To improve the safety of lithium-ion batteries (LIBs), a polyether amide–silica (PEI-SiO2) composite membrane was developed by the in situ hydrolysis of tetraethylorthosilicate (TEOS) and its subsequent self-assembly on the surface of PEI fibers. Because of the presence of the SiO2 shell, the PEI-SiO2 composite membrane exhibited good thermal stability at high temperatures. The composite membrane did not change its color and size after heating at 200°C for 1 h as well as exhibited excellent flame retardancy. Moreover, the membrane maintained its high porosity even after the introduction of shell layers. The electrolyte is completely absorbed in the membrane within 0.5 s. The electrolyte uptake was up to 625%, and the ionic conductivity was up to 1.9 mS/cm at room temperature. Compared to the polyolefin membrane and the pure PEI membrane, the PEI-SiO2 composite membrane showed higher electrochemical stability, with an electrochemical window of up to 5.5 V. The battery assembled with the composite membrane showed excellent cycle stability, and the capacity retention rate was as high as 98.6% after 50 cycles. The LIBs based on the PEI-SiO2 composite membrane exhibited safe operation and high electrochemical performance, thus highlighting the applicability of the composite membrane in high-power batteries.
HannanMAHoqueMMMohamedA, et al.Review of energy storage systems for electric vehicle applications: issues and challenges. Renew Sust Energy Rev2017; 69: 771–789.
2.
KimTSongWSonDY, et al.Lithium-ion batteries: outlook on present, future, and hybridized technologies. J Mater Chem A2019; 7(7): 2942–2964.
3.
KangYDengCWangZ, et al.Molecular sieve-modified separator for high-performance lithium-ion batteries. Nanoscale Res Lett2020; 15(1): 107.
4.
SunYLiuNCuiY. Promises and challenges of nanomaterials for lithium-based rechargeable batteries. Nat Energy2016; 1: 16071.
CostaCMLizundiaELanceros-MendezS. Polymers for advanced lithium-ion batteries: state of the art and future needs on polymers for the different battery components. Prog Energ Combust Sci2020; 79: 100846.
7.
IrinaBDianaSMariaB, et al.Physical and thermal properties of poly(ethylene terephthalate) fabric coated with electrospun polymide fibers. High Perform Polym2015; 27(5): 616–624.
LiLPascalTAConnellJG, et al.Molecular understanding of polyelectrolyte binders that actively regulate ion transport in sulfur cathodes. Nat Commun2017; 8(1): 2277.
10.
LeeHYanilmazMToprakciO, et al.A review of recent developments in membrane separators for rechargeable lithium-ion batteries. Energy Environ Sci2014; 7(12): 3857–3886.
11.
WardALDorisSELiL, et al.Materials genomics screens for adaptive ion transport behavior by redox-switchable microporous polymer membranes in lithium-sulfur batteries. ACS Cent Sci2017; 3(5): 399–406.
12.
ChaoZHongQingLJunKeP, et al.Polypropylene separators with robust mussel-inspired coatings for high lithium-ion battery performance. Chinese J Polym Sci2019; 37(10): 1015–1022.
13.
HeidariAAMahdaviH. Recent development of polyolefin-based microporous separators for Li-ion batteries: a review. Chem Rec2020; 20(6): 570–595.
14.
EthanRMcverryBTArieB, et al.Roll-to-roll functionalization of polyolefin separators for high performance lithium ion batteries. ACS Appl Energy Mater2018; 1(7): 3292–3300.
15.
ZahnRLagadecMFHessM, et al.Improving ionic conductivity and lithium-ion transference number in lithium-ion battery separators. ACS Appl Mater Interfaces2016; 8(48): 32637–32642.
16.
FrancisCFJKyratzisILBestAS. Lithium-ion battery separators for ionic-liquid electrolytes: a review. Adv Mater2020; 32(18): 1904205.
17.
LiuXRenDHsuH, et al.Thermal runaway of lithium-ion batteries without internal short circuit. Joule2018; 2(10): 2047–2064.
18.
InoueTMukaiK. Roles of positive or negative electrodes in the thermal runaway of lithium-ion batteries: accelerating rate calorimetry analyses with an all-inclusive microcell. Electrochem Commun2017; 77: 28–31.
19.
PengLShenXDaiJ, et al.Three-dimensional coating layer modified polyolefin ceramic-coated separators to enhance the safety performance of lithium-ion batteries. J Electrochem Soc2019; 166(10): A2111–A2120.
20.
PrasannaKKimCSLeeCW. Effect of SiO2 coating on polyethylene separator with different stretching ratios for application in lithium ion batteries. Mater Chem Phys2014; 146(3): 545–550.
21.
JeonHYeonDLeeT, et al.A water-based Al2O3 ceramic coating for polyethylene-based microporous separators for lithium-ion batteries. J Power Sources2016; 315(31): 161–168.
22.
LiuHXuJGuoB, et al.Effect of SiO2 content on performance of polypropylene separator for lithium-ion batteries. J Appl Polym Sci2014; 131(23): 41156.
23.
YanilmazMDiricanMZhangX. Evaluation of electrospun SiO2/nylon 6,6 nanofiber membranes as a thermally-stable separator for lithium-ion batteries. Electrochim Acta2014; 133: 501–508.
24.
GongWWangXLiZ, et al.A high-strength PPESK/PVDF fibrous membrane prepared by coaxial electrospinning for lithium-ion battery separator. High Perform Polym2018; 31(8): 948–958.
25.
LiangXYangYJinX, et al.The high performances of SiO2/Al2O3-coated electrospun polyimide fibrous separator for lithium-ion battery. J Membr Sci2015; 493: 1–7.
26.
LeeJLeeCLParkK, et al.Synthesis of an Al2O3-coated polyimide nanofiber mat and its electrochemical characteristics as a separator for lithium ion batteries. J Power Sources2014; 248(15): 1211–1217.
27.
ZhaiYXiaoKYuJ, et al.Fabrication of hierarchical structured SiO2/polyetherimide-polyurethane nanofibrous separators with high performance for lithium ion batteries. Electrochim Acta2015; 154: 219–226.
28.
PrasannaKLeeCW. Physical, thermal, and electrochemical characterization of stretched polyethylene separators for application in lithium-ion batteries. J Solid State Electrochem2013; 17(5): 1377–1382.
29.
WangZGuoFChenC, et al.Self-Assembly of PEI/SiO2 on polyethylene separators for Li-ion batteries with enhanced rate capability. ACS Appl Mater Interfaces2015; 7(5): 3314–3322.
30.
LiHLiLZhengS, et al.High temperature resistant separator of PVDF-HFP/DBP/C-TiO2 for lithium-ion batteries. Materials2019; 12(17): 2813.
31.
ShiJShenTHuH, et al.Sandwich-like heat-resistance composite separators with tunable pore structure for high power high safety lithium ion batteries. J Power Sources2014; 271(20): 134–142.
32.
ZhangJYueLKongQ, et al.Sustainable, heat-resistant and flame-retardant cellulose-based composite separator for high-performance lithium ion battery. Sci Rep2014; 4(1): 3935.
33.
KimKJKwonHKParkMS, et al.Ceramic composite separators coated with moisturized ZrO2 nanoparticles for improving the electrochemical performance and thermal stability of lithium ion batteries. Phys Chem Chem Phys2014; 16(20): 9337–9343.