Modeling Damage of the Hydrogen Enhanced Localized Plasticity in Stress Corrosion Cracking

Abstract

Stress corrosion cracking is an important and complex mode of failure in high-performance structural metals operating in deleterious environments, due to metallurgical, mechanical, and electrochemical factors. Depending on the material/solution system, the stress corrosion cracking mechanism may involve a combination of hydrogen embrittlement (HE) and anodic dissolution. In this article, a numerical model for predicting the mechanical behavior of hydrogen-induced damage in stress corrosion cracking is described. The methodology of modeling used in this study is based on the thermodynamics of continuum solids and elastoplastic damage. This model is based on a stress corrosion mechanism that occurs through the simultaneous interaction of hydrogen and plasticity. This mechanism is also called hydrogen-enhanced localized plasticity, which is a viable mechanism for hydrogen embrittlement. The model is applied to the fatigue damage problems of nuclear reactor pipe, and the results are compared with published fatigue life data obtained experimentally.

Keywords

stress corrosion cracking hydrogen embrittlement hydrogen-enhanced localized plasticity damage plasticity.

Get full access to this article

View all access options for this article.

References

Ahn, D.C. , Sofronis, P. and Dodds Jr, R.H. ( 2006). On Hydrogen-induced Plastic Flow Localization During Void Growth and Coalescence, International Journal of Hydrogen Energy, 32: 3734-3742.

Beachem, C.D. ( 1972). New Model for Hydrogen-assisted Cracking (Hydrogen Embrittlement) , Metallurgical and Materials Transactions B, 3: 441-455.

Birnbaum, H.K. and Sofronis, P. ( 1994). Hydrogen-enhanced Localized Plasticity - A Mechanism for Hydrogen-related Fracture, Materials Science and Engineering: A, 176: 191-202.

Chaboche, J.L. ( 1992). Continuum Damage Mechanics. Library of Congress Cataloguing In Publication data, Berlin, Springer-Verlag.

Chene, J. and Brass, A.M. ( 1992). Interaction Hydrogène - Métal, In: D. Desjardins and R. Oltra (eds), Corrosion Sous Contrainte - Phénoménologie et Mécanismes, Bombannes 1990, France Physique Editions , pp. 159-210.

Chopra, O.K. ( 1999). Effects of LWR Coolant Environments on Fatigue Design Curves of Austenitic Stainless Steels (NUREG/CR-5704, ANL-98/31), Technical Report prepared for NRC Documents Publications, Washington.

Chopra, O.K. and Shack, W.J. ( 2007). Effect of LWR Coolant Environments on the Fatigue Life of Reactor Materials (NUREG/CR-6909), Technical Report prepared for NRC Documents Publications, Washington.

Gilman, J.J. ( 1969). Micromechanics of Flow in Solids, New York, McGraw-Hill, pp. 185-199.

Hirth, J.P. ( 1980). Effects of Hydrogen on the Properties of Iron and Steel , Metallurgical and Materials Transactions A, 11: 861-890.

10.

Hirth, J.P. and Carnahan, B. ( 1978). Hydrogen Adsorption at Dislocations and Cracks in Fe , Acta Metallurgica, 26: 1795-1803.

11.

Lemaitre, J. and Chaboche, J.L. ( 1985). Mécanique des Milieux Solides, Paris, Dunod (French edition).

12.

McLellan, R.B. ( 1979). Thermodynamics and Diffusion Behaviour of Interstitial Solute Atoms in Crystals, Acta Metallurgica, 27: 1655-1663.

13.

Oriani, R.A. ( 1970). The Diffusion and Trapping of Hydrogen in Steel, Acta Metallurgica, 18: 147-157.

14.

Oriani, R.A. ( 1984). The Diffusion and Trapping of Hydrogen in Steel, In: Gibala, R. and Hehemann, R.F. (eds), Hydrogen Embrittlement and Stress Corrosion Cracking, Materials Park, OH, ASM International, pp. 29-41.

15.

Peisl, H. ( 1978). Lattice Strains due to Hydrogen in Metals, In: Alefeld, G. and Volkl, J. (eds), Hydrogen in Metals I, New York , Springer-Verlag, Vol. 28, pp. 53-74.

16.

Petch, N.J. ( 1956). Lowering of the Fracture Stress due to Surface Adsorption , Philosophical Magazine, 1: 331-335.

17.

Sofronis, P. , Liang, Y. and Aravas, N. ( 2001). Hydrogen Induced Shear Localisation of the Plastic Flow in Metals and Alloys, European Journal of Mechanics. A. Solids , 20: 857-872.

18.

Tabata, T. and Birnbaum, H.K. ( 1983). Direct Observation of the Effect of Hydrogen on the Behavior of Dislocations in Iron, Scripta Metallurgica, 17: 947-950.

19.

Thomas, G.J. ( 1980). Hydrogen Trapping in FCC Metals, In: Thompson, A.W. and Bernstein, I.M. (eds), Hydrogen Effects in Metals, New York, Transactions of the Metallurgical Society, AIME, pp. 77-85.

20.

Tien, J.K. , Thomson, A.W. , Bernstein, I.M. and Richards, R.J. ( 1976). Hydrogen Transport by Dislocations, Metallurgical and Materials Transactions A, 7: 821-829.

21.

Troiano, A.R. ( 1960). The Role of Hydrogen and Other Interstitials in the Mechanical Behavior of Metals, Trans. ASM, 52: 54-80.