Influence of a Ni-interlayer addition on microstructure,mechanical properties and corrosion resistance of dissimilar joints between Nimonic 75 alloy/Nitronic 50 steel using gas tungsten arc welding
The study investigates the effects of incorporating a nickel interlayer on the dissimilar metal weld (DMW) between Nimonic 75 superalloy (N75) and Nitronic 50 steel (N50) using the gas tungsten arc welding technique. A comparative investigation was made on the DMWs fabricated with and without an interlayer of 0.1 mm thickness. The weld metal (WM) fabricated with a nickel interlayer (named as interlayer weld) revealed the existence of both columnar and equiaxed dendrites compared to coarser columnar dendrites for the weld fabricated without an interlayer (named as autogenous weld). In addition, the interlayer weld facilitated the minimization of the welding thermal effects at the weld interface of the interlayer weld compared to the autogenous weld. The presence of finer equiaxed dendrites associated with a lesser degree of precipitation within the WM caused an increased microhardness, strength, and higher energy absorption for the interlayer weld. However, the fractured surfaces indicated ductile failure for both the DMWs. Additionally, the interlayer weld revealed improved corrosion resistance than the autogenous weld.
KhakianMNateghSMirdamadiS. Effect of bonding time on the microstructure and isothermal solidification completion during transient liquid phase bonding of dissimilar nickel-based superalloys IN738LC and Nimonic 75. J Alloys Compd2015; 653: 386–394.
2.
SinghSSinghABKumarM, et al.Dissimilar metal welds used in AUSC power plant, fabrication and structural integrity issues. IOP Conf Ser Mater Sci Eng2021; 1017: 012022.
3.
JibhakateRARamtekeSMSharmaS. Effect of heat input on the microstructures and mechanical properties of gas tungsten arc welded dissimilar joints between Hastelloy C-22 and Nitronic 50 stainless steel. Proc Inst Mech Eng L: J Mater Des Appl2025. DOI: https://doi.org/10.1177/14644207251369092.
4.
ElAFabioHAntonelloS, et al.Cold spinning of Nimonic 75 parts. Microstruct Evol Heat Treat2019; 8: 488–494.
5.
ZhangHLiPWangQ, et al.Electron beam welding of Nimonic 80A superalloy: microstructure evolution and EBSD study after aging heat treatment. J of Materi Eng and Perform2019; 28: 741–752.
6.
MorrisJWGuoZKrennCR, et al.The limits of strength and toughness in steel. ISIJ Int2001; 41: 599–611.
7.
RitterAHenryMF. Phase transformations during aging of a nitrogen-strengthened austenitic stainless steel. Metall Trans A1985; 16: 1759–1771.
8.
PadhanADSSharmaS.Influence of heat input on the microstructures, mechanical properties, and corrosion behaviour of dissimilar Nimonic 75 superalloy and Nitronic 50 austenitic stainless steel GTA welds. Proc Inst Mech Eng, L: J Mater: Des Appl. 2025. doi:10.1177/14644207251393426.
9.
KumarNAroraNSKG. Study on metallurgical and mechanical aspects of GMA welded nitronic steel under the influence of weld quenching. J Manuf Process2020; 56: 116–130.
10.
KhorramAHabibiHYazdipourA. The effect of diffusion welding parameters on the microstructural characteristics and mechanical properties of dissimilar joint between AISI 418 stainless steel and Inconel 738 superalloy using nickel interlayer. JWSTI2024; 10: 47–64.
11.
KumarNAroraN. Welding of nitrogen containing austenitic stainless steel using GMAW process. Mater Today Proc2021; 44: 1964–1968.
12.
XinJZhangHSunW, et al.Microstructures and mechanical properties of dissimilar laser welding of copper and 316L stainless steel with Ni interlayer. Cryogenics2021; 118: 103344.
13.
MauryaAKPandeyCChhibberR. Dissimilar welding of duplex stainless steel with Ni alloys: a review. Int J Press Vessel Pip2021; 192: 104439.
14.
FandeAWTaiwadeRVKumarN. Improvement in the microstructural properties of super duplex and austenitic stainless steel dissimilar joints by incorporating Ni-based austenitic interlayer. Mater Today Commun2022; 33: 104723.
15.
