A matrix resin poly(silicon-containing arylacetylene vinyl)s (PSAV) containing vinyl at both branch and terminal chains underwent synthesis via the zinc powder catalytic method using m-diacetylene benzene and dichloromethylvinylsilane as raw materials. Vinyl in the PSAV resin was crosslinked by the free radical initiator dibenzoyl peroxide to obtain a crosslinked network structure resin (PSAV-L). This approach sought to improve the thermal properties and other related properties of the matrix resin. A series of tests, such as rotated rheometer, FTIR, DSC, TGA, Py-GC-MS and universal testing machine, characterised processing property, curing behaviour, thermal properties and mechanical properties. The rheological curve shows that PSAV-L resin has a wide processing window (40–134.5°C), endowing the resin with excellent processing performance. Thermal curing behaviour indicates that PSAV-L resin can start curing at a lower temperature, namely, 32°C earlier than PSAV resin. TGA analysis shows that the degradation temperature at 5% weight loss (Td5) of PSAV-L resin stands at 579.4°C, 45.4°C higher than that of PSAV resin due to the fact that the crosslinking of vinyl gives PSAV-L resin a network structure. The flexural strength, flexural modulus and ILSS of the quartz fibre cloth reinforced PSAV-L resin composite (QF/PSAV-L) are 184.68 MPa, 15.50 GPa and 12.40 MPa. The PSAV-L resin exhibits the comprehensive properties of good processing performance, low curing temperature, excellent thermal performance and high mechanical properties.
WangDXiongXRenR, et al.Characterization and properties of high-temperature resistant structure adhesive based on novel toughened bismaleimide resins. High Perform Polym2020; 33: 488–496. DOI: 10.1177/0954008320970271.
2.
LuHDongYLiuX, et al.Enhanced magnetic properties of fesial soft magnetic composites prepared by utilizing psa as resin insulating layer. Polymers2021; 13: 1350. DOI: 10.3390/polym13091350.
3.
ChenJChuNZhaoM, et al.Synthesis and application of thermal latent initiators of epoxy resins: a review. J Appl Polym Sci2020; 137: 49592. DOI: 10.1002/app.49592.
4.
ZhangDLiuXBaiX, et al.Synthesis, characterization and properties of phthalonitrile-etherified resole resin. E-Polymers2020; 20: 500–509. DOI: 10.1515/epoly-2020-0051.
5.
ZhouHZhangLMaoY, et al.Synthesis and characterization of melt‐processable polyimides derived from diaminodiphenylsulfone and benzophenone tetracarboxylic dianhydride with excellent heat resistance and thermoplasticity. J Appl Polym Sci2021; 138: 51219. DOI: 10.1002/app.51219.
6.
GotoMMiyagiYMinamiM, et al.Synthesis and crosslinking reaction of polyacetylenes substituted with benzoxazine rings: thermally highly stable benzoxazine resins. J Polym Sci A Polym Chem2018; 56: 1884–1893. DOI: 10.1002/pola.29076.
7.
NakamuraSFujiiTMatsukawaS, et al.Specific heat, thermal conductivity, and magnetic susceptibility of cyanate ester resins - An alternative to commonly used epoxy resins. Cryogenics2018; 95: 76–81. DOI: 10.1016/j.cryogenics.2018.09.001.
8.
ZhouJLHuYHHuJJ, et al.Synthesis and properties of acetylene-containing cross-linkable triazine resin. EXPRESS Polym Lett2020; 14: 780–792.
9.
LiuZHuangYDengS. Synthesis and characterization of thermosetting polyacetylene‐terminated silicone resins. J Appl Polym Sci2019; 137: 48783. DOI: 10.1002/app.48783.
10.
LuLGuoKZhuJ, et al.Silicon‐containing fluorenylacetylene resins with low curing temperature and high thermal stability. J Appl Polym Sci2019; 136: 48262. DOI: 10.1002/app.48262.
11.
CorriuRJPDouglasWEYangZ-X. Synthesis of poly(alkynylsilanes) having various aromatic groups in the backbone. J Polym Sci C Polym Lett1990; 28: 431–437.
12.
CorriuRJ-PDouglasWEYangZ-X. Preparation of oligomers containing tetraphenylsilole, acetylene and aromatic groups in the main chain, and incorporation of iron carbonyl. Elsevier1993; 456: 35–39.
13.
LiuHQHarrodJF. Copper(I) chloride catalyzed cross-dehydrocoupling reactions between silanes and ethynyl compounds. a new method for the copolymerization of silanes and alkynes. Can J Chem1990; 68: 1100–1105. DOI: 10.1139/v90-170.
14.
ItohM. A novel synthesis of a highly heat‐resistant organosilicon polymer using base catalysts. Catal Surv Asia1999; 3: 61–69. DOI: 10.1023/A:1019051113699.
