Influence of Resin Molecular Weight on the Moisture Permeability of HDPE Blown Films

Abstract

A set of high density polyethylene (HDPE) blown films was produced from five resins of varying molecular weight under identical processing conditions. Film morphology was characterized in terms of crystalline content using refractometry as well as quantification of crystalline phase orientation through the application of Fourier transform infrared (FTIR) linear dichroism. Additional insight into film structure was gained through the use of scanning electron microscopy (SEM). Water vapor transmission rate (WVTR) was observed to increase with resin molecular weight. The enhanced permeability of the higher molecular weight films was associated with slightly lower crystalline content and greater crystalline orientation relative to the lower molecular weight films. Due to the small differences in morphology and permeation behavior noted, the effect of orientation on WVTR performance between the films studied was only significant for the most highly oriented film.

Keywords

HDPE molecular weight WVTR SEM FTIR blown films amorphous crystalline orientation

Get full access to this article

View all access options for this article.

References

1. Briston, J. (1989). Plastic Films, John Wiley and Sons, New York.

2. Oswin, C.R. (1975). Plastic Films and Packaging, John Wiley and Sons, New York.

3. Peterlin, A. (1975). Journal of Macromolecular Science-Physics, B1, 1: 57.

4. Schlotter, N.E. and Furlan, P.Y. (1992). Polymer, 33(16): 3323.

5. Krevelen, D.W. (1976). Properties of Polymers - Their Estimation and Correlation With Chemical Structure, 2nd edn, Elsevier, New York.

6. Ng, H.C. , Leung, W.P. and Choy, C.L. (1985). Journal of Polymer Science: Polymer Physics, 23: 973.

7. Araimo, L. , Candia, F. , Vittoria, V. and Peterlin, A. (1978). Journal of Polymer Science: Polymer Physics, 16: 2087.

8. Eby, R.K. (1964). Journal of Applied Physics, 35 (9): 2720.

9. Peacock, A.J. (2000). Handbook of Polyethylene - Structure, Properties, and Applications, Marcel Dekker Inc., New York.

10.

10. Maddams, W.F. and Preedy, J.E. (1978). Journal of Applied Polymer Science, 22: 2721.

11.

11. Maddams, W.F. and Preedy, J.E. (1978). Journal of Applied Polymer Science, 22: 2739.

12.

12. Maddams, W.F. and Preedy, J.E. (1978). Journal of Applied Polymer Science, 22: 2751.

13.

13. Hofmann, D. , Geiss, D. , Janke, A. , Michler, G.H. and Fielder, P. (1990). Journal of Applied Polymer Science, 39: 1595.

14.

14. Choi, K.J. , White, J.L. and Spruiell, J.E. (1982). Journal of Polymer Science; Polymer Physics, 20: 27.

15.

15. Keller, A. and Machin, M.J. (1997). Journal of Macromolecular Science Physics, B1, 1: 41.

16.

16. Pazur, R.J. and Prud’homme, R.E. (1996). Macromolecules, 29: 119.

17.

17. Prasad, A. , Shroff, R. , Rane, S. and Beaucage, G. (2001). Polymer, 42: 3103.

18.

18. Schael, W. (1968). Journal of Polymer Science, 12: 903.

19.

19. Krishnaswamy, R.K. and Janzen, J. (2001). Proceedings ANTEC 2001 - San Francisco.

20.

20. Wilkes, G.L. (1988). Encyclopedia of Polymer Science and Engineering - Rheooptical Properties, 14: 542.

21.

21. Krishnaswamy, R.K. (2000). Journal of Polymer Science: Polymer Physics, 38: 182.