This paper investigates the mechanical and wears resistance properties of AISI 5140 alloy steel coated with thin films of hydrogenated diamond-like carbon (HDLC) and titanium nitride (TiN). HDLC and TiN films were sputtered onto AISI 5140 alloy steel samples using the magnetron sputtering technique. In addition to coatings, the metallic substrates were also evaluated for hardness and wear resistance. The findings on wear losses, patterns, and wear trace widths were determined after the wear tests. In tribological tests, a variety of wear patterns were observed on both thin film coatings. The primary wear mechanisms of TiN coatings were found to be tribochemical wear, substrate material loss, and wear debris. However, the HDLC coating experienced wear due to ploughing action, with minor patches of the thin film being removed from the underlying material, but scanning electron microscopy observations showed no detectable wear. Using Raman spectroscopy, the structural properties of HDLC were analyzed, and the findings were compared to those of wear patterns. The results showed that the coating significantly improved the wear resistance of the AISI 5140 alloy steel and that the TiN-coated AISI 5140 alloy steel sample was more comparable to wear than the HDLC-coated AISI 5140 alloy steel sample. It is also shown that, as compared to an uncoated metallic substrate, the resilience of thin film coated components is a key factor impacting component life.
AslanA. Optimization and analysis of process parameters for flank wear, cutting forces and vibration in turning of AISI 5140: a comprehensive study. Measurement2020; 163: 107959.
2.
KaramişMB. Tribological behaviour of plasma nitrided 722M24 material under dry sliding conditions. Wear1991; 147: 385–399.
3.
AlsaranAAltunHKarakanM, et al.Effect of post-oxidizing on tribological and corrosion behaviour of plasma nitrided AISI 5140 steel. Surf Coat Technol2004; 176: 344–348.
4.
BuhagiarJSpiteriASaccoM, et al.Augmentation of crevice corrosion resistance of medical grade 316LVM stainless steel by plasma carburising. Corros Sci2012; 59: 169–178.
5.
NieDChenXWuQ. Mixed-mode fracture behaviors of AISI 1045 and AISI 5140 steels in compressor crankshafts – part I: mode I-III. Eng Fail Anal2020; 110: 104406.
6.
SenthilkumarPPradeepRSivakumarER. Experimental optimization on durability of exhaust valves in CI engines. J Chem Pharm Sci2016; 9: 1–4.
7.
EbrahimiAMoshksarMM. Evaluation of machinability in turning of microalloyed and quenched-tempered steels: tool wear, statistical analysis, chip morphology. J Mater Process Technol2009; 209: 910–921.
8.
CatauroMBollinoFPapaleF, et al.Corrosion behavior and mechanical properties of bioactive sol-gel coatings on titanium implants. Mater Sci Eng C2014; 43: 375–382.
9.
BullSJBeraseteguiEG. An overview of the potential of quantitative coating adhesion measurement by scratch testing. Tribol Int2006; 39: 99–114.
10.
SantecchiaEHamoudaAMSMusharavatiF, et al.Wear resistance investigation of titanium nitride-based coatings. Ceram Int2015; 41: 10349–10379.
11.
ChenYNieXLeylandA, et al.Substrate and bonding layer effects on performance of DLC and TiN biomedical coatings in hank’s solution under cyclic impact–sliding loads. Surf Coat Technol2013; 237: 219–229.
12.
DearnleyPA. A brief review of test methodologies for surface-engineered biomedical implant alloys. Surf Coat Technol2005; 198: 483–490.
13.
SivakumarRSenthilkumarPSreenivasanM, et al.Comprehensive study of hydrogenated diamond-like carbon coated AISI 5140 alloy steel. In: KumaresanGShanmugamNSDhinakaranV (eds) Advances in materials research. Singapore: Springer Singapore, 2021, pp.531–541.
14.
SivakumarESenthilkumarP. Investigation on effect of H-DLC and TiN coated inlet and exhaust valve on performance, emission and combustion characteristics of a diesel engine. TAGA J2018; 14: 333–346.
CuiWQinGDuanJ, et al.A graded nano-TiN coating on biomedical Ti alloy: low friction coefficient, good bonding and biocompatibility. Mater Sci Eng C: Mater Biol Appl2017; 71: 520–528.
17.