NieQWangXLiJ, et al.Effect of Ni interlayer on the microstructure, mechanical and corrosion properties of the dissimilar 1MnCrMoNi/X70 steels friction welding joint. Sci Technol Weld Join2021; 27: 61–67.
16.
WooIKikuchiY. Weldability of high nitrogen stainless steel. ISIJ Int2002; 42: 1334–1343.
17.
CaiXSunDLiH, et al.Dissimilar joining of TiAl alloy and Ni-based superalloy by laser welding technology using V/Cu composite interlayer. Opt Laser Technol2019; 111: 205–213.
18.
XiongJ. Diffusion bonding of nickel-based superalloy GH4099 with pure nickel interlayer. J Mater Sci2019; 54: 6552–6564.
19.
WangTZhangBChenG, et al.High strength electron beam welded titanium-stainless steel joint with V/Cu based composite filler metals. Vacuum2013; 94: 41–47.
WangZQWangXLNanYR, et al.Effect of Ni content on the microstructure and mechanical properties of weld metal with both-side submerged arc welding technique. Mater Charact2018; 138: 67–77.
22.
KurtBOrhanNSomunkiranI, et al.The effect of austenitic interface layer on microstructure of AISI 420 martensitic stainless steel joined by keyhole PTA welding process. Mater Des2009; 30: 661–664.
23.
KulkarniADwivediDKVasudevanM. Dissimilar metal welding of P91 steel–AISI 316L SS with Incoloy 800 and Inconel 600 interlayers by using activated TIG welding process and its effect on the microstructure and mechanical properties. J Mater Process Technol2019; 274: 116280.
24.
GaoXLiLLiuJ, et al.Analysis of Ni interlayer effects on laser beam welding of dissimilar pure Mo alloy to stainless steel. Int J Refract Met Hard Mater2021; 100: 105654.
25.
XiongJYuanLZhuY, et al.Diffusion bonding of nickel-based superalloy GH4099 with pure nickel interlayer. J Mater Sci2019: 6552–6564.
26.
CheepuMMuthupandiMAStainlessÁ. A new approach for using an interlayer and analysis of the friction welding of titanium to stainless steel. Trans Indian Inst Met2017; 70: 2591–2600.
27.
KangazianJShamanianM. Micro-texture and corrosion behavior of dissimilar joints of UNS S32750 stainless steel/UNS N08825 Ni-based superalloy. Mater Charact2019; 155: 109802.
28.
KangazianJShamanianM. Mechanical and microstructural evaluation of SAF 2507 and Incoloy 825 dissimilar welds. J Manuf Process2017; 26: 407–418.
29.
RamkumarTSelvakumarMNarayanasamyP, et al.Studies on the structural property, mechanical relationships and corrosion behaviour of Inconel 718 and SS 316L dissimilar joints by TIG welding without using activated flux. J Manuf Process2017; 30: 290–298.
30.
Anil KumarSSChopkarMKVermaJ, et al.Effect of filler and autogenous TIG welding on microstructure, mechanical properties and corrosion resistance of Nitronic 50 stainless steel. Mater Res Express2018; 6: 026557.
31.
ZhouXLiuDZhuW, et al.Morphology, microstructure and decomposition behavior of M2C carbides in high speed steel. J Iron Steel Res Int2017; 24: 43–49.
32.
KumarASharmaAGoelSK. Effect of heat treatment on microstructure, mechanical properties and erosion resistance of cast 23-8-N Nitronic steel. Mater Sci Eng A2015; 637: 56–62.
33.
SharmaSTaiwadeRVVashishthaH, et al.Consumable selection for pulsed current gas tungsten arc welded bimetallic joints between Super C-276 alloy and Ti-stabilized Grade 321. J Manuf Process2018; 32: 32–47.
34.
GuptaSKPatilAPRathodRC, et al.Tailoring the process parameters for Ti-stabilized 439 ferritic stainless steel welds by cold metal transfer process. J Mater Eng Perform2022; 33: 10663–10659.
35.
ShinozakiK. Welding and joining Fe and Ni-base superalloys. Weld Int2009; 15: 593–610.
36.
SharmaSTaiwadeRVVashishthaH. Effect of pulsed current gas tungsten arc process on the dissimilar weldments between nickel-based superalloy/austenitic stainless steel. ISIJ Int2017; 57: 1080–1086.
37.
