Preliminary Investigation on Bulletproof Panels Made from Ramie Fiber Reinforced Composites for NIJ Level II,IIA,and IV

Abstract

Ramie (Boehmeria nivea) is one of the strongest natural cellulose fibers. Optimizing abundant resources ramie as a candidate materials used for reinforcing in polymeric composite material is a must to obtained high-performance natural fibers reinforced polymer especially for bulletproof panel or high-impact flexibility safer structures. Ramie woven was treated using common chemical solvents that were ethanol, methyl ethyl ketone, acetone, and silane as coupling agent. Composite panels were made by hand lay-up process with epoxy as a matrix. These prototype bulletproof panels were to be believed lighter in weight and much lower economic cost than conventional bulletproof panels made from ceramic plate, Kevlar/aramid composite, and steel-based material as a popular today in military standard antiballistic equipments. From the bullet testing result, it showed that panel could be able to resist the penetration of high-impact projectile for level II with some fractures phenomenon. Level IV ballistic testing showed that all prototype panel could not resist the high-impact velocity of the projectile yet. It was found that ramie fibers have sufficient breaking strength and toughness for level II bullet testing, although still needs improvements to optimize process parameters to meet a very high military standard and application

Keywords

Ramie woven composite bulletproof panel ballistic testing NIJ standard.

References

Perepelkin, K.E. (2001). Fibre Polymer Composite, Basic Types, Principles of Fabrication and Properties, Fibre Chemistry, vol. 38(3), pp. 224-239, Springer Science.

Mueller, D.H. and Krobjilowski , A. (2003). New Discovery in the Properties of Composite Reinforced with Natural Fibers , Journal of Industrial Textiles, 33(2): 111-130.

Jacob, M. , Joseph, S. , Pothan, L.A. and Thomas, S. (2005). A Study of Advances in Characterization of Interfaces and Fiber Surfaces in Lignocellulosic Fiber Reinforced Composites, Composite Interfaces, 12(1-2): 95-124.

Rowell, R.M. , Han, J.S. and Rowell, J.S. (2000). Characterization and Factors Effecting Fiber Properties , Nat. Polymer and Agrofibers Composites, San Carlos, Brazil, pp. 115-133.

Andre, A. (2006). Fibers for Strengthening of Timber Structures, Technical Report, pp. 41-66, Lulea University of Technology, Swedia.

Marsyahyo, E. , Soekrisno, Rochardjo, H.S.B. and Jamasri (2007). Identification of Ramie Single Fiber Surface Topography Influenced by Solvent Based Treatment , Journal of Industrial Textiles, 38(2): 127-137.

Gibson, R.F. (1994). Principles of Composite Material Mechanics, Pen . McGraw Hill Int., Singapore.