Novel soluble and heat-resistant polyamides derived from 4-(4-diphenylphosphino) phenyl-2,6-bis(4-aminophenyl)pyridine and various aromatic dicarboxylic acids

New diamine, 4-(4-diphenylphosphino)phenyl-2,6-bis(4-aminophenyl)pyridine, was prepared, and the related polyamides (PAs) bearing 2,6-diphenylpyridyl units and pendant diphenylphosphinophenyl groups were synthesized by direct polycondensation of this diamine and various aromatic diacids in N-methyl-2-pyrrolidinone (NMP) using triphenyl phosphite and pyridine as condensing agents. The resulting PAs with inherent viscosities of 0.78–1.06 dL g⁻¹ are readily soluble in polar aprotic solvents such as NMP, N, N-dimethylacetamide, and dimethylsulfoxide as well as less polar solvents such as m-cresol and pyridine. All the PAs are amorphous and could be solution-cast into transparent, flexible, and tough films, which have tensile strengths of 68.2–88.8 MPa, tensile moduli of 1.9–2.4 GPa, and elongations at break of 5.4–10.3%. These polymer films also exhibit high optical transparence with the UV cutoff wavelength in the 361–412 nm range. These PAs display glass transition temperatures of 316–332°C, 10% mass loss temperatures of 524–553°C, and more than 48% residues at 800°C in nitrogen, respectively. Their high char yields and good limited oxygen index values ranging from 39 to 44 indicate the prepared PAs show good thermal stability and flame-retardant property.