SayiramGArivazhaganN. Microstructural characterization of dissimilar welds between Incoloy 800H and 321 austenitic stainless steel. Mater Charact2015; 102: 180–188.
38.
BanovicSWDupontJNMarderAR. Dilution and microsegregation in dissimilar metal welds between super austenitic stainless steel and nickel base alloys. Sci Technol Weld Join2002; 7: 374–383.
39.
MingHZhangZWangJ, et al.Microstructural characterization of an SA508–309L/308L–316L domestic dissimilar metal welded safe-end joint. Mater Charact2014; 97: 101–115.
40.
SireeshaMShankarVAlbertSK, et al.Microstructural features of dissimilar welds between 316LN austenitic stainless steel and alloy 800. Mater Sci Eng A2000; 292: 74–82.
41.
BaeslackBYWLippoldJC. Unmixed zone formation in austenitic stainless steel weldments. Weld J1979; 58: 168–176.
42.
VashishthaHTaiwadeRVSharmaS, et al.Effect of welding processes on microstructural and mechanical properties of dissimilar weldments between conventional austenitic and high nitrogen austenitic stainless steels. J Manuf Process2017; 25: 49–59.
43.
LippoldJCKoteckiDJ. Welding metallurgy and weldability of stainless steels. Hoboken: John Wiley & Sons, 2005.
44.
KinaAYSouzaVMTavaresSSM, et al.Microstructure and intergranular corrosion resistance evaluation of AISI 304 steel for high temperature service. Mater Charact2007; 59: 651–655.
45.
KulkarniADwivediDKVasudevanM. Microstructure and mechanical properties of A-TIG welded AISI 316L SS–Alloy 800 dissimilar metal joint. Mater Sci Eng A2020; 790: 139685.
46.
BangKPakSAhnS. Evaluation of weld metal hot cracking susceptibility in superaustenitic stainless steel. Met Mater Int2013; 19: 1267–1273.
47.
YanWShanYYYangK. Effect of TiN inclusions on the impact toughness of low-carbon microalloyed steels. Metall Mater Trans A2006; 37: 2147–2158.
48.
YanWShanYYYangK. Influence of TiN inclusions on the cleavage fracture behavior of low-carbon microalloyed steels. Miner Met Mater Soc ASM Int2007; 38: 1211–1222.
49.
JengSLChangYH. Microstructure and flow behavior of Ni-Cr-Fe welds with Nb and Mo additions. Mater Sci Eng A2013; 560: 343–350.
50.
KeehanEZachrissonJKarlssonL. Influence of cooling rate on microstructure and properties of high strength steel weld metal. Sci Technol Weld Join2013; 17: 233–238.
51.
HosseiniHSShamanianMKermanpurA. Characterization of microstructures and mechanical properties of Inconel 617/310 stainless steel dissimilar welds. Mater Charact2011; 62: 425–431.
52.
XuTShiYJiangZ, et al.Improvement of cryogenic toughness for 9% Ni steel keyhole TIG butt-welded joints with a Ni interlayer. Mater Sci Eng A2022; 835: 142661.
53.
MileticLIIlicANikolicRR, et al.Analysis of influence of the welding procedure on impact toughness of welded joints. Appl Sci2020; 10: 2205.
54.
TandonVThombreMAPatilAP, et al.Effect of heat input on the microstructural, mechanical, and corrosion properties of dissimilar weldment of conventional austenitic stainless steel and low-nickel stainless steel. Metallogr Microstruct Anal2020; 9: 668–677.
55.
TandonVPatilAPRathodRC. Enhanced corrosion resistance of Cr-Mn ASS by low temperature salt bath nitriding technique for the replacement of convectional Cr-Ni ASS. Anti-Corros Method Mater2019; 66: 439–445.
56.
KhanNAChakrabortyDKumarA. Effect of solution heat treatment on corrosion performance of multi-pass friction stir processed AA6061/ceria-stabilized zirconia composites for marine applications. J Mater Eng Perform2025; 34: 29340–29352.
57.
LimJYMcKrellTJEastwickG, et al.Corrosion of materials in supercritical carbon dioxide environments. In: Proceedings of the corrosion 2008. New Orleans, LA, 2008, 1–18.
58.
DandekarTRGuptaAKhatirkarRK, et al.Evolution of microstructure and texture in UNS S32750 super duplex stainless steel weldments. Trans Indian Inst Met2021; 74: 2267–2283.