Real world application of angular scan pulse-echo ultrasonic propagation imager for damage tolerance evaluation of full-scale composite fuselage

Abstract

Composite structures are assertively used for new airframe designs and manufacturing in military aircrafts because of superior strength-to-weight ratios and fatigue resistance. Because the composites have different fatigue failure characteristics compared with metals, it is necessary to develop different approaches for the composite fatigue design and testing. In this study, we propose an in situ damage evaluation technology with high spatial resolution during full-scale fatigue testing of composite aircraft structures. For real composite structure development considering composite fatigue characteristics, full-scale fatigue and damage tolerance tests of the composite fuselage structure were conducted to evaluate the structural characteristics. In the meantime, the laser ultrasonic nondestructive inspection method, called an angular scan pulse-echo ultrasonic propagation imager, which is fully noncontact, real-time, and portable to position it in between the complex test rigs, is used to observe in situ damage growth of the composite. Finally, the verification procedure assisted by the angular scan pulse-echo ultrasonic propagation imager assures no growth of the initial impact damages after lifetime operation and proves the damage tolerance capability of the developed composite fuselage structure.

Keywords

Full-scale fatigue test pulse-echo ultrasonic propagation imager composite fuselage structure impact damage damage tolerance

Get full access to this article

View all access options for this article.

References

CMH-17 Organization. Composite material handbook volume 3, polymer matrix composites: materials usage, design, and analysis. Pittsburgh, PA: SAE International, 2012.

Talreja

Singh

Damage and failure of composite materials. Cambridge: Cambridge University Press, 2012.

Talreja

Damage and fatigue in composites—a personal account. Compos Sci Technol 2008; 68(13): 2585–2591.

Ahmadzadeh

Shirazi

Varvani-Farahani

Damage assessment of CFRP [90/±45/0] composite laminates over fatigue cycles. Appl Compos Mater 2011; 18(6): 559–569.

Maimi

Camanho

Mayugo

, et al. Matrix cracking and delamination in laminated composites—part I: ply constitutive law, first ply failure and onset of delamination. Mech Mater 2011; 43(4): 169–185.

Pascoe

Alderliesten

Benedictus

Methods for the prediction of fatigue delamination growth in composites and adhesive bonds—a critical review. Eng Fract Mech 2013; 112: 72–96.

Thionnet

From fracture to damage mechanics: a behavior law for microcracked composites using the concept of crack opening mode. Compos Struct 2010; 92(3): 780–794.

Salavatian

Smith

LV.

An investigation of matrix damage in composite laminates using continuum damage mechanics. Compos Struct 2015; 131: 565–573.

MIL-STD-1530D: 2016. US: Department of Defense, Standard practice: aircraft structural integrity program (ASIP).

10.

JSSG-2006:1998. US: Department of Defense, Joint service specification guide—aircraft structures.

11.

Bae

Lee

. Development of single channeled serial-connected piezoelectric sensor array and damage visualization based on multi-source wave propagation imaging. J Intel Mat Syst Str 2016; 27(13): 1861–1870.

12.

Shin

Park

Hong

, et al. In situ non-destructive evaluation of an aircraft UHF antenna radome based on pulse-echo ultrasonic propagation imaging. Compos Struct 2017; 160: 16–22.

13.

Hong

Lee

Ihn

. In-situ NDE of composite repair patch and thick panel with substructures using mobile pulse-echo ultrasonic propagation imager. In: Proceedings of the 11th international workshop on structural health monitoring, San Francisco, CA, 12–14 September 2017, pp. 1–8. Stanford, CA: Stanford University.

14.

Abbas

Lee

JR.

High-speed angular-scan pulse-echo ultrasonic propagation imager for in situ non-destructive evaluation. Smart Struct Syst 2018; 22(2): 223–230.

15.

Hong

Lee

. Full-field pulse-echo ultrasonic wave propagation imaging for non-destructive composite inspection. In: Proceedings of the 20th international conference on composite materials, Copenhagen, 19–24 July 2015, pp. 3219–3222, http://www.iccm20.org/

16.

Lee

Chia

Park

, et al. Laser ultrasonic anomalous wave propagation imaging method with adjacent wave subtraction: algorithm. Opt Laser Technol 2012; 44(5): 1507–1515.