Ultimate bending performance and fatigue life of U-shaped metal bellows

Abstract

Metal bellows used in the flexible connection of metallurgical converter oxygen lance compensates for pipeline displacement through its bending deformation, and adjacent waveforms in the concentrated deformation area are squeezed, resulting in premature fracture. The bending geometric model of U-shaped metal bellows is established in this paper, and the geometric relationship between waveform structure parameters and ultimate bending radius is derived. Moreover, a mathematical model of bending moment (M) with bending angular displacement (θ) about wave height H and wave crest fillet radius Rc is established. Then, combined with Fe-safe fatigue life analysis software, the fatigue life and failure location of metal bellows are obtained. The optimal waveform parameter design range of DN80 metal bellows with high repeated bending fatigue life under large bending is determined. Finally, the bending performance and fatigue life of bellows are tested on a bending fatigue testing machine. The distribution law of fatigue life and the propagation law of cracks at the wave trough of metal bellows under different bending angular displacement amplitudes are obtained. The crack propagation mechanism and fracture mechanism under different displacement amplitudes are revealed by a scanning electron microscope. In the engineering application of large bending, the pipeline failure caused by the ultimate bending deformation of metal bellows can be avoided according to the prediction results of fatigue life.

Keywords

metal bellows ultimate bending radius bending performance fatigue life crack propagation mechanism

Get full access to this article

View all access options for this article.

References

Singace

El-Sobky

. Behaviour of axially crushed corrugated tubes. Int J Mech Sci 1997; 39(3): 249–268.

Sadighi Dizaji

Jafarmadar

Mobadersani

. Experimental studies on heat transfer and pressure drop characteristics for new arrangements of corrugated tubes in a double pipe heat exchanger. Int J Therm Sci 2015; 96: 211–220.

Zhang

Zou

, et al. Experimental study: correcting the calculation formula for a welded metal bellows' effective diameter. Sealing Technol 2016; 2016(10): 7–12.

Guan

Zhang

, et al. Failure of 304 stainless bellows expansion joint. Eng Fail Anal 2005; 12(3): 387–399.

Zhu

Wang

Sang

. The effect of environmental medium on fatigue life for U-shaped bellows expansion joints. Int J Fatigue 2006; 28(1): 28–32.

Yuan

Huo

Ren

. Mathematical description and mechanical characteristics of reinforced S-shaped bellows. Int J Pers Ves Pip 2019; 175: 103931.

Chen

J-J

Yin

Z-H

Yuan

X-J

, et al. A refined stiffness model of rolling lobe air spring with structural parameters and the stiffness characteristics of rubber bellows – ScienceDirect. Measurement 2021; 169: 108355.

Brodzinski

Cruikshank

Fournel

, et al. Failure mechanism and consolidation of the compensation bellows of the LHC cryogenic distribution line. Phys Proced 2015; 67: 129–134.

Gomes da Silva

Fragoso

HAP

Barrio

RCAG

, et al. Stress corrosion of an austenitic stainless steel expansion joint, a case study. Eng Fail Anal 2019; 97: 300–310.

10.

Costa Garrido

Končar

Brown

, et al. Pre-conceptual design of DEMO upper port duct bellows. Fusion Eng Des 2018; 136: 1130–1134.

11.

Yang

Xiao

Chen

, et al. Establishment of minimum relative bending radius of thin-walled tube no-mandrel bending. Forging Stamping Technol 2010; 35(2): 132–136.

12.

Huo

Yan

, et al. Bending characteristics of the reinforced S-shaped bellows under internal pressure – ScienceDirect. Int J Pers Ves Pip 2021; 192: 104412.

13.

Yang

Zhang

, et al. Multiple instability-constrained tube bending limits. J Mater Process Technol 2014; 214(2): 445–455.

14.

Xiang

, et al. Finite element analysis and experimental study on a bellows joint. Eng Struct 2017; 151: 584–598.

15.

Hao

Luo

Zhao

, et al. Effect of plate hardening behavior on the deformation of stainless steel metal bellows. J Mater Eng Perform 2017; 26: 5385–5395.

16.

Silvestre

Mendiguren

Galdos

, et al. Comparison of the hardening behaviour of different steel families: from mild and stainless steel to advanced high strength steels. Int J Mech Sci 2015; 101–102: 10–20.

17.

Expansion Joints Manufacturing Association (EJMA) . 1996.

18.

Ravi

Parameswaran

Ganeshkumar

, et al. Failure analysis of 316L austenitic stainless steel bellows used under dynamic sodium in a creep testing chamber. Eng Fail Anal 2016; 59: 366–376.

19.

Pavithra

Kumar

VSS

. Experimental investigation and numerical analysis on fatigue life of bellows. Mater Today 2018; 59: 18848–18856.

20.

Gomes da Silva

Fragoso

HAP

Barrio

RCAG

, et al. Stress corrosion of an austenitic stainless steel expansion joint, a case study. Eng Fail Anal 2019; 97: 300–310.

21.

Pavithra

Kumar

VSS

. Experimental investigation and numerical analysis on fatigue life of bellows. Mater Today 2018; 5: 18848–18856.

22.

Hao

Luo

Jin

. Failure analysis of corrugated metal hose under ultimate repeated bending process. Eng Fail Anal 2019; 109: 104295.

23.

Hao

Luo

Chen

, et al. Failure mechanism of unequal parameters metal bellows under repeated bending process. Eng Fail Anal 2021; 129: 105671.

24.

Qian

Yan

, et al. Limit bending moment for pipes with two circumferential flaws under combined internal pressure and bending. Int J Mech Sci 2016; 106: 319–330.

25.

Zhang

Yan

Yang

. A simplified model of maximum cross-section flattening in continuous rotary straightening process of thin-walled circular steel tubes. J Mater Process Technol 2016; 238: 305–314.

26.

Becht

. Fatigue of bellows, a new design approach. Int J Pers Ves Pip 2000; 77: 843–850.

27.

Hao

Z-l

C-y

Huang

Z-h

, et al. Hydraulic bulging process with axial feedings and strain field of U-shaped metal bellows. J Cent South Univ 2018; 2511: 2712–2721.

28.

Liu

Sheng

, et al. Manufacture and test of seismic bellows for ITER magnet feeder. Fusion Eng Des 2016; 109–111: 515–520.