Introduction of new implants should be monitored closely to capture any signs of compromising patient safety. Vitamin E infused highly-crosslinked polyethylene liners (VEPE) offer the potential for reduced wear. Highwall liners have been hypothesised to result in increased wear and potential liner fractures. The aim of this study was to determine the 3–7-year follow-up of highwall VEPE for primary total hip arthroplasty (THA), focusing on liner-related complications.
Methods:
We included 1221 consecutive THA operations from July 2010 to May 2014 with minimum follow-up of 3 (3.1–6.8) years Data collected included demographics, implant data, complications, reoperations, and deaths. Data were cross-referenced with the Danish Hip Arthroplasty Registry in order to ensure validity and completeness. Acetabular shell position was measured using Martell Hip Analysis Suite in a subgroup of 931 THAs.
Results:
Cumulative stem revision and shell revision at 3-year follow-up was 3.4% and 0.4% respectively. There were no revisions due to liner failure. Reason for revision included 11 dislocations, 15 soft-tissue revisions for infection, 44 stem revisions of which 34 were periprosthetic fractures and 13 shell revisions of which 6 were combined shell and stem revisions.
Conclusion:
Early follow-up of VEPE liners for primary THA have not shown any revisions associated with liner failure. Continued monitoring of new materials are necessary to capture any signs of compromised patient safety.
MalchauH.On Importance of stepwise introduction of new hip implant technology. Assessment of total hip replacement using clinical evaluation, radiostereometry, digitised radiography and a national hip registry. Doctoral Thesis, University of Gothenborg, Sweden, 1995.
2.
MalchauHBragdonCRMuratogluOK.The stepwise introduction of innovation into orthopedic surgery: the next level of dilemmas. J Arthroplasty2011; 26: 825–831.
3.
HansenVJGreeneMEBragdonMA, et al. Registries collecting level-I through IV Data: institutional and multicenter use: AAOS exhibit selection. J Bone Joint Surg Am2014; 96: e160.
4.
OralEGhaliBWRowellSL, et al. A surface crosslinked UHMWPE stabilized by vitamin E with low wear and high fatigue strength. Biomaterials2010; 31: 7051–7060.
5.
OralEWannomaeKKRowellSL, et al. Diffusion of vitamin E in ultra-high molecular weight polyethylene. Biomaterials2007; 28: 5225–5237.
6.
SultanPGTanVLaiM, et al. Independent contribution of elevated-rim acetabular liner and femoral head size to the stability of total hip implants. J Arthroplasty2002; 17: 289–292.
7.
InsullPJCobbettHFramptonCM, et al. The use of a lipped acetabular liner decreases the rate of revision for instability after total hip replacement. Bone Joint J2014; 96-B: 884–888.
8.
WyattMCWhitehouseMRKieserDC, et al. Are lipped polyethylene liners associated with increased revision rates in patients with uncemented acetabular components? An observational cohort study. Clin Orthop Relat Res2020; 478: 581–589.
9.
GaleaVPConnellyJWShareghiB, et al. Evaluation of in vivo wear of vitamin E-diffused highly crosslinked polyethylene at five years. Bone Joint J2018; 100-B: 1592–1599.
10.
SillesenNHGreeneMENebergallAK, et al. Three year RSA evaluation of vitamin E diffused highly cross-linked polyethylene liners and cup stability. J Arthroplasty2015; 30: 1260–1264.
11.
NebergallAKTroelsenARubashHE, et al. Five-year experience of vitamin E-diffused highly cross-linked polyethylene wear in total hip arthroplasty assessed by radiostereometric analysis. J Arthroplasty2016; 31: 1251–1255.
12.
SalemyrMMurenOAhlT, et al. Vitamin-E diffused highly cross-linked polyethylene liner compared to standard liners in total hip arthroplasty. A randomized, controlled trial. Int Orthop2015; 39: 1499–1505.
13.
LindalenEThoenPSNordslettenL, et al. Low wear rate at 6-year follow-up of vitamin E-infused cross-linked polyethylene: a randomised trial using 32- and 36-mm heads. HIP Int2019; 29: 355–362.
14.
TakahashiYMasaokaTYamamotoK, et al. Vitamin-E blended and infused highly cross-linked polyethylene for total hip arthroplasty: a comparison of three-dimensional crystalline morphology and strain recovery behavior. J Mech Behav Biomed Mater2014; 36: 59–70.
15.
HustedH.Fast-track hip and knee arthroplasty: clinical and organizational aspects. Acta Orthop Suppl2012; 83: 1–39.
16.
GundtoftPHVarnumCPedersenAB, et al. The Danish hip arthroplasty register. Clin Epidemiol2016; 8: 509–514.
17.
BarrackRLKrempecJAClohisyJC, et al. Accuracy of acetabular component position in hip arthroplasty. J Bone Joint Surg Am2013; 95: 1760–1768.
18.
CallananMCJarrettBBragdonCR, et al. The John Charnley Award: risk factors for cup malpositioning: quality improvement through a joint registry at a tertiary hospital. Clin Orthop Relat Res2011; 469: 319–329.
19.
AtkinsGJHaynesDRHowieDW, et al. Role of polyethylene particles in peri-prosthetic osteolysis: a review. World J Orthop2011; 2: 93–101.
20.
