This article reports the organomodification of Indian bentonite clay with three modifiers and the fire behavior of organomodified Indian bentonite clay/vinylester/glass nanocomposites. Indian bentonite (Na-IB) clay was organomodified using hexadimethyl ammonium bromide (HDTMA-Br), tetra-n-butylammonium bromide (TBA-Br) and triphenyl methyl phosphonium bromide (TPP-Br) by varying the cation exchange capacity. Basal spacing of 34 Å was observed in Na-IB modified with HDTMA-Br (HDTMABr-IB) followed by 28 Å in Na-IB modified with TPP-Br (TPPBr-IB) and 26 Å in Na-IB modified with TBA-Br (TBABr-IB). Fourier transform infrared spectra of HDTMABr-IB confirmed the attachment of functional groups, its zeta potential increased from −36.34 to 5.35 mV indicating greater surface potential and thermogravimetric analysis showed greater weight loss confirming Na+ ion exchange with alkyl amines. Energy-dispersive X-ray analysis showed compositional changes between modified and unmodified clay with the presence of 37.03% carbon in the HDTMABr-IB. Horizontal and vertical burning rates of vinylester/glass composites decreased with the addition of HDTMABr-IB. Limiting oxygen index increased by 40% with the addition of 5 wt% HDTMABr-IB to vinylester/glass.
AswiniKMShaikARamanujN. Characterization of surface-modified montmorillonite nanocomposites. Ceram Int2012; 38: 929–934.
2.
RajkiranTRKarticKCUpendraN. Synthesis and characterization of novel organo-montmorillonites. Appl Clay Sci2008; 38: 203–208.
3.
HeHFrostRLBostromT. Changes in the morphology of organoclays with HDTMA+ surfactant loading. Appl Clay Sci2006; 31(3–4): 262–271.
4.
XiYFrostRLHeH. Modification of Wyoming montmorillonite surfaces using a cationic surfactant. Langmuir2005; 21: 8675–8680.
5.
XiYDingZHeH. Structure of organoclays—an X-ray diffraction and thermogravimetric analysis study. J Colloid Interf Sci2004; 277: 116–120.
6.
RuiLRayLFWaydeNM. Synthesis, characterization of mono, di and tri alkyl surfactant intercalated Wyoming montmorillonite for the removal of phenol from aqueous systems. J Colloid Interf Sci2008; 327: 287–294.
7.
BoydSAShaobaiSLeeJF. Pentachlorophenol sorption by organo-clays. Clay Clay Miner1988; 36:125–130.
Vishnu MaheshKRNarasimha MurthyHNKumaraswamyBE. Synthesis and characterization of organomodified Na-MMT using cation and anion surfactants. Front Chem China2011; 6: 153–158.
10.
NadezdaSMihovilLJelenaL. Characterization of bentonite clay from “Greda” deposit. Proc Appl Ceram2011; 5: 97–101.
11.
XiYRayLFHongPH. Modification of the surfaces of Wyoming montmorillonite by the cationic surfactants alkyl trimethyl, dialkyl dimethyl, and trialkyl methyl ammonium bromides. J Colloid Interf Sci2007; 305: 150–158.
12.
Yun-HweiS. Preparations of organobentonite using nonionic surfactants. Chemosphere2001; 44: 989–995.
13.
MortlandMMShaobaiSBoydSA. Clay organic complexes as adsorbents for phenol and chlorophenols. Clay Clay Miner1986; 34: 581–585.
14.
SalawudeenOTIsamQYNassereldeenKA. Effect of modification on the physicochemical and thermal properties of organophilic clay modified with octadecylamine. Int J Eng Tech1990; 10(1): 27–35.
15.
SmithJAJaffePRChiouCT. Effect of ten quaternary ammonium cations on tetrachloromethane sorption to clay from water. Environ Sci Technol1990; 24: 1167–1172.
16.
BenamarMMohamedADDidierV. Modification of IB with diphosphonium salts: Synthesis and characterization. Mater Lett 2008; 62: 2493–2496.
17.
ZengQHYuABLuGQ. Clay-Based Polymer Nanocomposites: Research and Commercial Development. J Nanosci Nanotechno2005; 5: 1574–1592.