YariMLarijaniMMAfsharA, et al.Physical properties of sputtered amorphous carbon coating. J Alloys Compd2012; 513: 135–138.
18.
OnoprienkoAADanylenkoMI. Annealing effects in ag-doped amorphous carbon films deposited by dc magnetron sputtering. Surf Coat Technol2012; 206: 3450–3453.
19.
YanMWangXZhouH, et al.Microstructure, mechanical and tribological properties of graphite-like carbon coatings doped with tantalum. Appl Surf Sci2021; 542: 148404.
20.
VoevodinAADonleyMS. Preparation of amorphous diamond-like carbon by pulsed laser deposition: a critical review. Surf Coat Technol1996; 82: 199–213.
21.
RobertsonJ. Diamond-like amorphous carbon. Mater Sci Eng Res Rep2002; 37: 129–281.
22.
PengZLiHChenD, et al.Microstructure, composition and properties of cr–GLC graded coating deposited by unbalanced magnetron sputtering. Mater Res Express2019; 6: 076427.
23.
ErdemirADonnetC. Tribology of diamond-like carbon films: recent progress and future prospects. J Phys D: Appl Phys2006; 39: R311–R327.
Borrero-LópezOHoffmanMBendavidA, et al.Substrate effects on the mechanical properties and contact damage of diamond-like carbon thin films. Diamond Relat Mater2010; 19: 1273–1280.
26.
WangJYazdiMAPLomelloF, et al.Influence of microstructures on mechanical properties and tribology behaviors of TiN/TiXAl1—XN multilayer coatings. Surf Coat Technol2017; 320: 441–446.
27.
HsiehJHLiangCYuCH, et al.Deposition and characterization of TiAlN and multi-layered TiN/TiAlN coatings using unbalanced magnetron sputtering. Surf Coat Technol1998; 108–109: 132–137.
28.
LalKMeikapAKChattopadhyaySK, et al.Electrical resistivity of titanium nitride thin films prepared by ion beam-assisted deposition. Phys B: Conden Matter2001; 307: 150–157.
29.
BanerjeeRChandraRAyyubP. Influence of the sputtering gas on the preferred orientation of nanocrystalline titanium nitride thin films. Thin Solid Films2002; 405: 64–72.
30.
JeyachandranYLNarayandassSKMangalarajD, et al.Properties of titanium nitride films prepared by direct current magnetron sputtering. Mater Sci Eng A2007; 445–446: 223–236.
31.
WuhrerRYeungWYPhillipsMR, et al.Study on d.c. magnetron sputter deposition of titanium aluminium nitride thin films: effect of aluminium content on coating. Thin Solid Films1996; 290–291: 339–342.
32.
WahlströmUHultmanLSundgrenJE, et al.Crystal growth and microstructure of polycrystalline Ti1−xAlxN alloy films deposited by ultra-high-vacuum dual-target magnetron sputtering. Thin Solid Films1993; 235: 62–70.
33.
KearneyBTJugdersurenBCulbertsonJC, et al.Substrate and annealing temperature dependent electrical resistivity of sputtered titanium nitride thin films. Thin Solid Films2018; 661: 78–83.
34.
MatthewsARickerbyDS. Advanced surface coatings: a handbook of surface engineering. Dordrecht: Springer, 1991.
35.
MonaghanDTeerDLoganP, et al.Deposition of wear resistant coatings based on diamond like carbon by unbalanced magnetron sputtering. Surf Coat Technol1993; 60: 525–530.
36.
SánchezNARinconCZambranoG, et al.Characterization of diamond-like carbon (DLC) thin films prepared by rf magnetron sputtering. Thin Solid Films2000; 373: 247–250.
37.
SarakinosKBraunAZilkensC, et al.Exploring the potential of high power impulse magnetron sputtering for growth of diamond-like carbon films. Surf Coat Technol2012; 206: 2706–2710.
38.
VoevodinACapanoMSafrietA, et al.Combined magnetron sputtering and pulsed laser deposition of carbides and diamond-like carbon films. Appl Phys Lett1996; 69: 188–190.
39.
LiuLWangTHuangJ, et al.Diamond-like carbon thin films with high density and low internal stress deposited by coupling DC/RF magnetron sputtering. Diamond Relat Mater2016; 70: 151–158.
