Thermal cracking of a railway wheel tread due to tread braking–critical crack sizes and in fluence of repeated thermal cycles

Abstract

A numerical study of tread cracking due to thermal loading induced by tread braking is carried out. The analysis features a computationally efficient approach combining two-dimensional finite-element simulations with an analytical evaluation of resulting stress intensity factors. The analysis identifies critical sizes for when existing surface cracks are prone to propagate under thermal loading and resulting crack lengths after propagation. The results imply that fully functional brake systems are not likely to induce thermal crack propagation under normal stop braking, but that with pre-existing defects, a severe drag braking due to malfunctioning brakes may cause very deep cracking. Furthermore, the analysis concludes the cracking to be a static phenomenon related to the most severe brake cycle, i.e. later brake cycles of similar or lower severity will not cause any significant propagation of existing cracks. Additional three-dimensional finite-element simulations are used to validate the model, and they indicate two-dimensional results to be on the conservative side.

This paper originated from the 2011 IHHA Conference.

Keywords

Railway tread braking thermal cracking critical crack sizes

Get full access to this article

View all access options for this article.

References

Lewis

Olofsson

. Wheel-rail interface handbook, Oxford, Cambridge, New Delhi: Woodhead Publishing Limited and CRC Press LLC, 2009.

Vernersson

Caprioli

Kabo

Hansson

Ekberg

. Wheel tread damage: a numerical study of railway wheel tread plasticity under thermomechanical loading. In: Proc IMechE, Part F: J Rail and Rapid Transit 2010; 224.5: 435–443. doi: 10.1243/09544097JRRT358.

Abaqus. Abaqus analysis user's manual, 6.10. Providence, Rhode Island, USA: Simulia, 2010.

Vernersson T. Tread braking of railway wheels-noise related tread roughness and dimensioning wheel temperatures. PhD thesis. Chalmers University of Technology, 2006.

Jergeús

Lunden

. Thermally damaged railway wheels detected through a lateral measuring of residual deformations, Gothenburg: Chalmers University of Technology, Division of Solid Mechanics, 1992.

Donzella

Scepi

Solazzi

Trombini

. The effect of block braking on the residual stress state of a solid railway wheel. In: Proc IMechE, Part F: J Rail and Rapid Transit 1998; 212.2: 145–158. doi: 10.1243/0954409981530751.18.

Meizoso A, Mesnaola J and Giminez J. Life prediction of thermally cracked railway wheels: crack growth under mixed mode stress fields. In: Proc Int Wheelset Congress Sydney, Australia, 1992, pp. 169–173.

Murakami

. Stress intensity factors handbook 1987; Volume 1, Oxford, UK: Pergamon Press.

Diener

Ghidini

. Reliability and safety in railway products, a challenge for appliers and producers, Lucchini RS, Italy: La cittadinanza azienda grafica, 2008.

10.

Dowling

. Mechanical behavior of materials. Engineering methods for deformation, fracture, and fatigue, Upper Saddle River, NJ, USA: Pearson Prentice Hall, 1993.

11.

Anderson

. Fracture mechanics. Fundamentals and applications, 2nd edn. Boca Raton, Florida, USA: CRC Press, 1995.

12.

Gianni

Ghidini

Karlsson

Ekberg

. Bainitic steel grade for solid wheels: metallurgical, mechanical, and in-service testing. In: Proc IMechE, Part F: J Rail and Rapid Transit 2009; 223.2: 163–171. doi: 10.1243/09544097JRRT217.