A series of carbazole substituted poly(dimethylsiloxane) (PDMS) was synthesized by hydrosilylation reaction of 9-vinyl carbazole into PDMS structure. It was then crosslinked with vinyl trimethoxysilane by condensation reaction. The fabricated product increased in refractive index with increasing carbazole content. The higher carbazole content also produced high thermal stability with an increase in Tg and degradation temperature. This behaviour owe much to the carbazole moiety as well as the formation of crosslink network These features contribute to potential use as electronic devices encapsulants and coatings.
KumarR., KeemL.Y., MangN.C., and AbubakarA.Ultraviolet radiation curable epoxy resin encapsulant for light emitting diodes, Journal of applied polymer science, 100 (2006) 1048–1056.
2.
DasguptaP.K., EomI.-Y., MorrisK.J., and LiJ.Light emitting diode-based detectors: Absorbance, fluorescence and spectroelectrochemical measurements in a planar flow-through cell, Analytica Chimica Acta, 500 (2003) 337–364.
3.
CareyJ.A., CollinsW.D.III, and PosseltJ.L. High stability optical encapsulation and packaging for light-emitting diodes in the green, blue, and near UV range, U.S. Patent 6,204,523. (2003).
4.
TaiH.J., WangJ., ChenJ.H., and ChouH.L.Synthesis and properties of vinyl siloxane modified cresol novolac epoxy for electronic encapsulation, Journal of applied polymer science, 79 (2000) 652–661.
5.
ChojnowskiJ., and CyprykM.Synthesis of linear polysiloxanes, Silicon-containing Polymers.The Science and Technology of their Synthesis and Applications, (2000).
6.
KimJ.-S., YangS., and BaeB.-S.Thermal stability of sol–gel derived methacrylate oligosiloxane-based hybrids for LED encapsulants, Journal of Sol-gel Science and Technology, 53 (2010) 434–440.
7.
SafaK., BahadoriA., TofangdarzadehS., and NasirtabriziM.Trisyl modification of epoxy-and chloromethyl-polysiloxanes, Journal of the Iranian Chemical Society, 5 (2008) 37–47.
8.
WangW.Synthesis and characterization of UV-curable polydimethylsiloxane epoxy acrylate, European polymer journal, 39 (2003) 1117–1123.
9.
XieK., XuL., and ShiY.Modification and application of the polysiloxane with amino groups, J. Fiber Bioeng. Informatics, 1 (2008) 71–76.
10.
McGrathJ.E., RasmussenL., ShultzA.R., ShobhaH.K., SankarapandianM., GlassT., LongT.E., and PasqualeA.J.Novel carbazole phenoxy-based methacrylates to produce high-refractive index polymers, Polymer, 47 (2006) 4042–4057.
11.
RamliM.R., BisyrulM., OthmanH., ArifinA., and AhmadZ.Crosslink network of polydimethylsiloxane via addition and condensation (RTV) mechanisms. Part I: Synthesis and thermal properties, Polymer Degradation Stability, 96 (2011) 2064–2070.
12.
SperlingL.H.Introduction to physical polymer science, Wiley-Interscience, 2005.
13.
HauserR.L., WalkerC., and KilbourneF.Swelling of silicone elastomers, Industrial & Engineering Chemistry, 48 (1956) 1202–1208.
14.
ThomasV., and JayabalanM.A new generation of high flex life polyurethane urea for polymer heart valve—studies on in vivo biocompatibility and biodurability, Journal of Biomedical Materials Research Part A, 89 (2009) 192–205
15.
JinX., and ZhuD.Influence of curing temperature on the optical properties of fluorinated polyimide thin films, European Polymer Journal, 44 (2008) 3571–3577.
CromptonT.Analysis of organosilicon compoundsOrganic Silicon Compounds Volume 1 and Volume 2 (1989) 393–444.
18.
MoonI.K., OhJ.-W., and KimN.Synthesis and optical properties of benzocarbazole-substituted polysiloxanes for polymeric photorefractive materials, Journal of Photochemistry and Photobiology A: Chemistry, 194 (2008) 351–355.
19.
JewellJ.M.Model for the thermo-optic behavior of sodium borate and sodium aluminosilicate glasses, Journal of Non-crystalline Solids, 146 (1992) 145–153.
20.
KohjiyaS., and MaedaK., YamashitaS., ShibataY.Chemical modification of silicone elastomers for optics, Journal of Materials Science, 25 (1990) 3368–3374.
ChenD., NieJ., YiS., WuW., ZhongY., LiaoJ., and HuangC.Thermal behaviour and mechanical properties of novel RTV silicone rubbers using divinyl-hexa(trimethoxysilyl) ethyl]-POSS as crosslinker, Polymer Degradation and Stability, 95 (2010) 618–626.
23.
HuangY.-J., and LiangC.-M.Volume shrinkage characteristics in the cure of low-shrink unsaturated polyester resins, Polymer, 37 (1996) 401–412.
24.
TyngL.Y., RamliM.R., OthmanM.B.H., RamliR., IshakZ.A.M., and AhmadZ.Effect of crosslink density on the refractive index of a polysiloxane network based on 2,4,6,8-tetramethyl-2,4,6, 8-tetravinylcyclotetrasiloxane, Polymer International, 62 (2013) 382–389.
25.
DeshpandeG., and RezacM.E.Kinetic aspects of the thermal degradation of poly (dimethyl siloxane) and poly (dimethyl diphenyl siloxane), Polymer Degradation and Stability, 76 (2002) 17–24.
26.
HuangC.C., YangM.S., and LiangM.Synthesis of new thermosetting poly (2, 6-dimethyl-1, 4-phenylene oxide) s containing epoxide pendant groups, Journal of Polymer Science Part A: Polymer Chemistry, 44 (2006) 5875–5886.