In this paper, some recent data exploring mixed mode I + III fracture of cracked polymethyl methacrylate specimens are re-analysed in terms of the local energy. The data have been obtained by using a new loading fixture proposed for exploring mixed mode I + III fracture experimentally. While a large bulk of experimental results from cracked specimens of polymethyl methacrylate under pure modes of loading, in particular under mode I loading, can be found in the literature, only very few tests have been carried out considering multiaxial static loadings, and for this reason, only limited studies have been performed on possible criteria for the fracture assessment under mixed mode I + III conditions. By taking advantage of the recent set of data on polymethyl methacrylate tested at different values of the mode mixity ratio, a criterion based on the local strain energy density previously applied by the same authors only to pure modes of loading is successfully extended here to the case of tension and torsion loadings applied in combination. Good agreement is shown to exist between the theoretical estimates and the experimental data.
AlihaMRMAyatollahiMR (2014) Rock fracture toughness study using cracked chevron notched Brazilian disc specimen under pure modes I and II loading – A statistical approach. Theoretical and Applied Fracture Mechanics69: 17–25.
2.
AlihaMRMHosseinpourGRAyatollahiMR (2012) Application of cracked triangular specimen subjected to three-point bending for investigating fracture behavior of rock materials. Rock Mechanics and Rock Engineering46: 1023–1034.
3.
ASTM E399-90(1997) (1997) Standard test method for plane-strain fracture toughness of metallic materials.
4.
AyatollahiMSabooriB (2014) Maximum tangential strain energy density criterion for general mixed mode I/II/III brittle fracture. International Journal of Damage Mechanics24: 263–278.
5.
AyatollahiMRAlihaMRM (2009) Analysis of a new specimen for mixed mode fracture tests on brittle materials. Engineering Fracture Mechanics76: 1563–1573.
6.
AyatollahiMRSabooriB (2015) A new fixture for fracture tests under mixed mode I/III loading. European Journal of Mechanics – A/Solids51: 67–76.
7.
BertoFCampagnoloAGalloP (2015a) Brittle failure of graphite weakened by V-notches: A review of some recent results under different loading modes. Strength of Materials47: 488–506.
8.
BertoFCampagnoloALazzarinP (2015b) Fatigue strength of severely notched specimens made of Ti-6Al-4 V under multiaxial loading. Fatigue and Fracture of Engineering Materials and Structures38: 503–517.
9.
Berto F, Campagnolo A, Chebat F, et al. (2016) Fatigue strength of steel rollers with failure occurring at the weld root based on the local strain energy values: Modelling and fatigue assessment. International Journal of Fatigue 82: 643 –657.
10.
BertoFCendonDAALazzarinP (2013) Fracture behaviour of notched round bars made of PMMA subjected to torsion at −60℃. Engineering Fracture Mechanics102: 271–287.
11.
BertoFElicesMLazzarinP (2012a) Fracture behaviour of notched round bars made of PMMA subjected to torsion at room temperature. Engineering Fracture Mechanics90: 143–160.
12.
BertoFGalloPLazzarinP (2014) High temperature fatigue tests of a Cu-Be alloy and synthesis in terms of linear elastic strain energy density. Key Engineering Materials627: 77–80.
13.
BertoFLazzarinP (2009) A review of the volume-based strain energy density approach applied to V-notches and welded structures. Theoretical and Applied Fracture Mechanics52: 183–194.
14.
BertoFLazzarinP (2014) Recent developments in brittle and quasi-brittle failure assessment of engineering materials by means of local approaches. Materials Science and Engineering R Reports75: 1–48.
15.
BertoFLazzarinPAyatollahiMR (2012b) Brittle fracture of sharp and blunt V-notches in isostatic graphite under torsion loading. Carbon N Y50: 1942–1952.
16.
BertoFLazzarinPYatesJR (2011) Multiaxial fatigue of V-notched steel specimens: A non-conventional application of the local energy method. Fatigue and Fracture of Engineering Materials and Structures34: 921–943.
17.
BhattacharjeeDKnottJF (1995) Effect of mixed mode I and II loading on the fracture surface of polymethyl methacrylate (PMMA). International Journal of Fracture72: 359–381.
18.
ChangJXuJMutohY (2006) A general mixed-mode brittle fracture criterion for cracked materials. Engineering Fracture Mechanics73: 1249–1263.
19.
Cho S, Nakamura Y, Mohanty B, et al. (2006) Study on control of crack-propagation in blasting. In: Fragblast 8, Santiago, Chile, pp.124–128.
20.
CookeMLPollardDD (1996) Fracture propagation paths under mixed mode loading within rectangular blocks of polymethyl methacrylate. Journal of Geophysical Research101: 3387.
21.
