The effect of microstructure and lead content on the tribological properties of bearing alloys

Abstract

Owing to the presence of lead in the alloy, leaded tin bronzes have excellent seizure resistance in bearing applications where lubrication may become absent or impaired. However, ecological concerns over the toxicity of lead have caused a growing demand for a feasible substitute. This requires a thorough understanding of the role of microstructure and lead content on the tribological properties of leaded tin bronze bearings. In this study, the effect of these qualities was tested with a specialised device simulating thrust bearings in boundary lubrication conditions, as well as with conventional unlubricated pin-on-disc testing. Ball-on-disc testing was also tried to see the effect of reversing the pin-on-disc material pair on tribological behaviour in dry sliding. The presence of lead in the tested bronze alloys was found to increase the capability of the alloy to sustain a lubricant film. The effect of the actual amount of lead was small beyond 4 wt%. In pin-on-disc testing, the microstructure of the alloy was found to have a significantly higher effect on tribological behaviour than lead content. Fine microstructure and small lead globule size were found to lead to a tendency to microcracking at the lead/copper matrix interfacial boundaries, resulting in rapid wear rates and low friction coefficients in dry sliding. The capability of lead to smear between sliding surfaces was verified in ball-on-disc testing.

Keywords

Leaded tin bronze lead content microstructure tribological testing bearing

Get full access to this article

View all access options for this article.

References

Budinski

. Tribonetic characteristics of copper alloys. In: Proceeding of the second international conference on wear of materials 1979; vol 25: 97–104. . ASME.

Prasad

Patwardhan

Yegneswaran

. Factors controlling dry sliding wear behaviour of a leaded tin bronze. Mater Sci Technol 1996; 12: 427–435.

Prasad

Patwardhan

Yegneswaran

. Dry sliding wear characteristics of some zinc-aluminium alloys: A comparative study with a conventional bearing bronze at a slow speed. Wear 1996; 199: 142–151.

Prasad

. Dry sliding wear response of some bearing alloys as influenced by the nature of microconstituents and sliding conditions. Metal Mater Trans A 1997; 28: 809–815.

Prasad

. Sliding wear behaviour of bronzes under varying material composition, microstructure and test conditions. Wear 2004; 257: 110–123.

Kestursatya

Kim

Rohatgi

. Wear performance of copper–graphite composite and a leaded copper alloy. Mater Sci Eng A 2003; 339: 150–158.

Equey

Houriet

Mischler

. Wear and frictional mechanisms of copper-based bearing alloys. Wear 2013; 273: 9–16.

Equey S, Bosc P, Mischler S, et al. Effect of microstructure on the wear and frictional mechanisms of copper-based bearing alloys. In: Nordtrib 14th Nordic symposium on tribology, Storforsen, Sweden, 2010.

Pasanen

Kleemola

Lehtovaara

. Development of a test device for the evaluation of hydrodynamic lubrication in thrust bearings. Finn J Tribol 2008; 27: 12–20.

10.

Archard

. Contact and rubbing of flat surfaces. J Appl Phys 1953; 24: 981–988.