Fatigue failure of 45# steel in dry sliding against Kevlar/PTFE hybrid composite under elevated load

Abstract

Frictional failure is inevitable for friction pairs. A common sense about the frictional failure of steel-polymer composite friction pair is that the polymer composites are the primary failure part rather than the steel counterpart. However, an opposite case was newly found in the case of fabric self-lubricating liner (Kevlar/PTFE hybrid composite) spherical plain-bearing under elevated load: the steel counterbody suffered a fatigue failure before the fabric composite fails, which resulted in the final failure of the bearing. This paper investigated such fatigue failure of surface chrome plated 45# steel by systematically studying the wear characteristics of 45# steel and fabric composite, the stress distribution of the 45# steel and fatigue features within cross section of the 45# steel. Results showed that wear characteristics of both fabric composite and 45# steel exhibited regional characters. Failure mechanism of the 45# steel was found to be fatigue failure (mainly fatigue pitting), which was revealed by mathematical analysis of the stress distribution of the 45# steel and the fatigue cracks found within subsurface of the cross section of the 45# steel.

Keywords

Dry sliding friction and wear polymer-matrix composite steel fatigue failure

Get full access to this article

View all access options for this article.

References

Koike

Kida

Santos

, et al. Self-lubrication of PEEK polymer bearings in rolling contact fatigue under radial loads. Tribol Int 2012; 49: 30–38.

Olofsson

Andersson

Bjorklund

. Simulation of mild wear in boundary lubricated spherical roller thrust bearings. Wear 2000; 241: 180–185.

Durak

Duran

. Tribological and fatigue failure properties of porous P/M bearing. Int J Fatigue 2008; 30: 745–755.

Sudhakar

. Failure analysis of automobile bimetal bearings. Eng Fail Anal 2002; 9: 221–225.

Yonekura

Chittenden

Dearnley

. Wear mechanisms of steel roller bearings protected by thin, hard and low friction coatings. Wear 2005; 259: 779–788.

Park

Lee

Kim

, et al. Development of heavy duty hybrid carbon–phenolic hemispherical bearings. Compos Struct 2006; 73: 88–98.

Kim

Hwang

, et al. The sliding friction of hybrid composite journal bearing under various test conditions. Tribol Lett 2009; 35: 211–219.

Jia

, et al. Effects of weft density on the friction and wear properties of self-lubricating fabric liners for journal bearings under heavy load conditions. Wear 2014; 318: 124–129.

Yang

, et al. Influence of weave structures on the tribological properties of hybrid Kevlar/PTFE fabric composites. Chin J Mech Eng 2012; 25: 1044–1051.

10.

Yang

, et al. Fabrication of nano serpentine-potassium acetate intercalation compound and its effect as additive on tribological properties of the fabric self-lubricating liner. Wear 2014; 318: 202–211.

11.

Fan

Yang

Feng

, et al. Tribological properties of fabric self-lubricating liner based on organic montmorillonite (OMMT) reinforced phenolic (PF) nanocomposites as hybrid matrices. Tribol Lett 2015; 57: 1–12.

12.

Man

Petrenec

Obrtlik

, et al. AFM and TEM study of cyclic slip localization in fatigued ferritic X10CrAl24 stainless steel. Acta Mater 2004; 52: 5551–5561.

13.

Zhao

Jiang

. Fatigue of 7075-T651 aluminum alloy. Int J Fatigue 2008; 30: 834–849.

14.

Zhong

Tian

. Foundation knowledge of failure analysis, 1st ed. Beijing: China Machine Press, 1990, pp. 84–84.

15.

Bakshi

Shipway

Bhadeshia

HKDH

. Three-body abrasive wear of fine pearlite, nanostructured bainite and martensite. Wear 2013; 308: 46–53.