EwingPDSwedlowJLWilliamsJG (1976) Further results on the angled crack problem. International Journal of Fracture12: 85–93.
22.
GalloPBertoF (2015) High temperature fatigue tests and crack growth in 40CrMoV13.9 notched components. Fracture and Structural Integrity34: 180–189.
23.
GómezFJElicesMBertoF (2007) Local strain energy to assess the static failure of U-notches in plates under mixed mode loading. International Journal of Fracture145: 29–45.
24.
GoughHJPollardHV (1936) Properties of some materials for cast crankshafts, with special reference to combined stresses. Arch Proc Inst Automobile Eng 1906–1947 (vols 1–41)31: 821–893.
LanWDengXSuttonMA (2006) Study of slant fracture in ductile materials. International Journal of Fracture141: 469–496.
27.
LazzarinPBertoF (2005) Some expressions for the strain energy in a finite volume surrounding the root of blunt V-notches. International Journal of Fracture135: 161–185.
28.
LazzarinPBertoFElicesM (2009) Brittle failures from U- and V-notches in mode I and mixed, I + II, mode: A synthesis based on the strain energy density averaged on finite-size volumes. Fatigue and Fracture of Engineering Materials and Structures32: 671–684.
29.
LazzarinPSonsinoCMZambardiR (2004) A notch stress intensity approach to assess the multiaxial fatigue strength of welded tube-to-flange joints subjected to combined loadings. Fatigue and Fracture of Engineering Materials and Structures27: 127–140.
30.
LazzarinPZambardiR (2001) A finite-volume-energy based approach to predict the static and fatigue behavior of components with sharp V-shaped notches. International Journal of Fracture112: 275–298.
31.
LinBMearMERavi-ChandarK (2010) Criterion for initiation of cracks under mixed-mode I + III loading. International Journal of Fracture165: 175–188.
32.
LivieriPLazzarinP (2005) Fatigue strength of steel and aluminium welded joints based on generalised stress intensity factors and local strain energy values. International Journal of Fracture133: 247–276.
33.
ManoharanMHirthJPRosenfieldAR (1991) Combined mode I-mode III fracture toughness of a spherodized 1090 steel. Acta Metallurgica et Materialia39: 1203–1210.
34.
PetersenDKumarAHirthJ (1994) A suggested test procedure to measure mixed mode I–III fracture toughness of brittle materials. Journal of Testing and Evaluation22: 327.
35.
PookLP (1985) The fatigue crack direction and threshold behaviour of mild steel under mixed mode I and III loading. International Journal of Fatigue7: 21–30.
36.
RichardHABenitzK (1983) A loading device for the creation of mixed mode in fracture mechanics. International Journal of Fracture22: R55–R58.
37.
ShettyDKRosenfieldARDuckworthWH (1987) Mixed-mode fracture in biaxial stress state: Application of the diametral-compression (Brazilian disk) test. Engineering Fracture Mechanics26: 825–840.
38.
SihGC (1974) Strain-energy-density factor applied to mixed mode crack problems. International Journal of Fracture10: 305–321.
39.
SusmelLTaylorD (2008) The theory of critical distances to predict static strength of notched brittle components subjected to mixed-mode loading. Engineering Fracture Mechanics75: 534–550.
40.
Sutton MA, Deng X and Reynolds A (2006) Crack growth and stress intensity prediction techniques. Report, Delivery Order 0027-1: Mixed Mode Failure Criteria, University of South Carolina, USA, March.
41.
TorabiABertoF (2014) Strain energy density to assess mode II fracture in U-notched disk-type graphite plates. International Journal of Damage Mechanics23: 917–930.
42.
TorabiAFakoorMDarbaniM (2013) Pure shear fracture study in a brittle graphite material containing a U-notch. International Journal of Damage Mechanics23: 839–854.
43.
TorabiARCampagnoloABertoF (2015a) Experimental and theoretical investigation of brittle fracture in key-hole notches under mixed mode I/II loading. Acta Mechanica226: 2313–2322.
44.
TorabiARCampagnoloABertoF (2015b) Tensile fracture analysis of V-notches with end holes by means of the local energy. Physical Mesomechanics18: 5–12.
45.
WilliamsJGEwingPD (1972) Fracture under complex stress – The angled crack problem. International Journal of Fracture Mechanics8: 441–446.
46.
XeidakisGSSamarasISZacharopoulosDA (1996) Crack growth in a mixed-mode loading on marble beams under three point bending. International Journal of Fracture79: 197–208.
47.
YosibashZBussibaAGiladI (2004) Failure criteria for brittle elastic materials. International Journal of Fracture125: 307–333.
48.
YukioUKazuoITetsuyaY (1983) Characteristics of brittle fracture under general combined modes including those under bi-axial tensile loads. Engineering Fracture Mechanics18: 1131–1158.