. Microwave processing of advanced composites with high electromagnetic power heating. Sampe J 2007; 43: 77–82.

23.

Nightingale

Day

. Flexural and interlaminar shear strength properties of carbon fibre/epoxy composites cured thermally and with microwave radiation. Compos A Appl Sci Manuf 2002; 33: 1021–1030. DOI: 10.1016/S1359-835X(02)00031-3.

24.

Hang

. Analysis and optimization of temperature distribution in carbon fiber reinforced composite materials during microwave curing process. J Mater Proc Technol 2014; 214: 544–550. DOI: 10.1016/j.jmatprotec.2013.10.012.