This study considers the bearing strengths and failure modes of woven-glass–epoxy prepreg composite mechanically fastened joints. For the study, the specimens were immersed in natural seawater in the laboratory for over 1 year. The edge distance-to-hole diameter (E/D) ratio and the specimen width-to-hole-diameter ratio (W/D) were systematically altered during experiments. Failure modes were determined by observing the failure regions on the specimens. Damage progression in pin-loaded specimens prepared from woven-glass–epoxy prepreg was also examined using a scanning electron microscopy for three different percentages of ultimate failure load. According to the experimental investigation results, it was observed that the bearing load values obtained from the specimens immersed in seawater decreased considerably in comparison to unimmersed specimens.
AktaşA.DirikoluM.H. (2003). The Effect of Stacking Sequence of Carbon Epoxy Composite Laminates on Pinned-Joint Strength, Composite Structures, 62: 107–111.
2.
AktaşA.Uzunİ. (2008). Sea Water Effect on Pinned-Joint Glass Fibre Composite Materials, Composite Structures, 85: 59–63.
3.
ArunK.V.BasavarajappaS.SherigaraB.S. (2010). Damage Characterisation of Glass/Textile Fabric Polymer Hybrid Composites in Seawater Environment, Materials and Design, 31: 930–939.
4.
ASTM D 953-D (1982). Standard Test Method for Bearing Strength of Plastics, ASTM Designation, pp. 342–346.
5.
CamanhoP.P.MatthewsF.L. (1999). A Progressive Damage Model for Mechanically Fastened Joints in Composite Laminates, Journal of Composite Materials, 33: 2248–2280.
6.
ChoiJ.H.BanC.S.KweonJ.H. (2008). Failure Load Prediction of a Mechanically Fastened Composite Joint Subjected to a Clamping Force, Journal of Composite Materials, 42: 1415–1429.
7.
ChungC.-H.LeeY.-J. (2005). Progressive Failure of Marine GFRP Laminated Plates Under Static Water Pressure, Journal of Composite Materials, 39: 1081–1102.
8.
CollingsT.A. (1982). On the Bearing Strengths of Carbon Fiber–Reinforced Plastic Laminates, Composites, 13: 241–252.
9.
DanoM.-L.GendronG.PicardA. (2000). Stress and Failure Analysis of Mechanically Fastened Joints in Composite Laminates, Composite Structures, 50: 287–296.
10.
EsendemirÜ. (2008). Failure Analysis of Woven Glass-Epoxy Prepreg Bolted Joints under Different Clamping Moments, Advanced Composite Letters, 17: 165–175.
11.
FrizzellR.M.McCarthyC.T.McCarthyM.A. (2008). An Experimental Investigation into the Progression of Damage in Pin-Loaded Fibre Metal Laminates, Composites Part B: Engineering, 39: 907–925.
12.
HuangG.SunH. (2007). Effect of Water Absorption on the Mechanical Properties of Glass/Polyester Composites, Materials and Design, 28: 1647–1650.
13.
KootsookosA.MouritzA. (2004). Seawater Durability of Glass- and Carbon-Polymer Composites, Composite Science and Technology, 64: 1503–1511.
MallickP.K. (1993). Fiber-Reinforced Composites, New York, Marcel Dekker Inc.
16.
OkutanB.AslanZ.KarakuzuR. (2001). A Study of the Effects of Various Geometric Parameters on the Failure Strength of Pin-Loaded Woven-Glass-Fiber Reinforced Epoxy Laminate, Composite Science and Technology, 61: 1491–1497.
17.
OkutanB.KarakuzuR. (2003). The Strength of Pinned Joints in Laminated Composites, Composite Science and Technology, 63: 893–905.
18.
PalP.BhattacharyyaS.K. (2007). Progressive Failure Analysis of Cross-ply Laminated Composite Plates by Finite Element Method, Journal of Reinforced Plastics and Composites, 26: 465–477.
19.
PalP.RayC. (2002). Progressive Failure Analysis of Laminated Composite Plates by Finite Element Method, Journal of Reinforced Plastics and Composites, 21: 1505–1513.
20.
ParkH.J. (2001). Effects of Stacking Sequence and Clamping Force on the Bearing Strengths of Mechanically Fastened Joints in Composite Laminates, Composite Structures, 53: 213–221.
21.
QuinnW.J.MatthewsF.L. (1977). The Effect of Stacking Sequence on the Pin-Bearing Strength in Glass Fiber Reinforced Plastic, Journal of Composite Materials, 11: 139–145.
22.
ReddyY.S.ReddyJ.N. (1993). Three-Dimensional Finite Element Progressive Failure Analysis of Composite Laminates Under Axial Extension, Journal of Composites Technology and Research, 15: 73–87.
23.
ThoppulS.D.FineganJ.GibsonR.F. (2009). Mechanics of Mechanically Fastened Joints in Polymer–Matrix Composite Structures: A Review, Composite Science and Technology, 69: 301–329.
24.
ValenzaA.FioreV.BorsellinoC.CalabreseL.BellaG.D. (2007). Failure Map of Composite Laminate Mechanical Joint, Journal of Composite Materials, 41: 951–964.
25.
WhitneyT.J.IarveE.V.BrockmanR.A. (2004). Singular Stress Fields Near Contact Boundaries in a Composite Bolted Joint, International Journal of Solids and Structures, 41: 1893–1909.
YılmazT.SınmazçelikT. (2007). Investigation of Load Bearing Performances of Pin Connected Carbon/Polyphenylene Sulphide Composites under Static Loading Conditions, Materials and Design, 28: 520–527.
28.
YılmazT.SınmazçelikT. (2009). Effects of Geometric Parameters on the Pin-Bearing Strength of Glass/Polyphenylenesulphide Composites, Journal of Composite Materials, 43: 2239–2253.