Crack Opening Displacement and the Associated Response of Laminates with Varying Constraints

Abstract

This paper reports an experimental study of the opening displacement behavior of 90-ply cracks in a class of composite laminates where the constraint to cracking is varied systematically. The study is motivated by a synergistic approach to damage mechanics proposed by Talreja (1996) where the crack opening displacement forms a key micromechanically determined parameter in a continuum damage formulation of the composite response. It is found that although the opening displacement shows scatter from point to point along a crack length, its average over the crack length forms a robust parameter. This parameter, when introduced as the damage influence coefficient in a continuum description of damage, allows satisfactory predictions of the elastic moduli changes due to transverse cracks in the considered class of laminates with varying constraints.

Get full access to this article

View all access options for this article.

References

Allen, D. H. , Harris, C. E. and Groves, S. E. 1987. "A Thermomechanical Constitutive Theory for Elastic Composites with Distributed Damage-Part II: Application to Matrix Cracking in Laminated Composites," Int. J. Solids Struc., 23:1319-1338.

Allen, D. H. , Harris, C. E. and Groves, S. E. 1990. "Damage Modeling in Laminated Composites," Yielding, Damage, and Failure of Anisotropic Solids, J. P. Boehler , ed., London: Mechanical Engineering Publications, pp. 535-550.

Hashin,Z. 1985. "Analysis of Cracked Laminates: A Variational Approach," Mech. Mater., 4:121-136.

Ladeveze, P. 1990. "A Damage Mechanics for Composite Materials," Integration of Theory and Applications in Applied Mechanics, Dordecht: Kluwer, pp. 13-24.

Ladeveze, P. 1991. "About a Damage Mechanics Approach," Mechanics and Mechanisms in Composites and Multimaterials, D. Baptiste , ed., London: Mechanical Engineering Publications, pp. 119-142.

Lee, J. W. , Allen, D. H. and Harris, C. E. 1989. "Internal State Variable Approach for Predicting Stiffness Reductions in Fibrous Laminated Composites with Matrix Cracks," J. Comp. Mater., 23:1273-1291.

Saha, R. 1995. "Investigation of a Continuum Damage Model Using Experimental and Numerical Techniques," Ph.D. Thesis, School of Aerospace Engineering, Georgia Institute of Technology.

Talreja, R. 1985a. "A Continuum Mechanics Characterization of Damage in Composite Materials," Proc. R. Soc. Lond, A399:195-216.

Talreja, R. 1985b. "Transverse Cracking and Stiffness Reduction in Composite Laminates," J. Comp. Mater., 19:355-375.

10.

Talreja, R. 1986. "Stiffness Properties of Composite Laminates with Matrix Cracking and Interior Delamination," Engng Fracture Mech., 5/6:751-762.

11.

Talreja, R. 1990. "Internal Variable Damage Mechanics of Composite Materials," Yielding, Damage, and Failure of Anisotropic Solids, J. P. Boehler , ed., London: Mechanical Engineering Publications, pp. 509-533.

12.

Talreja, R. 1994. "Damage Characterization by Internal Variables," Damage Mechanics of Composite Materials, R. Talreja , ed., Amsterdam: Elsevier, pp. 53-78.

13.

Talreja, R. 1996. "A Synergistic Damage Mechanics Approach to Durability of Composite Material Systems," Progress in Durability Analysis of Composite Systems, A. Cardon , H. Fukuda and K. Reifsnider , eds., Rotterdam: Balkema, pp. 117-129.

14.

Varna, J. and Berglund, L. A. 1991. "Multiple Transverse Cracking and Stiffness Reduction in Cross-Ply Laminates," J. Comp. Tech. Res., 13:97-106.

15.

Varna, J. , Berglund, L. A. , Talreja, R. and Jakovics, A. 1993. "A Study of the Opening Displacement of Transverse Cracks in Cross-Ply Laminates," Int. J. Damage Mech., 2:272-289.

16.

Varna, J. , Berglund, L. A. , Krasnikovs, A. and Chilalenko, A. 1997. "Crack Opening Geometry in Cracked Composites Laminates," Int. J. Damage Mech., 6:96-118.