Development and fracture toughness characterization of a nylon nanomat epoxy adhesive reinforcement

Abstract

The potential of an electrospun nylon nanofibrous mat as adhesive carrier and reinforcing web in adhesive bonding has been proven by the authors in a previous work. In that work, a pre-preg nanomat was developed using a low-viscosity epoxy resin for composite hand lay-up, in order to favour wetting of the nanofibres and to minimize air entrapment. However, the resin for hand lay-up exhibited a poor bonding performance when compared to the one typical of epoxy adhesives. The present work is therefore aimed at developing a laboratory route to add an electrospun polymeric nanomat to a two-part epoxy adhesive joint. Three different adhesives with increasing viscosity have been preliminarily evaluated regarding the entrapment of air after curing. The most promising one has been used to manufacture a small-size, Al-alloy double cantilever beam joint and compare the performance with and without the nanomat. Three different precracking procedures have also been developed and evaluated, namely fatigue precracking (A), razor blade tapping (B) and nanomat exfoliation (C). The results indicate that the fracture toughness of the nanomat-reinforced adhesive joint is similar to the neat adhesive one at the beginning of the propagation but it becomes much higher as the crack advances.

Keywords

Nanomaterials/nanostructures bonding reinforcement fracture toughness bonded joints aluminium alloys

Get full access to this article

View all access options for this article.

References

da Silva

LFM

Oechsner

Adams

. Handbook of adhesion technology, Berlin: Springer, 2011.

Kinloch

. Toughening epoxy adhesives to meet today's challenges. MRS Bull 2003; 28: 445–448.

Takeda

Narita

. Fracture behavior and crack sensing capability of bonded carbon fiber composite joints with carbon nanotube-based polymer adhesive layer under Mode I loading. Comp Sci Technol 2017; 146: 26–33.

Burkholder

Kwon

Pollak

. Effect of carbon nanotube reinforcement on fracture strength of composite adhesive joints. J Mater Sci 2011; 46: 3370–3377.

Jakubinek

Ashrafi

Zhang

. Single-walled carbon nanotube-epoxy composites for structural and conductive aerospace adhesives. Comp B 2015; 69: 87–93.

Gude

Prolongo

Ureña

. Toughening effect of carbon nanotubes and carbon nanofibres in epoxy adhesives for joining carbon fibre laminates. Int J Adhes Adhes 2015; 62: 139–145.

Korayem

Chen

Zhang

et al.

Failure of CFRP-to-steel double strap joint bonded using carbon nanotubes modified epoxy adhesive at moderately elevated temperatures. Comp B 2016; 94: 95–101.

Khoramishad H and Khakzad M. Toughening epoxy adhesives with multi-walled carbon nanotubes. J Adhes 2018; 94: 15–29.

Zielecki

Kubit

Trzepieciński

et al.

Impact of multiwall carbon nanotubes on the fatigue strength of adhesive joints. Int J Adhes Adhes 2017; 73: 16–21.

10.

Huang

Zhang

Kotaki

et al.

A review on polymer nanofibers by electrospinning and their applications in nanocomposites. Comp Sci Technol 2003; 63: 2223–2253.

11.

Zucchelli

Focarete

Gualandi

et al.

Electrospun nanofibers for enhancing structural performance of composite materials. Polym Adv Technol 2011; 22: 339–349.

12.

Palazzetti

Zucchelli

Trendafilova

. The self-reinforcing effect of Nylon 6,6 nano-fibres on CFRP laminates subjected to low velocity impact. Compos Struct 2013; 106: 661–671.

13.

Moroni

Palazzetti

Zucchelli

et al.

A numerical investigation on the interlaminar strength of nanomodified composite interfaces. Compos B 2013; 55: 635–641.

14.

Giuliese

Palazzetti

Moroni

et al.

Cohesive zone modelling of delamination response of a composite laminate with interleaved nylon 6,6 nanofibres. Compos B 2015; 78: 384–392.

15.

Beckermann

Pickering

. Mode I and Mode II interlaminar fracture toughness of composite laminates interleaved with electrospun nanofibre veils. Compos A 2015; 72: 11–21.

16.

Saghafi

Palazzetti

Zucchelli

et al.

Influence of electrospun nanofibers on the interlaminar properties of unidirectional epoxy resin/glass fiber composite laminates. J Reinf Plast Comp 2015; 34: 907–914.

17.

Zhang

Bharti

et al.

Localized toughening of carbon/epoxy laminates using dissolvable thermoplastic interleaves and electrospun fibres. Compos A 2015; 79: 116–126.

18.

Daelemans

van der Heijden

De Baere

et al.

Interlaminar toughening of resin transfer molded laminates by electrospun polycaprolactone structures: Effect of the interleave morphology. Comp Sci Technol 2016; 124: 17–26.

19.

Daelemans

van der Heijden

De Baere

et al.

Compos A 2017; 94: 10–20.

20.

Kim

. Effect of the core/ shell-structured meta-aramid/epoxy nanofiber on the mechanical and thermal properties in epoxy adhesive composites by electrospinning. J Adhes 2014; 90: 787–801.

21.

Kim

. Effects of post-treatment of meta-aramid nanofiber mats on the adhesion strength of epoxy adhesive joints. Compos Struct 2017; 159: 636–645.

22.

Razavi SMJ, Esmaeely Neisiany R, Ayatollahi MR, et al. Fracture assessment of polyacrylonitrile nanofiber-reinforced epoxy adhesive. Theor Appl Fract Mech 2018; 97: 448–453.

23.

Ekrem

Avcı

. Effects of polyvinyl alcohol nanofiber mats on the adhesion strength and fracture toughness of epoxy adhesive joints. Compos B 2018; 138: 256–264.

24.

Musiari F, Pirondi A, Zucchelli A, et al. Experimental investigation on the enhancement of Mode I fracture toughness of adhesive bonded joints by electrospun nanofibers. J Adhes 2018; 94: 974–990.

25.

Kinloch

. Adhesion and adhesives: science and technology, London: Chapman & Hall, 1987.

26.

Krenk

. Energy release rate of symmetric adhesive joints. Eng Fract Mech 1992; 43: 549–559.