Experimental Failure Analysis of Glass-Epoxy Laminated Composite Bolted-Joints with Clearance Under Preload

Abstract

In this study, a failure analysis of glass-epoxy laminated composite bolted-joints with bolt/hole clearance under various torques was carried out. To estimate the effects of joint geometry and fiber orientation on the failure strength and failure mode, parametric studies were conducted experimentally. The two different geometrical parameters were the edge distance-to-hole diameter ratio (E/D) and plate width-to-hole diameter ratio (W/D), E/D ratio was selected from 1 to 5, and W/D ratio was chosen from 2 to 5. The bolt preload torque was also carried out as 0, 3, and 6 Nm. To investigate the material parameters effect, laminated plates were oriented as three different stacking sequences [90^o]₈, [45^o]₈, and [0^o]₈. The experiments were carried out with a clearance between the diameters of the bolt and the circular hole of 5 and 6 mm, respectively. According to experimental results, failure mode and bearing strength are strongly influenced by both material parameters and geometrical parameters. Additionally, when a torque is applied to the bolted-joints, the failure mechanism is affected by its increasing values.

Keywords

glass-epoxy composites laminated composites bolted joints bearing strength failure analysis.

Get full access to this article

View all access options for this article.

References

Aktas, A. and Dirikolu, M.H. ( 2003). The Effect of Stacking Sequence of Carbon Epoxy Composite Laminates on Pinned-joint Strength, Composite Structures , 62: 107-111.

Chang, F.K. ( 1986). The Effect of Pin-load Distribution on the Strength of Pin Loaded Holes in Laminated Composites, Journal of Composite Materials, 20: 401-408.

Chang, F.K. , Scott, R.A. and Springer, G.S. ( 1982). Strength of Mechanically Fastened Composite Joints , Journal of Composite Materials, 16: 470-494.

Chang, F.K. , Scott, R.A. and Springer, G.S. ( 1984). Failure Strength of Nonlinearly Elastic Composite Laminates Containing a Pin Loaded Hole, Journal of Composite Materials , 18: 464-477.

Cheng, M. and Chen, W. ( 2006). Modeling Transverse Behavior of Kevlar Km2 Single Fibers with Deformation-induced Damage, International Journal of Damage Mechanics, 15: 5-39.

Dano, M.L. , Gendron, G. and Picard, A. ( 2000). Stress and Failure Analysis of Mechanically Fastened Joints in Composite Laminates, Composite Structures, 50: 287-296.

Gibson, R.F. ( 1994). Principles of Composite Material Mechanics, Mc Graw-Hill, New York.

Hamada, H. and Maekawa, Z.I. ( 1996). Strength Prediction of Mechanically Fastened QuasiIsotropic Carbon/Epoxy Joints, Journal of Composite Materials, 30: 1596-1612.

İçten, B.M. and Sayman, O. ( 2003). Failure Analysis of Pin-loaded Aluminum-glass-epoxy Sandwich Composite Plates, Composites Science and Technology , 63: 727-737.

10.

Jones, R.M. ( 1999). Mechanics of Composite Material, Taylor & Francis, Philadelphia.

11.

Ju, J.W. , Ko, Y.F. and Ruan, H.N. ( 2006). Effective Elastoplastic Damage Mechanics for Fiber-reinforced Composites with Evolutionary Complete Fiber Debonding, International Journal of Damage Mechanics, 15: 237-265.

12.

Lin, C.-C. and Lin, C-H. ( 1999). Stresses around Pin-loaded Hole in Composite Laminates Using Direct Boundary Element Method, International Journal of Solids and Structures, 36: 763-783.

13.

Mallick, P.K. ( 1993). Fiber-reinforced Composites Materials, Manufacturing, and Design, 2nd edn, Marcel Decker , New York, USA.

14.

Okutan, B. ( 2002). The Effects of Geometric Parameters on the Failure Strength for Pin-loaded Multi-directional Fiber-Glass Reinforced Epoxy Laminate , Composites Part B: Engineering, 33: 567-578.

15.

Pierron, F. , Cerisier, F. and Grediac, M. ( 2000). A Numerical and Experimental Study of Woven Composite Pin-joints, Journal of Composite Materials, 34: 1028-1054.

16.

Reddy, J.N. ( 1997). Mechanics of Laminated Composite Plates Theory and Analysis, Florida, USA, CRC Press.

17.

Scalea, F.L.D. , Cappello, F. and Cloud, G.L. ( 1999). On the Elastic Behavior of a Cross-Ply Composite Pin-joint with Clearance Fits, Journal of Thermoplastic Composite Materials , 12: 13-22.

18.

Tong, L. ( 2000). Bearing Failure of Composite Bolted Joints with Non-uniform Bolt-to-Washer Clearance, Composites Part A: Applied Science and Manufacturing, 31: 609-615.

19.

Whitworth, H.A. , Othieno, M. and Barton, O. ( 2003). Failure Analysis of Composite Pin Loaded Joints , Composite Structures, 59: 261-266.

20.

Wu, T.J. and Hahn, H.T. ( 1997). The Bearing Strength of E-Glass/Vinyl-Ester Composites Fabricated by Vartm, Composites Science and Technology, 58: 1519-1529.