40.
OliverWCPharrGM. Measurement of hardness and elastic modulus by instrumented indentation: Advances in understanding and refinements to methodology. J Mater Res2004; 19: 3–20. DOI: 10.1557/jmr.2004.19.1.3
41.
GouWLiGChuX, et al.Effect of negative self-bias voltage on microstructure and properties of DLC films deposited by RF glow discharge. Surf Coat Technol2007; 201: 5043–5045. https://doi.org/10.1016/j.surfcoat.2006.07.199
42.
MenčíkJ. Uncertainties and Errors in Nanoindentation. In: NemecekJ (ed) Nanoindentation in materials science. London, UK: IntechOpen, 2012.
43.
BhushanB. Nanotribology, nanomechanics, and materials characterization. In: BhushanB (ed) Nanotribology and nanomechanics II: nanotribology, biomimetics, and industrial applications. Berlin/Heidelberg: Springer Berlin Heidelberg, 2011, pp.3–106.
44.
BullSJ. Failure mode maps in the thin film scratch adhesion testTribol Int1997; 30: 491–498.
45.
SivakumarERSilambarasanRSenthilkumarP. Wear resistance investigation of tin and H-diamond like carbon coated AISI 5140 steel in dry sliding wear condition. J Balkan Tribol Assoc2018; 24: 663–673.
NledengvistPHogmarkS. Experiences from scratch testing of tribological PVD coatings. Tribol Int1997; 30: 507–516.
48.
KrishnaRJonesANEdgeR, et al.Residual stress measurements in polycrystalline graphite with micro-Raman spectroscopy. Radiat Phys Chem2015; 111: 14–23.
49.
FerrariACRobertsonJ. Interpretation of Raman spectra of disordered and amorphous carbon. Phys Rev B2000; 61: 14095.
50.
PangHWangXZhangG, et al.Characterization of diamond-like carbon films by SEM, XRD and Raman spectroscopy. Appl Surf Sci2010; 256: 6403–6407.
51.
CaoCZhuHWangH. Electrodeposition diamond-like carbon films from organic liquids. Thin Solid Films2000; 368: 203–207.
52.
TuinstraFKoenigJL. Raman spectrum of graphite. J Chem Phys1970; 53: 1126–1130.
53.
VishwakarmaPNPrasadVSubramanyamSV, et al.Structural morphology of amorphous conducting carbon film. Bull Mater Sci2005; 28: 609–615.
54.
DillonROWoollamJAKatkanantV. Use of Raman scattering to investigate disorder and crystallite formation in as-deposited and annealed carbon films. Phys Rev B1984; 29: 3482–3489.
55.
CapoteGCoratEJTrava-AiroldiVJ. Deposition of amorphous hydrogenated carbon films on steel surfaces through the enhanced asymmetrical modified bipolar pulsed-DC PECVD method. Surf Coat Technol2014; 260: 133–138.
56.
VettivelSCJeganRVigneshJ, et al.Surface characteristics and wear depth profile of the TiN, TiAlN and AlCrN coated stainless steel in dry sliding wear condition. Surf Interf2017; 6: 1–10.
57.
HuangXEtsionIShaoT. Effects of elastic modulus mismatch between coating and substrate on the friction and wear properties of TiN and TiAlN coating systems. Wear2015; 338–339: 54–61.
58.
SaravananIElaya PerumalAVettivelSC, et al.Optimizing wear behavior of TiN coated SS 316L against Ti alloy using response surface methodology. Mater Des2015; 67: 469–482.
59.
ŁępickaMGrądzka-DahlkeM. Surface modification of Ti6Al4V titanium alloy for biomedical applications and its effect on tribological performance-a review. Rev Adv Mater Sci2016; 46: 86–103.
60.
DearnleyPNevilleATurnerS, et al.Coatings tribology drivers for high density plasma technologies. Surf Eng2010; 26: 80–96.
61.
DhandapaniVSThangavelEArumugamM, et al.Effect of Ag content on the microstructure, tribological and corrosion properties of amorphous carbon coatings on 316L SS. Surf Coat Technol2014; 240: 128–136.
62.
SolisJZhaoHWangC, et al.Tribological performance of an H-DLC coating prepared by PECVD. Appl Surf Sci2016; 383: 222–232.