18.
TemuujinJJadambaaTsBurmaaG. Characterisation of acid activated montmorillonite clay from Tuulant (Mongolia). Ceram Int2004; 30: 251–255.
19.
VenugopalBRMichaelR. Layer-by-layer composite of anionic and cationic clays by metathesis. J Colloid Interf Sci2011; 355: 396–401.
20.
HakanAMehmetATFilipDP. Synthesis and characterization of polymer/clay nanocomposites by intercalated chain transfer agent. Eur Polym J2008; 44: 1949–1954.
21.
MansorBAWisamHHNorazowabtI. Modification of montmorillonite by new surfactant. J Eng Appl Sci2009; 4: 184–188.
22.
HyungMLJoonhoYMikyungH. Magnesium hydroxide flame retardant and its application to a low-density polyethylene/ethylene vinyl acetate composite. J Ceram Process Res2009; 10: 571–576.
23.
LaiaHAnaIFJoseIV. Thermal stability and flame retardancy of LDPE/EVA blends filled with synthetic hydromagnesite/aluminium hydroxide/montmorillonite and magnesium hydroxide/aluminium hydroxide/montmorillonite mixtures. Polym Degrad Stabil2007; 92: 1082–1087.
24.
ChuangTHGuoWChengKC. Thermal properties and flammability of ethylene-vinyl acetate copolymer/montmorillonite/polyethylene nanocomposites with flame retardants. J Polym Res2004; 11: 169–174.
25.
XuZBKZhouWWPengMX. Thermal characteristic of organomodified montmorillonite. Chinese J Polym Sci2010; 28: 615–662.
26.
YukselenYErzinY. Artificial neural networks approach for zeta potential of montmorillonite in the presence of different cations. Environ Geol2008; 54: 1059–1066.
27.
KhoeiniMBazgirSTamizifarM. Investigation of the modification process and morphology of organosilane modified nanoclay. Ceram Silik2009; 53: 254–259.
28.
HoffmannBDietrichCThomannR. Morphological and rheological characterization of polystyrene-nanocomposites. Macromol Rapid Comm2000; 21: 57–61.
29.
XieWHwuJMJiangGJ. A study of the effect of surfactants on the properties of polystyrene-montmorillonite nanocomposites. Polym Eng Sci2003; 43: 214–222.
30.
LeeSYKimSJ. Expansion characteristics of organoclay as a precursor to nanocomposites. Colloid Surface A2002; 211: 19–26.
31.
LimeiZHuaCXiaohuiJ. Modification of montmorillonite surfaces using a novel class of cationic gemini surfactants. J Colloid Interf Sci2009; 332: 16–21.
32.
ShadpourMMohammadD. Preparation and characterization of new organoclays using natural amino acids and Cloisite Na+. Appl Clay Sci2011; 51: 353–359.
33.
PetrPMartinaTSonaS. Study of cetyltrimethylammonium and cetylpyridinium adsorption on montmorillonite. J Colloid Interf Sci2006; 304: 29–36.
34.
WisamHHMansorBAEmadA. Synthesis and characterization of organoclay from sodium montmorillonite and fatty hydroxamic acids. Am J Appl Sci2009; 6: 1567–1572.
35.
TakeichiTZeidamRAgagT. Polybenzoxazines/clay hybrid nanocomposites: influence of preparation method on the curing behavior and properties of polybenzoxazine. Polymer2002; 43: 45–53.
36.
El-SheikhyRAl-ShamraniMKobayashiA. Application of natural silicate-aluminum powder in advanced smart nanocomposite coating. Trans JWRI2009; 38: 49–52.
37.
ZhangJHereidJHagenM. Effects of nanoclay and fire retardants on fire retardancy of a polymer blend of EVA and LDPE. Fire Safety J2009; 44: 504–513.
38.
KiliarisPPapaspyridesCD. Polymer/layered silicate (clay) nanocomposites: An overview of flame retardancy. Prog Polym Sci2010; 35: 902–958.
39.
BharatkumarDZ, Use of non-traditional fillers to reduce flammability of polyester resin composites. Polymeri2009; 30:10–17.