15.
LingZZhuJCaiC, et al.Highly heat‐resistant branched silicon‐containing arylacetylene resins with low curing temperature. Polym Int2021; 70: 1595–1603. DOI: 10.1002/pi.6254.
16.
WanLGuoKZhuJ, et al.Improvement of the oxidation resistance of silicon‐containing arylacetylene resins upon the introduction of carbazoles. J Appl Polym Sci2020; 138: 49642. DOI: 10.1002/app.49642.
17.
PanLTaharaKMasukoT, et al.Methyl-transfer reaction to alkylthiol catalyzed by a simple vitamin B12 model complex using zinc powder. Inorg Chim Acta2011; 368: 194–199. DOI: 10.1016/j.ica.2011.01.004.
18.
DuCChenY. Zinc powder catalysed formylation and urealation of amines using CO 2 as a C1 building block. Chin J Chem2020; 38: 1057–1064. DOI: 10.1002/cjoc.202000072.
19.
HuangYDengSLiuZ. Star‐shaped silicon‐containing arylacetylene resin based on a one‐pot synthesis using zinc powder catalysis with improved processing and thermal properties. J Appl Polym Sci2019; 136: 48248. DOI: 10.1002/app.48248.
20.
SugitaHHatanakaYHiyamaT. Silylation of 1-alkynes with chlorosilanes promoted by zinc: preparation of alkynylsilanes in a single step. Tetrahedron Lett1995. DOI: 10.1016/0040-4039(95)00391-o.
21.
ShenHJiangXZhouY, et al.Synthesis of silicon-containing arylacetylene resin catalyzed by zinc powder. Chin J Process Eng2014; 14: 329–334.
22.
HuangPLiuZShaoY, et al.Mechanistic investigation of zinc-promoted silylation of phenylacetylene and chlorosilane: a combined experimental and computational study. Phys Chem Chem Phys2020; 22: 22935–22942. DOI: 10.1039/d0cp04127k.
23.
BiermannUMetzgerJOCatalyticC. C-Bond forming additions to unsaturated fatty compounds. Top Catal2004; 38: 3675–3677. DOI: 10.1023/B:TOCA.0000013546.97468.
24.
LiuLWardRMSchomakerJM. Mechanistic aspects and synthetic applications of radical additions to allenes. Chem Rev2019; 119: 12422–12490. DOI: 10.1021/acs.chemrev.9b00312.
25.
NugayTKeszlerBLDeodharT, et al.Low cost bifunctional initiators for bidirectional living cationic polymerization of olefins i isobutylene. J Polym Sci A Polym Chem2017; 55: 3716–3724. DOI: 10.1002/pola.28756.
26.
KimDHParkSSParkSH, et al.Preparation of polystyrene-polyolefin multiblock copolymers by sequential coordination and anionic polymerization. RSC Adv2017; 7: 5948–5956. DOI: 10.1039/c6ra25848d.
27.
PollitAAYeSSeferosDS. Elucidating the role of catalyst steric and electronic effects in controlling the synthesis of π-conjugated polymers. Macromolecules2020; 53: 138–148. DOI: 10.1021/acs.macromol.9b02098.
28.
LiuYYueZGaoJ. Synthesis, characterization, and thermally activated polymerization behavior of bisphenol-S/aniline based benzoxazine. Polymer2010; 51: 3722–3729. DOI: 10.1016/j.polymer.2010.06.009.
29.
WannaborwornMPraserthdamPJongsomjitB. Observation of different catalytic activity of various 1-olefins during ethylene/1-olefin copolymerization with homogeneous metallocene catalysts. Molecules2011; 16: 373–383. DOI: 10.3390/molecules16010373.
30.
YamadaBZetterlundPBSatoE. Utility of propenyl groups in free radical polymerization: effects of steric hindrance on formation and reaction behavior as versatile intermediates. Prog Polym Sci2006; 31: 835–877. DOI: 10.1016/j.progpolymsci.2006.08.005.
31.
HsiaoK-TLittleRRestrepoO, et al.A study of direct cure kinetics characterization during liquid composite molding. Composites A Appl Sci Manuf2006; 37: 925–933. DOI: 10.1016/j.compositesa.2005.01.019.
32.
GuoKLiPZhuY, et al.Thermal curing and degradation behaviour of silicon-containing arylacetylene resins. Polym Degrad Stab2016; 131: 98–105. DOI: 10.1016/j.polymdegradstab.2016.07.006.
33.
KurokiSOkitaKKakiganoT, et al.Thermosetting mechanism study of poly[(phenylsilylene)ethynylene-1,3-phenyleneethynylene] by solid-state nmr spectroscopy and computational chemistry. Macromolecules1998; 31: 2804–2808. DOI: 10.1021/ma971133g.