The addition of polyamide veil (PAV) to the interlaminar area of carbon fiber (CF) fabric/epoxy composites can effectively increase their toughness with high accuracy. Vacuum-assisted resin infusion (VARI) was used to fabricate composite structures. VARI was applied to obtain a PAV, which is an interleaf between fabric piles of CFs. The thermoplastic PAV was dissolved in epoxy when the PAV was cured at high temperature. A phase-separated morphology with a PAV-rich secondary phase was formed during the curing process. Experimental results indicated that compression after impact (CAI), which is the average value of CAI, increased by threefold when two layers of PAV were added. The thermal and mechanical characteristics of the composite were analyzed and compared at room temperature and high-temperature wet conditions.
SohnMHuX. Processing of carbon-fibre/epoxy composites with cost-effective interlaminar reinforcement. Compos Sci Technol1998; 58(2): 211–220.
2.
RichardsonMOWWisheartMJ. Review of low-velocity impact properties of composite materials. Composites Part A1996; 12(27): 1123–1131.
3.
OuYGonzálezCVilatelaJJ. Interlaminar toughening in structural carbon fiber/epoxy composites interleaved with carbon nanotube veils. Compos Part A: Appl Sci Manuf2019; 124: 105477.
4.
Ebrahimnezhad-KhaljiriHEslami-FarsaniR. Experimental investigation of flexural properties of glass fiber-epoxy self-healable composite structures containing capsulated epoxy healing agent and NiCl2 (imidazole)4catalyst. J Ind Text2019; 2025532204.
5.
SuhDKuMNamJ, et al.Equilibrium water uptake of epoxy/carbon fiber composites in hygrothermal environmental conditions. J Compos Mater2001; 35(3): 264–278.
6.
KuoHTzengCYehCB, et al.A study of the physical properties and chemical reagents of epoxy mortar floor intermediate coating using recycled glass sand as filler. P I Mech Eng, Part E: J Pro Mech Eng2018; 233: 701–708.
7.
KrishnaswamySBhattacharyyaDAbhyankarH, et al.Morphological, optical and thermal characterisation of aerogel-epoxy composites for enhanced thermal insulation. J Compos Mater2018; 53: 909–923.
8.
PoggettiIDysonJSánchezDM, et al.Distributed internal strain measurement of the fluid-solid state coefficients of thermal expansion below the glass transition temperature during a composite manufacturing process. J Compos Mater2018; 52(22): 3053–3084.
9.
LiuPYangJPengX. Delamination analysis of carbon fiber composites under hygrothermal environment using acoustic emission. J Compos Mater2016; 51(11): 1557–1571.
10.
ZhangXXuWXiaX, et al.Toughening of cycloaliphatic epoxy resin by nanosize silicon dioxide. Mater Lett2006; 60(28): 3319–3323.
11.
ZhouHXuS. A new method to prepare rubber toughened epoxy with high modulus and high impact strength. Mater Lett2014; 121: 238–240.
12.
ZhouJChengCJiangM, et al.Polyethersulfone melt-spun fibers plasticized with epoxy oligomer. Mater Lett2018; 210: 263–266.
13.
WeiCLiuZBaoY, et al.Evaluating thermal expansion coefficient and density of ceramic coatings by relative method. Mater Lett2015; 161: 542–544.
14.
WongDWYLinLMcGrailPT, et al.Improved fracture toughness of carbon fibre/epoxy composite laminates using dissolvable thermoplastic fibres. Compos Part A: Appl Sci Manuf2010; 41(6): 759–767.
15.
WangCHSidhuKYangT, et al.Interlayer self-healing and toughening of carbon fibre/epoxy composites using copolymer films. Compos Part A: Appl Sci Manuf2012, 43(3): 512–518.
16.
NingHLiYLiJ, et al.Toughening effect of CB-epoxy interleaf on the interlaminar mechanical properties of CFRP laminates. Compos Part A: Appl Sci Manuf2015; 68: 226–234.
17.
Awang NgahSTaylorAC. Toughening performance of glass fibre composites with core-shell rubber and silica nanoparticle modified matrices. Compos Part A: Appl Sci Manuf2016; 80: 292–303.
18.
DowneyMADrzalLT. Toughening of carbon fiber-reinforced epoxy polymer composites utilizing fiber surface treatment and sizing. Compos Part A: Appl Sci Manuf2016; 90: 687–698.