Glyn-JonesSIsaacSHauptfleischJ, et al. Does highly cross-linked polyethylene wear less than conventional polyethylene in total hip arthroplasty? A double-blind, randomized, and controlled trial using roentgen stereophotogrammetric analysis. J Arthroplasty2008; 23: 337–343.
21.
HannaSASomervilleLMcCaldenRW, et al. Highly cross-linked polyethylene decreases the rate of revision of total hip arthroplasty compared with conventional polyethylene at 13 years’ follow-up. Bone Joint J2016; 98-B: 28–32.
22.
de SteigerRLorimerMGravesSE. Cross-linked polyethylene for total hip arthroplasty markedly reduces revision surgery at 16 years. J Bone Joint Surg Am2018; 100: 1281–1288.
23.
NebergallAKGreeneMERubashH, et al. Thirteen-year evaluation of highly cross-linked polyethylene articulating with either 28-mm or 36-mm femoral heads using radiostereometric analysis and computerized tomography. J Arthroplasty2016; 31: 269–276.
24.
OralEMuratogluOK.Vitamin E diffused, highly crosslinked UHMWPE: a review. Int Orthop2011; 35: 215–223.
25.
OralEO’BrienCDoshiB, et al. High temperature homogenization improves impact toughness of vitamin E-diffused, irradiated UHMWPE. J Orthop Res2017; 35: 1343–1347.
26.
SillesenNHGreeneMENebergallAK, et al. 3-year follow-up of a long-term registry-based multicentre study on vitamin E diffused polyethylene in total hip replacement. Hip Int2016; 26: 97–103.
27.
NebergallAKGreeneMELaursenMB, et al. Vitamin E diffused highly cross-linked polyethylene in total hip arthroplasty at five years: a randomised controlled trial using radiostereometric analysis. Bone Joint J2017; 99-B: 577–584.
28.
RochcongarGBuiaGBourrouxE, et al. Creep and wear in vitamin E-infused highly cross-linked polyethylene cups for total hip arthroplasty. J Bone Joint Surg Am2018; 100: 107–114.
29.
BrazierBGMeskoJW.Superior rim fracture of a vitamin E-infused highly cross-linked polyethylene (HXLPE) liner leading to total hip arthroplasty revision. Arthroplast Today2018; 4: 287–290.
30.
BatesMDMauerhanDR.Early fracture of a vitamin-E-infused, highly cross-linked polyethylene liner after total hip arthroplasty: a case report. JBJS Case Connect2015; 5: e65.
31.
TakahashiYTateiwaTShishidoT, et al. Size and thickness effect on creep behavior in conventional and vitamin E-diffused highly crosslinked polyethylene for total hip arthroplasty. J Mech Behav Biomed Mater2016; 62: 399–406.
32.
CarliAVNegusJJHaddadFS.Periprosthetic femoral fractures and trying to avoid them. Bone Joint J2017; 99-B: 50–59.
33.
GromovKBersangANielsenCS, et al. Risk factors for post-operative periprosthetic fractures following primary total hip arthroplasty with a proximally coated double-tapered cementless femoral component. Bone Joint J2017; 99-B: 451–457.
34.
KostensaloIJunnilaMVirolainenP, et al. Effect of femoral head size on risk of revision for dislocation after total hip arthroplasty: a population-based analysis of 42,379 primary procedures from the Finnish Arthroplasty Register. Acta Orthop2013; 84: 342–347.
35.
HailerNPGarellickGKärrholmJ.Uncemented and cemented primary total hip arthroplasty in the Swedish Hip Arthroplasty Register. Acta Orthop2010; 81: 34–41.
36.
BoesenachBvan der HeideHJNelissenRG.No improvement in long-term wear and revision rates with the second-generation Biomet cup (RingLoc) in young patients: 141 hips followed for median 12 years. Acta Orthop2011; 82: 664–668.
37.
EskelinenARemesVHeleniusI, et al. Uncemented total hip arthroplasty for primary osteoarthritis in young patients: a mid-to long-term follow-up study from the Finnish Arthroplasty Register. Acta Orthop2006; 77: 57–70.
38.
YamaguchiMAkisueTBauerTW, et al. The spatial location of impingement in total hip arthroplasty. J Arthroplasty2000; 15: 305–313.
39.
HarrisWH.Edge loading has a paradoxical effect on wear in metal-on-polyethylene total hip arthroplasties. Clin Orthop Relat Res2012; 470: 3077–3082.
40.
WilliamsSSchepersAIsaacG, et al. The 2007 Otto Aufranc Award. Ceramic-on-metal hip arthroplasties: a comparative in vitro and in vivo study. Clin Orthop Relat Res2007; 465: 23–32.
41.
TakahashiYTateiwaTPezzottiG, et al. Improved resistance to neck-liner impingement in second-generation highly crosslinked polyethylene-the role of vitamin E and crosslinks. J Arthroplasty2016; 31: 2926–2932.
42.
GaleaVPRojanasopondistPLaursenM, et al. Evaluation of vitamin E-diffused highly crosslinked polyethylene wear and porous titanium-coated shell stability: a seven-year randomized control trial using radiostereometric analysis. Bone Joint J2019; 101-B: 760–767.
43.
WyattMCRobertoAFoxall-SmiM, et al. Does vitamin E highly-crosslinked polyethylene convey an advantage in primary total hip replacement? A systematic review and meta-analysis. HIP Int2020; 30: 598–608.