19.
LuoJYangSLeiL, et al.Toughening, synergistic fire retardation and water resistance of polydimethylsiloxane grafted graphene oxide to epoxy nanocomposites with trace phosphorus. Compos Part A: Appl Sci Manuf2017; 100: 275–284.
20.
WongDWYZhangHBilottiE, et al.Interlaminar toughening of woven fabric carbon/epoxy composite laminates using hybrid aramid/phenoxy interleaves. Compos Part A-Appl S2017; 101: 151–159.
21.
HoffmannJScharrG. Mode I delamination fatigue resistance of unidirectional and quasi-isotropic composite laminates reinforced with rectangular z-pins. Compos Part A: Appl Sci Manuf2018; 115: 228–235.
22.
GilbertENHayesBSSeferisJC. Interlayer toughened unidirectional carbon prepreg systems: effect of preformed particle morphology. Composites Part A: Applied Science and Manufacturing2003; 34: 245–252.
23.
WooEMHseihHK. Morphology development in epoxy/polymer systems: Thermosetting epoxy micro particles with a thermoplastic shell. Polymer1988; 39(1): 7–13.
24.
ZengSDuanPShenM, et al.Interlaminar fracture toughness, adhesion and mechanical properties of MWCNT-glass fiber fabric composites: effect of MWCNT aspect ratios. Polym Compos2018; 40: E1329–E1337.
25.
ZhangLLiJWuJ, et al.Effects of flame retardants on liquid oxygen compatibility of epoxy resin containing binaphthyl based on combination of mechanical impact testing and theoretical analysis. High Perform Polym2016; 28(9): 1024–1032.
26.
LiGLiPZhangCYuY. Inhomogeneous toughening of carbon fiber/epoxy composite using electrospun polysulfone nanofibrous membranes by in situ phase separation. Compos science and technology2008; 68: 987–994.
27.
SebaeyTAGonzálezEVLopesCS, et al.Damage resistance and damage tolerance of dispersed CFRP laminates: design and optimization. Compos Struct2013; 95: 569–576.
28.
ZhangALuHZhangD. Effects of voids on residual tensile strength after impact of hygrothermal conditioned CFRP laminates. Compos Struct2013; 95: 322–327.
29.
YuGWuLFengL, et al.Thermal and mechanical properties of carbon fiber polymer-matrix composites with a 3D thermal conductive pathway. Compos Struct2016; 149: 213–219.
30.
FukudaHWatanabeTItabashiM, et al.Compression bending test for CFRP pipe. Compos Sci Technol2002; 62(15): 2075–2081.
31.
DuXZhouHSunW, et al.Graphene/epoxy interleaves for delamination toughening and monitoring of crack damage in carbon fibre/epoxy composite laminates. Compos Sci Technol2017; 140: 123–133.
32.
LiTLiMGuY, et al.Mechanical enhancement effect of the interlayer hybrid CNT film/carbon fiber/epoxy composite. Compos Sci Technol2018; 166: 176–182.
33.
YuanJZhangZYangM, et al.POSS grafted hybrid-fabric composites with a biomimic middle layer for simultaneously improved UV resistance and tribological properties. Compos Sci Technol2018; 160: 69–78.
34.
GrunenfelderLKNuttSR. Void formation in composite prepregs – Effect of dissolved moisture. Compos Sci Technol2010; 70(16): 2304–2309.
35.
HiremathCPSenthilnathanKNaikNK, et al.Microstructural damage based modeling of thermal conductivity of cyclically loaded CFRP. Compos Sci Technol2018; 154: 37–44.
36.
KimSYJonesARSottosNR, et al.Manufacturing of unidirectional glass/epoxy prepreg with microencapsulated liquid healing agents. Compos Sci Technol2017; 153: 190–197.
37.
ChenJWangKZhaoY. Enhanced interfacial interactions of carbon fiber reinforced PEEK composites by regulating PEI and graphene oxide complex sizing at the interface. Compos Sci Technol2018; 154: 175–186.
38.
Abdel-RaheemNAHalimSFAl-KhoribiAH. The effect of different curing conditions on hardness, thickness, and residual stress of carbon fiber reinforced epoxy composites. J Compos Mater2017; 52(14): 1959–1970.